Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Compressive Strength | 234 MPa @Thickness 12.7 mm |
34000 psi @Thickness 0.500 in |
ASTM D695 |
Industrial Laminates/Norplex NP310 Cotton Fabric Description: Canvas machining grade for structural and mechanical applications. Better impact strength than phenolic paper grades. MIL-I-24768/16. Thickness Tested: 0.062, 0.125", and 0.500". |
|||
Compressive Strength | 234 MPa @Thickness 12.7 mm |
34000 psi @Thickness 0.500 in |
ASTM D695 |
Industrial Laminates/Norplex NP310E Cotton Fabric Description: Manufactured with a domestic cotton fabric and phenolic resin. Similar to NP310 with improved moisture resistance and electrical properties. Mechanical properties equivalent to NP310. M.. |
|||
Compressive Strength | 234 MPa @Thickness 12.7 mm |
34000 psi @Thickness 0.500 in |
ASTM D695 |
Industrial Laminates/Norplex NP329 Cotton Fabric Description: Bleached linen with melamine resin system. Provides better arc resistance than NP320E. Also, resistant to ammonia based refrigerants. Hard, durable material should be heated to punch, .. |
|||
Compressive Strength | 234 - 241 MPa | 34000 - 35000 psi | |
Bulk Molding Compounds BMC 1608 Very High Strength, Corrosion Resistant BMC 1608 is a very high strength, general purpose, corrosion resistant material. Recommended for compression molding only. UL® recognized. Meets FDA requirements for food contact. This material was.. |
|||
Compressive Strength | 234 MPa @Thickness 12.7 mm |
34000 psi @Thickness 0.500 in |
ASTM D695 |
Industrial Laminates/Norplex NP321 Cotton Fabric
(discontinued **) Description: NP321 consists of a fine weave cotton fabric (linen) impregnated with a phenolic resin binder. Applications include vanes for air and liquid pumps, and compressors. NP321 remains very f.. |