Mechanical Properties | Metric | English | Comments |
---|---|---|---|
100% Modulus | 0.00670 GPa | 0.972 ksi | Die C; Cross direction; ASTM D412 |
Teknor Apex Sarlink® 4190 Thermoplastic Elastomer A highly engineered Thermoplastic Elastomer for use in demanding applications. Sarlink® 4190 is a medium hardness grade possessing exceptional tensile strength, superior compression set, chemical.. |
|||
100% Modulus | 0.00670 GPa | 0.972 ksi | Die C; Cross direction; ASTM D412 |
Teknor Apex Sarlink® 4490 Thermoplastic Elastomer A NSF certified, highly engineered Thermoplastic Elastomer for use in demanding applications. Sarlink® 4490 is a medium hardness grade possessing exceptional tensile strength, superior compressio.. |
|||
100% Modulus | 0.00670 GPa | 0.972 ksi | Cured 10 minutes at 180°C |
DuPont Vamac® DP 4.5 phr Peroxide Test Compound Vamac® DP is an ethylene acrylic dipolymer elastomer. Its general performance characteristics are similar to those of the Vamac® terpolymers, including:Good oil and chemical resistanceHigh temper.. |
|||
100% Modulus | 0.00670 GPa @Temperature 23.0 °C |
0.972 ksi @Temperature 73.4 °F |
12 months, Weathering @ 45° South, 12 mil - Black, Shelf |
Lubrizol Estane® 58610 Thermoplastic Polyurethane Features: Combines flexibility, toughness and excellent roll release for calendering and melt coating applications.Uses: Injection molding and general extrusion techniques. It is used in film, shee.. |
|||
100% Modulus | 0.00670 GPa | 0.972 ksi | Press Cure 7 minutes @ 177°C, Post Cure 24 hours @ 260°C |
3M Dyneon™ FC 2230 Fluoroelastomer 3M™ Dyneon™ Fluoroelastomer FC 2230 can be compounded using standard water cooled internal mixers or two-roll mills with standard fillers and ingredients utilized in typical fluoroelastomer formul.. |
|||
100% Modulus | 0.00670 GPa | 0.972 ksi | Cured 7 min at 177°C and Post Cured 16 hr at 232°C |
DuPont Performance Polymers GLT305 Peroxide Cured Fluoroelastomer (FKM) Formulation
(discontinued **) FormulationViton® GLT305 |