Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength | >= 12.0 MPa | >= 1740 psi | Type IV, 500mm/min; ISO 37 |
S&E Specialty Polymers XP23-45 PVC Description: PVC weatherable, integral colored, filledApplication: Body side molding and wind shield molding which meets GMW16084 Type 4, Grade E, Class B, GMP.PVC.003 & Ford WSK-M4D689-A3Informatio.. |
|||
Tensile Strength | 12.0 MPa | 1740 psi | ISO 527 |
Premix Thermoplastics PRE-ELEC® PE 1297 Conductive Thermoplastic Compound PRE-ELEC® PE 1297 is a conductive thermoplastic compound based on PE-HD. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PRE-ELEC® PE.. |
|||
Tensile Strength | >= 12.0 MPa | >= 1740 psi | DIN 53504 |
NEXA® PFX8050 Perfluoroelastomer NEXA produces sealing elements for extreme and critical applications, particularly where high temperature, wet conditions (steam/water), purity and chemical resistance are important factors to consi.. |
|||
Tensile Strength | 12.0 MPa | 1740 psi | ASTM D2095 |
Permabond UV670 UV-curable Adhesive PERMABOND UV670 is a single part, fast curing, UV curable adhesive. The cured adhesive is tough, flexible and has excellent impact resistance. Permabond UV670 is well suited for bonding glass to met.. |
|||
Tensile Strength | 12.0 MPa | 1740 psi | Type IV 500mm/min; ASTM D638 |
S&E Specialty Polymers TufTech™ XP-116-221(1) PVC Compound Application: Automotive – PVC, integral colored, exterior weatherable, extrusion & injection molding compoundInformation provided by S&E Specialty Polymers |
|||
Tensile Strength | 12.0 MPa | 1740 psi | ISO 37 |
Kraton® D42070 B (O/E SBS) Branched Copolymer Description: Kraton® D4270B is an oiled, branched copolymer based on styrene and butadiene with a polystyrene content of 32%. It is supplied from South America in the physical form identified: D4.. |
|||
Tensile Strength | 12.0 MPa | 1740 psi | ISO 37 |
Kraton® D4270 J (O/E SBS) Branched Block Copolymer Description: Kraton D4270 J is an oil-extended branched block copolymer based on styrene and butadiene, with bound styrene in the neat polymer of 32% mass. It is supplied from Japan in the physical .. |
|||
Tensile Strength | >= 12.0 MPa | >= 1740 psi | extruded; ASTM D4894, ASTM D4745 |
Guarniflon PTFE G453 Polytetrafluoroethylene 25% Carbographite PTFE G Standard Compound with carbon..Properties: Good thermal and electrical conductivity. Good resistance to deformation. Excellent resistance to load with low coefficient of friction and high .. |
|||
Tensile Strength | 12.0 - 16.0 MPa | 1740 - 2320 psi | molded; ASTM D4745 |
Guarniflon PTFE G456 Polytetrafluoroethylene 25% Hard Carbon PTFE G Special Compound with carbon..Properties: Good thermal and electrical conductivity. Good resistance to deformation. Excellent resistance to load with low coefficient of friction and high w.. |
|||
Tensile Strength | 12.0 MPa | 1740 psi | |
Momentive Performance Materials Addisilâ„¢ 1140 M Industrial Molding Heat Cured Rubber Heat cured rubber is a high consistency product that can be molded, extruded or calendered using conventional rubber processing equipment to meet a wide range of cost, durability and performance sta.. |
|||
Tensile Strength | 12.0 MPa | 1740 psi | MD |
JPJ Technologies LLDPE Virgin for Masterbatches Information provided by JPJ Technologies |
|||
Tensile Strength | 12.0 MPa | 1740 psi | |
Momentive Performance Materials Silplusâ„¢ 50 HS High Strength Heat Cured Rubber Heat cured rubber is a high consistency product that can be molded, extruded or calendered using conventional rubber processing equipment to meet a wide range of cost, durability and performance sta.. |
|||
Tensile Strength | 12.0 MPa | 1740 psi | |
Sawbones Solid Rigid Polyurethane Foam 30 pcf Density Solid Rigid Polyurethane FoamPrimary UseSolid rigid polyurethane foam is primarily used as an alternative test medium for human cancellous bone. These products are not intended to replicate the mech.. |
|||
Tensile Strength | 12.0 - 25.0 MPa | 1740 - 3630 psi | Moulding Direction; BS2782:Pt3 |
Dalau Dalcon 021 75% Virgin PTFE, 25% Carbon Coke Applications & Industries: General: Carbon / Coke (soft) filler is good in dry running conditions, adds to the creep resistance, increases the hardness and raises the thermal conductivity of PTFE; C.. |
|||
Tensile Strength | 12.0 MPa | 1740 psi | DIN EN ISO 527 |
