- Polymer Property : Modulus of Elasticity = 154 GPa
Polymer Property : Modulus of Elasticity = 154 GPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Modulus of Elasticity | 154 GPa @Temperature 900 °C |
22300 ksi @Temperature 1650 °F |
|
| Haynes 25 alloy, cold worked sheet, 15% cold reduction, aged at 370°C (700°F) for 1 hour Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| Modulus of Elasticity | 154 GPa @Temperature 900 °C |
22300 ksi @Temperature 1650 °F |
|
| Haynes 25 alloy, hot rolled and 1230°C solution annealed sheet Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| Modulus of Elasticity | 154 GPa @Temperature 815 °C |
22300 ksi @Temperature 1500 °F |
|
| Haynes HR-160® alloy plate, aged 1000 hours at 649°C (1200°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
| Modulus of Elasticity | 154 GPa @Temperature 815 °C |
22300 ksi @Temperature 1500 °F |
|
| Haynes HR-160® alloy, hot rolled and solution annealed plate Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
| Modulus of Elasticity | 154 GPa @Temperature 815 °C |
22300 ksi @Temperature 1500 °F |
|
| Haynes HR-160® alloy, plate, aged 1000 hours at 760°C (1400°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
| Modulus of Elasticity | 154 GPa @Temperature 815 °C |
22300 ksi @Temperature 1500 °F |
|
| Haynes HR-160® alloy, plate, aged 8000 hours at 760°C (1400°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
| Modulus of Elasticity | 154 GPa @Temperature 900 °C |
22300 ksi @Temperature 1650 °F |
|
| Haynes 25 alloy, cold worked sheet, 10% cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| Modulus of Elasticity | 154 GPa @Temperature 900 °C |
22300 ksi @Temperature 1650 °F |
|
| Haynes 25 alloy, room temperature sheet after 1000 hours of 870°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| Modulus of Elasticity | 154 GPa @Temperature 900 °C |
22300 ksi @Temperature 1650 °F |
|
| Haynes 25 alloy, room temperature sheet after 2500 hours of 650°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| Modulus of Elasticity | 154 GPa @Temperature 900 °C |
22300 ksi @Temperature 1650 °F |
|
| Haynes 25 alloy, room temperature sheet after 500 hours of 650°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| Modulus of Elasticity | 154 GPa @Temperature 900 °C |
22300 ksi @Temperature 1650 °F |
|
| Haynes 25 alloy, room temperature sheet after 500 hours of 870°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| Modulus of Elasticity | 154 GPa @Temperature 900 °C |
22300 ksi @Temperature 1650 °F |
|
| Haynes 263® alloy, cold rolled sheet, solution treated and aged Very good aged strength properties, excellent fabrication characteristics when annealed, excellent intermediate temperature tensile ductility, is not normally subject to strain age cracking, excelle.. |
|||
| Modulus of Elasticity | 154 GPa @Temperature 871 °C |
22300 ksi @Temperature 1600 °F |
heat-treated at 1121°C (2050°F), rapid quenched, plate |
| Haynes Hastelloy® C-22® alloy, 10% cold worked sheet HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
| Modulus of Elasticity | 154 GPa @Temperature 871 °C |
22300 ksi @Temperature 1600 °F |
heat-treated at 1121°C (2050°F), rapid quenched, plate |
| Haynes Hastelloy® C-22® alloy, 30% cold worked sheet HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
| Modulus of Elasticity | 154 GPa @Temperature 871 °C |
22300 ksi @Temperature 1600 °F |
heat-treated at 1121°C (2050°F), rapid quenched, plate |
| Haynes Hastelloy® C-22® alloy, 40% cold worked sheet HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
| Modulus of Elasticity | 154 GPa @Temperature 871 °C |
22300 ksi @Temperature 1600 °F |
heat-treated at 1121°C (2050°F), rapid quenched, plate |
| Haynes Hastelloy® C-22® alloy, 40% cold worked sheet, aged 100 hours at 500°C HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
| Modulus of Elasticity | 154 GPa @Temperature 871 °C |
22300 ksi @Temperature 1600 °F |
heat-treated at 1121°C (2050°F), rapid quenched, plate |
| Haynes Hastelloy® C-22® alloy, 60% cold worked sheet, aged 100 hours at 500°C HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
| Modulus of Elasticity | 154 GPa @Temperature 871 °C |
22300 ksi @Temperature 1600 °F |
heat-treated at 1121°C (2050°F), rapid quenched, plate |
| Haynes Hastelloy® C-22® alloy, GTAW, aged 4000 hours at 450°C (800°F), notched HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
| Modulus of Elasticity | 154 GPa @Temperature 871 °C |
22300 ksi @Temperature 1600 °F |
heat-treated at 1121°C (2050°F), rapid quenched, plate |
| Haynes Hastelloy® C-22® alloy, SMAW weld, 316L base metal, C-22 weld metal HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
| Modulus of Elasticity | 154 GPa @Temperature 871 °C |
22300 ksi @Temperature 1600 °F |
heat-treated at 1121°C (2050°F), rapid quenched, plate |
| Haynes Hastelloy® C-22® alloy, transverse, GMAW short arc weldment, plate HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
| Modulus of Elasticity | 154 GPa @Temperature 900 °C |
22300 ksi @Temperature 1650 °F |
|
| Haynes 25 alloy, room temperature after 0% cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
| Modulus of Elasticity | 154 GPa @Temperature 900 °C |
22300 ksi @Temperature 1650 °F |
|
| Haynes 25 alloy, room temperature after 10% cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
| Modulus of Elasticity | 154 GPa @Temperature 900 °C |
22300 ksi @Temperature 1650 °F |
|
| Haynes 25 alloy, room temperature after 10% cold reduction, 1065°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
| Modulus of Elasticity | 154 GPa @Temperature 900 °C |
22300 ksi @Temperature 1650 °F |
|
| Haynes 25 alloy, room temperature after 15% cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
| Modulus of Elasticity | 154 GPa @Temperature 900 °C |
22300 ksi @Temperature 1650 °F |
|
| Haynes 25 alloy, room temperature after 15% cold reduction, 1120°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
| Modulus of Elasticity | 154 GPa @Temperature 871 °C |
22300 ksi @Temperature 1600 °F |
heat-treated at 1121°C (2050°F), rapid quenched, plate |
| Haynes Hastelloy® C-22® alloy, all-weld metal, SMAW HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
| Modulus of Elasticity | 154 GPa @Temperature 871 °C |
22300 ksi @Temperature 1600 °F |
heat-treated at 1121°C (2050°F), rapid quenched, plate |
| Haynes Hastelloy® C-22® alloy, GMAW, as welded, notched HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
| Modulus of Elasticity | 154 GPa @Temperature 871 °C |
22300 ksi @Temperature 1600 °F |
heat-treated at 1121°C (2050°F), rapid quenched, plate |
| Haynes Hastelloy® C-22® alloy, GTAW weld, 904L base metal, C-22 weld metal HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
| Modulus of Elasticity | 154 GPa @Temperature 871 °C |
22300 ksi @Temperature 1600 °F |
heat-treated at 1121°C (2050°F), rapid quenched, plate |
| Haynes Hastelloy® C-22® alloy, GTAW, as welded, unnotched HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
| Modulus of Elasticity | 154 GPa @Temperature 900 °C |
22300 ksi @Temperature 1650 °F |
|
| Haynes 25 alloy, room temperature after 15% cold reduction, 1065°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||