Mechanical Properties | Metric | English | Comments |
---|---|---|---|
100% Modulus | 0.00483 GPa | 0.700 ksi | ASTM D412 |
Teknor Apex UNIPRENE® 7400-80 Thermoplastic Elastomer Information provided by Teknor Apex Company |
|||
100% Modulus | 0.00483 GPa | 0.700 ksi | heat aged one week at 300ºF |
TSE Industries Millathane® 5004 Millable Polyurethane Elastomer with 60 PHR N330 (HAF) Black MILLATHANE 5004 is a millable polyurethane elastomer having excellent processing characteristics. MILLATHANE 5004 stocks can be readily processed on conventional rubber equipment. Vulcanization is c.. |
|||
100% Modulus | 0.00483 GPa | 0.700 ksi | |
TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 2.0 PHR DBPH-50 MILLATHANE HT is a polyester millable polyurethane which has the ability to withstand elevated temperatures. Polyurethanes have been known for their excellent resistance to abrasion, impact, tear st.. |
|||
100% Modulus | 0.00483 GPa | 0.700 ksi | ASTM D412 |
Teknor Apex UNIPRENE® 7010-80 Thermoplastic Elastomer Information provided by Teknor Apex Company |
|||
100% Modulus | 0.00483 GPa | 0.700 ksi | ASTM D-638 |
Axiall 6741 Moldings & Extrusions Flexible PVC A low gravity profile extrusion compound recommended for weatherstrips, extruded shapes, hoses and flexible gaskets. Provides good adhesion to rigid PVC in co-extruded products.Information provided.. |
|||
100% Modulus | 0.00483 GPa | 0.700 ksi | After 7 days at 257°F (125°C); ASTM D573; ISO 188 |
Advanced Polymer Alloys Alcryn® 4670 BK Melt Processable Rubber Alcryn melt-processable rubber (MPR) is a true rubber, based on a partially cross-linked, chlorinated olefin interpolymer alloy. Alcryn is designed for the manufacture of rubber parts with high prod.. |
|||
100% Modulus | 0.00483 GPa | 0.700 ksi | Press Cure 5 minutes @ 177°C, Post Cure 24 hours @ 260°C |
3M Dyneon™ FLS 2530 Fluoroelastomer 3M™ Dyneon™ Fluoroelastomer FLS 2530 can be compounded using standard water cooled internal mixers or two-roll mills with standard fillers and ingredients utilized in typical fluoroelastomer formu.. |
|||
100% Modulus | 0.00483 GPa | 0.700 ksi | ASTM D-638 |
Axiall 50897 Moldings & Extrusions Flexible PVC Migration resistant, flexible PVC compound recommended for injection molding and extrusion applications.Information provided by Georgia GulfGeorgia Gulf became Axiall Corporation in 2013. |
|||
100% Modulus | 0.00483 GPa | 0.700 ksi | Press Cure 5 minutes @ 177°C, Post Cure 24 hours @ 260°C |
3M Dyneon™ FE 5622Q Fluoroelastomer 3M™ Dyneon™ Fluoroelastomer FE 5622Q can be compounded using standard water cooled internal mixers or two-roll mills with standard fillers and ingredients utilized in typical fluoroelastomer formu.. |
|||
100% Modulus | 0.00483 GPa | 0.700 ksi | heat aged one week at 300ºF |
TSE Industries Millathane® 5004 Millable Polyurethane Elastomer with 60 PHR N330 (HAF) Black MILLATHANE 5004 is a millable polyurethane elastomer having excellent processing characteristics. MILLATHANE 5004 stocks can be readily processed on conventional rubber equipment. Vulcanization is c.. |
|||
100% Modulus | 0.00483 GPa | 0.700 ksi | ASTM D638 |
Colorite Polymers 6718 General Purpose Vinyl Compound Description: Colorite produces many vinyl compounds. They have the compounds that perfectly suit whatever the application. Requirements such as ultraviolet ray resistance, fungus resistance, flame r.. |
|||
100% Modulus | 0.00483 GPa | 0.700 ksi | ASTM D638 |
Colorite Polymers Vinylbond 96-1203-40 Compound Description: Vinylbond 96-1203-40 is a flexible vinyl extrusion compound formulated specifically for the window market industry. This particular compound offers excellent bonding characteristics to .. |
|||
100% Modulus | 0.00483 GPa | 0.700 ksi | |
TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 2.0 PHR DBPH-50 MILLATHANE HT is a polyester millable polyurethane which has the ability to withstand elevated temperatures. Polyurethanes have been known for their excellent resistance to abrasion, impact, tear st.. |
|||
100% Modulus | 0.00483 GPa | 0.700 ksi | Press Cure 7 minutes @ 177°C, Post Cure 24 hours @ 260°C |
3M Dyneon™ FC 2177D Fluoroelastomer 3M™ Dyneon™ Fluoroelastomer FC 2177D can be compounded using standard water cooled internal mixers or two-roll mills with standard fillers and ingredients utilized in typical fluoroelastomer formu.. |
|||
100% Modulus | 0.00483 GPa | 0.700 ksi | ASTM D-638 |
Axiall 4750 Flexible PVC General purpose molding and extrusion compound well suited for automotive floor mats.Information provided by Georgia GulfGeorgia Gulf became Axiall Corporation in 2013. |