Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Modulus of Elasticity | 214 GPa | 31000 ksi | sheet at RT |
Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, 1.6 mm thick sheet Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
Modulus of Elasticity | 214 GPa | 31000 ksi | sheet at RT |
Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, 12.7 mm (1/2 in.) thick plate Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
Modulus of Elasticity | 214 GPa | 31000 ksi | sheet at RT |
Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 1.0 mm thick sheet Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
Modulus of Elasticity | 214 GPa | 31000 ksi | sheet at RT |
Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 15.9 mm thick plate Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
Modulus of Elasticity | 214 GPa | 31000 ksi | sheet at RT |
Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 15.9 mm thick plate, aged 3 hours at 816°C Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
Modulus of Elasticity | 214 GPa | 31000 ksi | sheet at RT |
Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 7.9 mm thick plate, aged 3 hours at 816°C Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
Modulus of Elasticity | 214 GPa @Temperature 200 °C |
31000 ksi @Temperature 392 °F |
|
Haynes 25 alloy, cold worked sheet, 15% cold reduction, aged at 370°C (700°F) for 1 hour Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Modulus of Elasticity | 214 GPa | 31000 ksi | sheet at RT |
Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 3.2 mm thick sheet Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
Modulus of Elasticity | 214 GPa @Temperature 200 °C |
31000 ksi @Temperature 392 °F |
|
Haynes 25 alloy, cold worked sheet, 10% cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Modulus of Elasticity | 214 GPa @Temperature 200 °C |
31000 ksi @Temperature 392 °F |
|
Haynes 25 alloy, room temperature after 20% cold reduction, 1175°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Modulus of Elasticity | 214 GPa @Temperature 200 °C |
31000 ksi @Temperature 392 °F |
|
Haynes 25 alloy, room temperature after 25% cold reduction, 1065°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Modulus of Elasticity | 214 GPa @Temperature 200 °C |
31000 ksi @Temperature 392 °F |
|
Haynes 25 alloy, room temperature after 25% cold reduction, 1175°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Modulus of Elasticity | 214 GPa @Temperature 200 °C |
31000 ksi @Temperature 392 °F |
|
Haynes 25 alloy, room temperature sheet after 100 hours of 870°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Modulus of Elasticity | 214 GPa @Temperature 200 °C |
31000 ksi @Temperature 392 °F |
|
Haynes 25 alloy, room temperature sheet after 1000 hours of 650°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Modulus of Elasticity | 214 GPa @Temperature 200 °C |
31000 ksi @Temperature 392 °F |
|
Haynes 25 alloy, room temperature sheet after 2500 hours of 650°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Modulus of Elasticity | 214 GPa | 31000 ksi | |
Latrobe DuraTechâ„¢ M4 High Carbon Powder Metal High Speed Steel (ASTM M4) DuraTech M4 high speed steel is an extremely versatile high speed steel which provides a unique combination of high wear resistance with high impact toughness and transverse bend strength. A large v.. |
|||
Modulus of Elasticity | 214 GPa | 31000 ksi | |
Latrobe DuraTechâ„¢ M48 Powder Metal High Speed Steel (ASTM M48) DuraTech M48 super high speed steel is a high-performance high speed steel which exhibits superior hot (red) hardness compared to T15 and M42 high speed steels, and wear resistance comparable to tha.. |
|||
Modulus of Elasticity | 214 GPa | 31000 ksi | |
Crucible Steel CPM® REX® 121 HS High Speed Steel CPM REX 121 is a new high vanadium cobalt bearing tool steel designed to offer a combination of the highest wear resistance, attainable hardness, and red hardness available in a high speed steel. It.. |
|||
Modulus of Elasticity | 214 GPa | 31000 ksi | |
Crucible Steel CPM® Rex® T15(HS), AISI T15 High Speed Steel Rex® T15(HS) CPM Rex T15 is a super high speed steel made by the Crucible Particle Metallurgy (CPM) process. It is a tungsten type high speed containing high vanadium for excellent abrasion resistance, and cobal.. |
|||
Modulus of Elasticity | 214 GPa @Temperature 399 °C |
31000 ksi @Temperature 750 °F |
hardened and tempered |
Bohler-Uddeholm UDDEHOLM VANADIS 30 AISI M2 + Co SUPERCLEAN 3 Powder Metallurgical Cold Work Tool Steel Uddeholm Vanadis 30 is a Co high alloyed powder metallurgy high speed steel corresponding to AISI M3:2 + Co. The high compressive strength, 67 HRC, and good abrasive wear resistance makes Uddeholm V.. |
|||
Modulus of Elasticity | 214 GPa | 31000 ksi | |
Carpenter Micro-Melt® HS-76 Alloy (AISI M48) Micro-Melt® HS-76 alloy is a super high speed steel possessing abrasion resistance equal to T15 and superior red hardness to T15 and M42. It is heat treatable to HRC 70 and is a good candidate for .. |
|||
Modulus of Elasticity | 214 GPa | 31000 ksi | |
ATI Allegheny Ludlum Altemp® X-750 Nickel-Based superalloy Characteristics: precipitation hardenable, high strength up to 1300°F, oxidation resistant up to 1800°F. Applications: aerospace, heat treatment fixtures, forming tools, extrusion dies.Information.. |
|||
Modulus of Elasticity | 214 GPa | 31000 ksi | longitudinal |
ATI Allegheny Ludlum Stainless Steel Type 301, annealed (UNS S30100) Allegheny Ludlum Type 301 is a high strength grade of steel available in six conditions or tempers, its resistance to atmosphere corrosion and its bright, attractive surface make it an excellent cho.. |
|||
Modulus of Elasticity | 214 GPa @Temperature 200 °C |
31000 ksi @Temperature 392 °F |
|
Haynes 25 alloy, room temperature after 0% cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
Modulus of Elasticity | 214 GPa @Temperature 200 °C |
31000 ksi @Temperature 392 °F |
|
Haynes 25 alloy, room temperature after 15% cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
Modulus of Elasticity | 214 GPa @Temperature 200 °C |
31000 ksi @Temperature 392 °F |
|
Haynes 25 alloy, room temperature after 15% cold reduction, 1175°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
Modulus of Elasticity | 214 GPa | 31000 ksi | |
Haynes Multimet® alloy, 533.4 by 82.55 mm forging, stress relieved at 649°C (1200°F), air cooled Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductility, and i.. |
|||
Modulus of Elasticity | 214 GPa @Temperature 200 °C |
31000 ksi @Temperature 392 °F |
|
Haynes 25 alloy, room temperature after 10% cold reduction, 1120°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |