Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Compressive Strength | 6.00 MPa | 870 psi | 1% strain over 1000 hours; ISO.899 DIN.53444 |
Omnia Plastica Akulon® PA6 G.Oil - Omniamid Oil - at 50% RH Cast Nylon 6 with the addition of 6% of special lubricating oil which remains in solution in the material. The unique method of production results in a micro distribution of oil particles with a hom.. |
|||
Compressive Strength | 6.00 MPa | 870 psi | 1% strain over 1000 hours; ISO.899 DIN.53444 |
Omnia Plastica Omniamid PA 6 - Akulon 6 - at 50% RH Semi-crystalline polymer of polyamide obtained by the polymerisation of the caprolactam. Its large popularity is due to both its good overall features as well as its cost-performance relationship. T.. |
|||
Compressive Strength | 6.00 MPa | 870 psi | 1% strain over 1000 hours; ISO.899 DIN.53444 |
Omnia Plastica Omniamid PA6 GHR - HR - at 50% RH Cast nylon 6 produced with the addition of graphite and a special lubricator which gives to this product better properties than natural PA6G. Whilst retaining the general features of OMNIAMID G it i.. |
|||
Compressive Strength | 6.00 MPa | 870 psi | Solid; ASTM D1621 |
Sawbones Fourth-Generation Simulated Cancellous Bone (Rigid Polyurethane Bone) Fourth-generation bones model natural cortical bone using a mixture of short glass fibers and epoxy resin pressure injected around a foam core. Standard bone models are manufactured with a solid rig.. |
|||
Compressive Strength | 6.00 MPa @Strain 3.50 % |
870 psi @Strain 3.50 % |
DIN EN ISO 604 |
Wolf Kunststoff ZEDEX® ZX-100EL55 A1F Polymer Alloy, Elastomer Modified Main Characteristics: Rubbery; Soft; High shock absorption; High impact resistance; Elongation > 300%Applications: Handling, Vessel and Pump, Steel and Water, Chemical Engineering, Automitve Technol.. |
|||
Compressive Strength | 6.00 MPa | 870 psi | In the In Plane Direction |
Cymat A35620SC 040SS Stabilized Aluminum Foam Description: Cymat A35620SC 040SS stabilized aluminum foam (SAF) is a closed cell aluminum foam formed from A356 aluminum alloy with a density of 0.4 g/cm3. The mechanical properties of SAF make it .. |