Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength | 165 MPa | 23900 psi | ASTM D638 |
NHEP Spectron™ E5469 Nylon 66, 33% Glass Fiber Natural color. E5469 exhibits high rigidity, mechanical strength, and excellent appearance. It is suitable for wide range of applications.Property data measured at room temperature, 50% RH.Informat.. |
|||
Tensile Strength | 165 MPa | 23900 psi | ASTM D638 |
NHEP Spectron™ E6666 Nylon 66, 30% Glass Fiber Natural color. E6666 exhibits high rigidity, mechanical strength, and excellent appearance. It is suitable for wide range of applications.Property data measured at room temperature, 50% RH.Informati.. |
|||
Tensile Strength | 165 MPa | 24000 psi | ASTM D638 |
Quantum PEEK 30% Glass Fiber Filled Information provided by Quantum Advanced Engineering Plastics |
|||
Tensile Strength | 165 MPa | 23900 psi | ASTM D638 |
PolyOne Bergamid™ XP6042701 Polyamide 6 (Nylon 6) Injection Speed: 50 to 80% Holding Time: 3 to 9 sec Injection Time: 1 to 3.5 sec Cycle Time: 18 to 60 secInformation provided by PolyOne |
|||
Tensile Strength | 165 MPa @Temperature 23.0 °C |
23900 psi @Temperature 73.4 °F |
DAM; ASTM D638 |
DuPont Performance Polymers Zytel® 77G33L BK031 Nylon 612
(Unverified Data**) Zytel® 77G33L BK031 is a 33% glass fiber reinforced, black polyamide 612 resin for injection molding.Information provided by DuPont Performance Polymers |
|||
Tensile Strength | 165 MPa | 23900 psi | ASTM D638 |
Kuraray Genestarâ„¢ G1302 Nylon, 30% Glass Filled Abrasion Resistance HB grade. Halogen free, following the standards that Br is less than 900ppm, Cl is less than 900ppm, and total of halogen amount (Br and Cl) is less than 1500ppm. It delivers low.. |
|||
Tensile Strength | 165 MPa | 23900 psi | ASTM D638 |
Kuraray Genestarâ„¢ GN2332 Nylon, 33% Glass Filled High Flow V-0 Grade. Improves flow-ability in thin-walled parts. Used for components requiring high-flowability, such as 0.3 mm pitch connectors. |
|||
Tensile Strength | 165 MPa | 23900 psi | ASTM D638 |
Kuraray Genestarâ„¢ GP2450NH-2 Nylon, 45% Glass Filled Standard V-0 Grade. Halogen free, following the standards that Br is less than 900ppm, Cl is less than 900ppm, and total of halogen amount (Br and Cl) is less than 1500ppm.This grade meets UL94, V-0.. |
|||
Tensile Strength | 165 MPa | 23900 psi | ASTM D638 |
Kuraray Genestarâ„¢ GW2458HF Nylon, 45% Glass Filled Low Warpage, High Flow V-0 Grade. It is suited for low warpage and high flow applications, making it well suited for card connectors. |
|||
Tensile Strength | 165 MPa | 23900 psi | ASTM D638 |
Solvay Specialty Polymers Ryton® R-4-230BL Polyphenylene Sulfide (PPS), 40% Glass Fiber Ryton® R-4-230NA and R-4-230BL 40% glass fiber reinforced polyphenylene sulfide compounds provide reduced flash and improved processability compared to other polyphenylene sulfide injection moldi.. |
|||
Tensile Strength | 165 MPa | 23900 psi | ASTM D638 |
Solvay Specialty Polymers Ryton® R-4-240BL Polyphenylene Sulfide (PPS), 40% Glass Fiber Ryton® R-4-240NA and R-4-240BL 40% glass fiber reinforced polyphenylene sulfide compounds provide enhanced mechanical strength and toughness compared to other polyphenylene sulfide compounds.Feat.. |
|||
Tensile Strength | 165 MPa | 24000 psi | ASTM D638 |
Teknor Apex Chemlon® 340G Nylon 610, Glass Fiber Reinforced Processing Method: Injection Molding Forms: PelletsInformation Provided by Teknor Apex |
|||
Tensile Strength | 165 MPa | 23900 psi | dry; ISO 527 |
Azoty Tarnow™ Tarnamid® T-27 GF40 FRV0 Polyamide 6 - Flame Retarded, Reinforced Flame retarded grades, flammability class V0, reinforced with 40% glass fibers, without addition of any halogen compounds, red phosphorus and asbestos, doesn't release any toxic gases during burning.. |
|||
Tensile Strength | 165 MPa | 23900 psi | Alloy 1100 Property; ASTM D345 |
Arlon 91B32R016AC Aluminum Clad Silicone Press Pad with "C-finish" Design/Construction:Side 2: Alloy 1100 H18 Aluminum FoilSide 1: Cured Silicone RubberThis data represents typical values for the production material and should not be used as material specificatio.. |