Wolf Kunststoff ZEDEX® ZX-550PV A7A Polymer Alloy Main Characteristics: Modified friction wear; Tough; Soft; Reduced wear at temperatures at 100 ° CApplications: Chemical Engineering; Laboratory Technology; Automitve Technology; Machine ToolsInfor.. |
|||
Tensile Strength | 12.0 - 25.0 MPa | 1740 - 3630 psi | Moulding Direction; BS2782:Pt3 |
Dalau Dalcon 021 75% Virgin PTFE, 25% Carbon Coke Applications & Industries: General: Carbon / Coke (soft) filler is good in dry running conditions, adds to the creep resistance, increases the hardness and raises the thermal conductivity of PTFE; C.. |
|||
Tensile Strength | 12.0 MPa | 1740 psi | ISO 527 |
Fainplast Compounds Hax™ HF 417 Flame Retardant Polyolefin Cable Compound Thermoplastic halogen free flame retardant compound based on polyolefins and mineral fillersGrade description:SheathingInformation provided by Fainplast Compounds |
|||
Tensile Strength | 12.0 MPa | 1740 psi | ISO 527 |
Fainplast Compounds Hax™ HF 211 Flame Retardant Polyolefin Cable Compound Thermoplastic halogen free flame retardant compound based on polyolefins and mineral fillersGrade description:Insulation and sheathing, improved processabilityInformation provided by Fainplast Compo.. |
|||
Tensile Strength | 12.0 MPa | 1740 psi | ISO 527 |
Fainplast Compounds Hax™ HF 4021/TC Flame Retardant Polyolefin Cable Compound Thermoplastic halogen free flame retardant compound based on polyolefins and mineral fillersGrade description:Improved flame retardancyInformation provided by Fainplast Compounds |
|||
Tensile Strength | 12.0 MPa | 1740 psi | ISO 527 |
Fainplast Compounds Hax™ HF 4024 Flame Retardant Polyolefin Cable Compound Thermoplastic halogen free flame retardant compound based on polyolefins and mineral fillersGrade description:Insulation and sheathing, improved processabilityInformation provided by Fainplast Compo.. |
|||
Tensile Strength | 12.0 MPa | 1740 psi | Crosslinked specimen; ISO 527 |
Fainplast Compounds Hax™ HFX 521 Crosslinkable HFFR Cable Compound Polyolefin based HFFR silane grafted compound; cross-linkable by heat and moisture and by addition of suitable catalystGrade description:• Oil resistant sheathingInformation provided by Fainplast C.. |
|||
Tensile Strength | 12.0 MPa @Strain 300 % |
1740 psi @Strain 300 % |
ISO 37 |
BASF Elastollan 1185 A M TPUR Description: Thermoplastic Polyether Polyurethane Elastomers with outstanding hydrolysis resistance, low temperature flexibility and resistance to micro-organisms.Typical Applications: Cable sheathi.. |
|||
Tensile Strength | 12.0 MPa @Strain 20.0 % |
1740 psi @Strain 20.0 % |
ISO 37 |
BASF Elastollan C 59 D TPUR Description: Thermoplastic Polyester Polyurethane Elastomers with excellent mechanical properties and chemical resistance, outstanding wear resistance, high tear and tensile strength, good damping c.. |
|||
Tensile Strength | 12.0 MPa @Strain 20.0 % |
1740 psi @Strain 20.0 % |
ISO 37 |
BASF Elastollan 664 DU TPUR Description: Thermoplastic Polyester Polyurethane Elastomers with excellent mechanical properties and wear resistance, good damping characteristics and a high resilience performance.Typical Applicat.. |
|||
Tensile Strength | 12.0 MPa | 1740 psi | |
AlphaGary Megolon™ S336 Low Smoke Halogen Free Highly fire retardant compound for use in demanding fire tests and constructions. Application examples include Data Cables, Optical Cables. |
|||
Tensile Strength | 12.0 MPa | 1740 psi | |
AlphaGary Megolon™ S800 Low Smoke Halogen Free A thermoplastic, halogen free, fire retardant high speed cable sheathing compound for general purpose applications. This product exhibits excellent processing characteristics including the ability t.. |
|||
Tensile Strength | 12.0 MPa | 1740 psi | ISO 527 |
Fainplast Compounds Hax™ HF 213 Flame Retardant Polyolefin Cable Compound Thermoplastic halogen free flame retardant compound based on polyolefins and mineral fillersGrade description:General purpose, improved processabilityInformation provided by Fainplast Compounds |
|||
Tensile Strength | 12.0 MPa | 1740 psi | wrap; ISO 37 Type 2 |
Rogers Corporation Bisco® A2 R 3.0 Engineered Solid Silicone Mass Layer, Fiberglass Reinforced Sound Barrier BISCO® A2 Fiberglass Reinforced Sound Barrier provides a similar level of sound absorption and flame resistance as the non-reinforced A2 Sound Barrier with the addition of increased tensile and tea.. |