Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Compressive Strength | 133 MPa @Temperature 204 °C |
19300 psi @Temperature 400 °F |
|
Haysite Heatmeiser® H340 Platen Insulation Haysite’s family of mold and platen insulation products are specially engineered fiberglass reinforced thermoset polyester composites which offer superior energy efficiency, temperature control.. |
|||
Compressive Strength | 133 MPa | 19300 psi | break; DIN EN ISO 604 |
Wolf Kunststoff ZEDEX® ZX-410V7T A4T Polymer Alloy, Fiber Reinforced, Friction Modified Main Characteristics: Fiber-reinforced; Friction-modified; Very high stiffness (higher than that of fiber-reinforced PEEK); Very low thermal expansion coefficient; Low friction; High wear resistance.. |
|||
Compressive Strength | 133 MPa | 19300 psi | ASTM D695 |
Ensinger HYDLAR® Z Nylon, Pultruded Aramid Fiber Reinforced (PA) HYDLAR® possesses a combination of physical properties that cannot be found in any other commercially available engineered plastic. Design engineers have created a family of superior wear and abra.. |
|||
Compressive Strength | <= 133 MPa | <= 19300 psi | ASTM D695 |
Ensinger Tecapeek® XP-102 Compression Molded PEEK Compound, Filled with 15% Graphite and 10% PTFE Ensinger Special Polymers offers over twenty different VICTREX® PEEK blends to choose from and has the capability to blend custom compounds for specific applications. Compression molding results in.. |
|||
Compressive Strength | 133 MPa | 19300 psi | 10% Deformation; ASTM D695 |
Ensinger Tecapeek® XP-96 Compression Molded PEEK Ensinger Special Polymers offers over twenty different VICTREX® PEEK blends to choose from and has the capability to blend custom compounds for specific applications. Compression molding results in.. |
|||
Compressive Strength | 133 MPa | 19300 psi | 10% Deformation; ASTM D695 |
Ensinger Tecapeek® XP-96B Compression Molded PEEK, Unfilled, Black Pigmented Ensinger Special Polymers offers over twenty different VICTREX® PEEK blends to choose from and has the capability to blend custom compounds for specific applications. Compression molding results in.. |
|||
Compressive Strength | 133 MPa @Temperature 23.0 °C |
19300 psi @Temperature 73.4 °F |
EN ISO 604 |
Ensinger TECASINT 3032 Polyimide, Black, 40% Graphite (PI) TECASINT is a range of non-melting high temperature polyimides characterized by high strength over a wide range of temperatures, good long term thermal stability, minimal thermal expansion and excel.. |
|||
Compressive Strength | 133 - 161 MPa | 19300 - 23300 psi | |
Bulk Molding Compounds BMC T40(20) Die Casting Replacement Grade Molding Compound BMC T40(20) was formulated as a direct replacement for aluminum die casting applications. T40(20) is UL recognized. Excellent mechanical properties and dimensional control allow molded parts to ma.. |