Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Modulus of Elasticity | 2.41 GPa | 350 ksi | ASTM D638 |
Novatec Novaloy® 9000 PVC + ABS Novaloy® 9000 is a specialty engineering alloy of ABS/PVC designed for injection molding, profile and sheet extrusion. Novaloy® 9000 has been formulated to provide excellent processing characte.. |
|||
Modulus of Elasticity | 2.41 - 2.81 GPa @Temperature 30.0 - 120 °C |
350 - 408 ksi @Temperature 86.0 - 248 °F |
Average value: 1.78 GPa Grade Count:1 |
Overview of materials for Acetal Copolymer, Unreinforced This property data is a summary of similar materials in the MatWeb database for the category "Acetal Copolymer, Unreinforced". Each property range of values reported is minimum and maximum values of.. |
|||
Modulus of Elasticity | 2.41 - 2.81 GPa @Thickness 1.50 - 4.00 mm |
350 - 408 ksi @Thickness 0.0591 - 0.157 in |
Average value: 1.78 GPa Grade Count:1 |
Overview of materials for Acetal Copolymer, Unreinforced This property data is a summary of similar materials in the MatWeb database for the category "Acetal Copolymer, Unreinforced". Each property range of values reported is minimum and maximum values of.. |
|||
Modulus of Elasticity | 2.41 - 3.65 GPa | 350 - 530 ksi | Average value: 3.17 GPa Grade Count:8 |
Overview of materials for Polycarbonate, Aramid Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, Aramid Fiber Reinforced". Each property range of values reported is minimum and maximum v.. |
|||
Modulus of Elasticity | 2.41 - 4.50 GPa | 350 - 653 ksi | Average value: 3.73 GPa Grade Count:7 |
Overview of materials for Thermoplastic Polyimide, Unfilled |
|||
Modulus of Elasticity | 2.41 - 4.14 GPa | 350 - 600 ksi | Average value: 3.58 GPa Grade Count:17 |
Overview of materials for Nylon 66, MoS2 Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, MoS2 Filled". Each property range of values reported is minimum and maximum values of appropri.. |
|||
Modulus of Elasticity | 2.41 - 11.0 GPa | 350 - 1600 ksi | Average value: 4.79 GPa Grade Count:42 |
Overview of materials for Nylon 66, Aramid Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Aramid Fiber Filled". Each property range of values reported is minimum and maximum values of .. |
|||
Modulus of Elasticity | 2.41 GPa | 350 ksi | |
Hybrid Plastics Nanoreinforced® POSS® 5% POSS-polyimide Nanoreinforced® POSS® Polyimide is a hybrid nanocomposite that can serve as oxidation resistant and highly bondable form of polyimide. Upon exposure to oxidizing oxygen the POSS® polyimide .. |
|||
Modulus of Elasticity | 2.41 GPa | 350 ksi | Secant; ASTM D882 |
Specialty Coating Systems Parylene N Poly (P-Xylylene) Coating Parylene N, poly(para-xylylene), is a completely linear, highly crystalline material. Parylene N is a primary dielectric, exhibiting a very low dissipation factor, high dielectric strength, and a lo.. |
|||
Modulus of Elasticity | 2.41 - 13.8 GPa | 350 - 2000 ksi | Average value: 6.03 GPa Grade Count:86 |
Overview of materials for Polycarbonate, Glass + PTFE Filled This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, Glass + PTFE Filled". Each property range of values reported is minimum and maximum value.. |
|||
Modulus of Elasticity | 2.41 GPa | 350 ksi | ASTM D790 |
Chesterton ARC CS2 Low-viscosity, Composite concrete primer sealer Description: An advanced composite formulated to protect concrete surfaces from mild chemical attack. It is normally applied at a thickness of 250-375 microns (10-15 mils) per coat. Non-shrinking. 1.. |