Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength | >= 862 MPa | >= 125000 psi | |
Eagle Brass 301 Austenitic Stainless Steel, 1/4 Hardened Type 301 is a chromium-nickel stainless steel that provides high strength and good ductility with chromium and nickel contents lowered to increase the work hardening range. This permits higher tens.. |
|||
Tensile Strength | >= 862 MPa | >= 125000 psi | |
Eagle Brass 302 Austenitic Stainless Steel, 1/4 Hardened Types 302 is a widely used variation of the basic 18-8 grade with variations of nickel, chromium and carbon content. It is weakly magnetic when cold rolled.Information provided by Eagle Brass Compa.. |
|||
Tensile Strength | >= 862 MPa | >= 125000 psi | |
Eagle Brass 305 Austenitic Stainless Steel, 1/4 Hardened Type 305 is a chromium nickel stainless steel that can be spun and deep drawn more easily due to an increased nickel content that decreases work hardening. It is nonmagnetic under most conditions. .. |
|||
Tensile Strength | >= 862 MPa | >= 125000 psi | |
Eagle Brass 316 Austenitic Stainless Steel, 1/4 Hardened The Mo addition increases general corrosion resistance to pitting from chloride ion solutions, and provides increased strength at elevated temperatures. Properties are similar to those of Type 304 .. |
|||
Tensile Strength | >= 862 MPa | >= 125000 psi | |
Eagle Brass 316L Austenitic Stainless Steel, 1/4 Hardened Type 316L is an extra-low carbon version of Type 316 that minimizes carbide precipitation. Typical uses include exhaust manifolds, furnace parts, heat exchangers, jet engine parts, pharmaceutical a.. |
|||
Tensile Strength | 862 MPa | 125000 psi | |
Chicago Extruded Metals BioBrass® UNS C95520 As-Cast Aluminum Bronze This alloy is registered with the U.S. EPA as Antimicrobial.Information provided by Chicago Extruded Metals |
|||
Tensile Strength | >= 862 MPa | >= 125000 psi | |
Eagle Brass 304 Austenitic Stainless Steel, 1/4 Hardened Types 304 is a widely used variation of the basic 18-8 grade with variations of nickel, chromium and carbon content. It is weakly magnetic when cold rolled.Information provided by Eagle Brass Compa.. |
|||
Tensile Strength | >= 862 MPa | >= 125000 psi | |
Eagle Brass 304L Austenitic Stainless Steel, 1/4 Hardened Type 304L is a very common variation of the basic 18-8 grade with variations of nickel, chromium and carbon content. It is weakly magnetic when cold rolled. Lower carbon 304L minimizes chromium ca.. |
|||
Tensile Strength | 862 MPa @Temperature -5.56 °C |
125000 psi @Temperature 22.0 °F |
Heat Treated to 24-32 HRC |
Schmolz + Bickenbach Holder Block Plastic Mold Steel Description: Holder Block is a modified AISI-4130 material with higher chromium and molybdenum content specifically designed holder steel for molds and dies and The material is forged on a 5000 ton.. |