Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Compressive Strength | 90.0 - 147 MPa | 13100 - 21300 psi | Type B, 5mm/min; ISO 604:2002 |
Nylacast H.S. Blue Cast Nylon 6, Heat Stabilized HS Blue is a heat Stabilised Cast Nylon 6. Its mechanical properties are maintained when operating at higher temperature and improves mechanical properties. This helps to reduce the stress distortio.. |
|||
Compressive Strength | 90.0 MPa | 13100 psi | ASTM D695 |
IDI Composites 46-3 Thermoset Polyester, Molding Superior electrical performance with low pressure molding for V-O flammability in encapsulation applications.Data provided by the manufacturer. |
|||
Compressive Strength | 90.0 MPa | 13100 psi | Sample Type B, 5 mm/min; ISO 604:2002 |
Global EPP PA 66E Extruded Polyamide 66 Polyamides, commonly referred to as nylons, are macromolecular, partially crystalline thermoplastics. Their physical properties are mainly determined by the composition and structure of their molecu.. |
|||
Compressive Strength | 90.0 MPa | 13100 psi | Sample Type B, 5 mm/min; ISO 604:2002 |
Global EPP PA 6C IMPACT Cast Polyamide 6 + Plasticizer Cast nylons are generally accepted as the primary engineering polymer, suitable for virtually any plain bearing application. By varying the conditions of polymerisation the mechanical properties of .. |
|||
Compressive Strength | 90.0 MPa | 13100 psi | Sample Type B, 5 mm/min; ISO 604:2002 |
Global EPP PA 6E Extruded Polyamide 6 Polyamides, commonly referred to as nylons, are macromolecular, partially crystalline thermoplastics. Their physical properties are mainly determined by the composition and structure of their molecu.. |
|||
Compressive Strength | 90.0 MPa | 13100 psi | Cold Crushing Strength |
Gouda Vuurvast AK 60 AP Dense Refractory Brick Description: This phosphate bonded brick combines a very good thermal shock resistance with high slag resistance and low creep. Application: frit melting furnaces, incinerators, burner blocks, lime .. |
|||
Compressive Strength | 90.0 MPa | 13100 psi | |
Haysite 14100 Polyester BMC, 15% Glass Reinforced The 14100 series bulk molding compound is an electrical grade material that can be compression, transfer, or injection molded. Offering good mechanical strength and excellent electrical properties, .. |
|||
Compressive Strength | 90.0 MPa | 13100 psi | |
Haysite 20000 Polyester BMC, 15% Glass Reinforced The 20000 series bulk molding compound is an electrical grade that can be compression, transfer, or injection molded. Offering good arc/track properties and mechanical strength, this grade is also r.. |
|||
Compressive Strength | 90.0 MPa | 13100 psi | Sample Type B, 5 mm/min; ISO 604:2002 |
Global EPP PA 612 Copolymer Cast Polyamide 612 Cast nylons are generally accepted as the primary engineering polymer, suitable for virtually any plain bearing application. By varying the conditions of polymerisation the mechanical properties of .. |
|||
Compressive Strength | 90.0 MPa | 13100 psi | Cold Crushing Strength |
Gouda Vuurvast AK 85 KM Dense Refractory Brick Description: This brick based on mullite and corundum, is characterized by a very low porosity, high slag resistance, low creep and very good thermal shock resistance.Remarks: This data represents a.. |
|||
Compressive Strength | 90.0 MPa | 13100 psi | 20% pressing; EN ISO 604 |
Schwartz Technical Plastics LAMIGAMID® 310 Cast Polyamide 6, Conditioned Application: sheaves, wheels, rollers, mandrell segments, coupling parts, vibrator parts etc.Information provided by Schwartz Technical Plastics GmbH |
|||
Compressive Strength | 90.0 MPa | 13100 psi | 20% pressing; EN ISO 604 |
Schwartz Technical Plastics LAMIGAMID® 310 Cast Polyamide 6, Dry Application: sheaves, wheels, rollers, mandrell segments, coupling parts, vibrator parts etc.Information provided by Schwartz Technical Plastics GmbH |
|||
Compressive Strength | 90.0 MPa | 13100 psi | Absolute Drying; ASTM-D695 |
Toyobo GLAMIDE® T-662 Nylon-66 GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing a.. |
|||
Compressive Strength | 90.0 MPa | 13100 psi | Absolute Drying; ASTM-D695 |
Toyobo GLAMIDE® TY-835TC Nylon-66 GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing a.. |
|||
Compressive Strength | 90.0 MPa @Temperature 23.0 °C |
13100 psi @Temperature 73.4 °F |
ASTM D695 |
Toyobo T-661 Nylon 66, Standard Grade (DAM) Features: Non-reinforced, Standard GradeInformation provided by Toyobo. |
|||
Compressive Strength | 90.0 MPa | 13100 psi | ISO 604 |
Chevron Phillips Xtel® XE3035BL Polyphenylene Sulfide Alloy Xtel® XE3035BL is a high performance, glass fiber reinforced, PPS based alloy developed to provide exceptionally high ductility and impact resistance along with good thermal stability.Information p.. |
|||
Compressive Strength | 90.0 MPa | 13100 psi | ISO 604 |
Chevron Phillips Xtel® XE3035NA Polyphenylene Sulfide Alloy Xtel® XE3035NA is a high performance, glass fiber reinforced, PPS based alloy developed to provide exceptionally high ductility and impact resistance along with good thermal stability.Information p.. |
|||
Compressive Strength | >= 90.0 MPa | >= 13100 psi | Perpendicular to laminations; IEC 1212-2 5.3 |
Hippe MF CC 201 Woven Cotton Cloth Reinforced Melamine Resin - Sheet Used in mechanical and electrical applications (coarse weave: >130 g/m2, =30 threads/cm). Arc and tracking resistant.Information provided by Hippe. |
|||
Compressive Strength | >= 90.0 MPa | >= 13100 psi | Axial; IEC 1212-2 4.2 |
Hippe PF CC 41 Woven Cotton Cloth Reinforced Phenolic Resin - Round, Molded Tube and Rod Used in mechanical and electrical applications. Fine weave (more than 30 threads per cm).Information provided by Hippe. |
|||
Compressive Strength | 90.0 - 105 MPa | 13100 - 15200 psi | GB/T 1040 |
Beijing Evergrow Resources MoS2 Filled Nylon Information provided by Beijing Evergrow Resources. |