Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength | 1100 MPa | 160000 psi | |
Kuraray Vectran® NT 1500/300 LCP Fiber  is a high-performance multifilament yarn spun from liquid crystal polymer (LCP).  fiber exhibits exceptional strength and rigidity. Pound for pound  fiber is five times stronger than steel an.. |
|||
Tensile Strength | >= 1100 MPa @Temperature 427 °C |
>= 160000 psi @Temperature 800 °F |
|
Wingate Alloys Winco 44 Prehardened, Machinable Alloy Steel for Difficult Tooling and Maintenance Applications Winco 44 is a free machining, “ready-to-use” alloy steel. The unique physical and mechanical properties of the grade – at both normal and elevated temperatures – result in outstanding service in.. |
|||
Tensile Strength | 1100 MPa | 160000 psi | |
Wingate Alloys Winco Heat Treated, High Tensile Alloy Steel for Maintenance and Machine Repair Electric furnace grade alloy steel in small heats for superior quality control.Winco is a well balanced machinable alloy made to strict specifications for maximum efficiency under extremely hard usa.. |
|||
Tensile Strength | 1100 MPa | 160000 psi | |
Wingate Alloys Winco TGP Turned, Ground and Polished Heat-Treated High Tensile Alloy Steel Advantages:Turned, ground and polished to precision sizes so it is extremely accurate as to straightness and finish – almost ready for immediate installation.Will withstand shock and vibration to p.. |
|||
Tensile Strength | 1100 MPa | 160000 psi | |
Schmolz + Bickenbach CorroPlast® Plastic Mold Steel Description: CorroPlast® is a pre-hardened, free-machining 400 series stainless steel, specifically developed for mold bases for processing plastic; and Supplied in the pre-hardened condition with .. |
|||
Tensile Strength | 1100 MPa @Temperature -5.56 °C |
160000 psi @Temperature 22.0 °F |
Hardened and tempered to 34 HRC |
Schmolz + Bickenbach Formadur® 2085 Plastic Mold Steel Description: FORMADUR 2085 is a free-machining corrosion-resistant mold frame steelCharacteristics: Lower mold production costs due to improved machinability; Improved corrosion resistance compared .. |