Polymer Property : Tensile Creep Modulus, 1 hour = 479000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Creep Modulus, 1 hour	3300 - 7700 MPa	479000 - 1.12e+6 psi	Average value: 4770 MPa Grade Count:3
Overview of materials for Acetal Copolymer, 30% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Acetal Copolymer, 30% Glass Fiber Reinforced". Specific grades with glass content between 25% and 34% ar..
Tensile Creep Modulus, 1 hour	3300 MPa	479000 psi	ISO 899-1
Lanxess PocanÂ® B 7425 000000 PBT, 20% Glass Spheres PBT, 20% glass spheres, injection molding, low tendency to warp, improved surface finish
Tensile Creep Modulus, 1 hour	3300 MPa	479000 psi	ISO 899
Styrolution PS 165 N/L GPPS Styrolution PS 165N/L is a high molecular weight, good flowing grade, often blended with high impact extrusion grades.High molecular weightGood flow characteristicsAppropriate for blending with HIPS..
Tensile Creep Modulus, 1 hour	3300 MPa	479000 psi	ISO 899
Styrolution PS 168 N/L GPPS Styrolution PS 168N/L is a high molecular weight, heat resistant grade with high mechanical strength. It is suitable for physically or chemically expanded extruded sheet. It is also suitable for use..
Tensile Creep Modulus, 1 hour	3300 MPa	479000 psi	ISO 899
Styrolution PS 168N GPPS Styrolution PS 168N is a high molecular weight, heat resistant grade used where high strength is required. Suitable for physically or chemically expanded extruded sheet. Also use as a blend componen..
Tensile Creep Modulus, 1 hour	3300 MPa	479000 psi	ISO 899
Styrolution PS 158 N/L GPPS Styrolution PS 158N/L is a heat resistant, rapid freezing general purpose grade. It is suitable for expanded sheet and film; for blends with high impact polystyrene in heat contact applications; for..
Tensile Creep Modulus, 1 hour	3300 MPa	479000 psi	ISO 899
Styrolution PS 158K GPPS Styrolution PS 158K is a heat resistant, rapid freezing general purpose grade. It is suitable for expanded sheet and film; for blends with high impact Styrolution PS in heat contact applications; fo..
Tensile Creep Modulus, 1 hour	3300 MPa @Time 3600 sec	479000 psi @Time 1.00 hour	50%RH; ISO 899-1
DuPont Performance Polymers Zytel® 70G13HS1L NC010 Nylon 66 (Unverified Data**) 13% Glass Reinforced Heat Stabilized Polyamide 66 Zytel 70G13HS1L NC010 is a 13% glass fiber reinforced heat stabilized polyamide 66 resin for injection molding.Information provided by DuPont Perfor..
Tensile Creep Modulus, 1 hour	3300 MPa	479000 psi
BASF Polystyrol® 165 H Polystyrene (Europe) High molecular grades, often blended with high-impact extrusion grades (e.g. for dairy products).Data was collected by ISO methods and provided by BASF.
Tensile Creep Modulus, 1 hour	3300 MPa	479000 psi
BASF Polystyrol® 168 N Polystyrene (Europe) High molecular, heat-resistant grades used where high strength is required. Suitable for expanded film.Data was collected by ISO methods and provided by BASF.
Tensile Creep Modulus, 1 hour	3300 MPa	479000 psi
BASF Polystyrol® 158 K Polystyrene (Global) Heat-resistant, rapid freezing general-purpose grade. Suitable for expanded film and for blending with Styrolux and impact-modified Polystyrol in heat contact applications (e.g. coffee cups).Data w..