Polymer Property : Linear Mold Shrinkage, Flow = 0.0040 in/in Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Physical Properties	Metric	English	Comments
Linear Mold Shrinkage, Flow	0.0040 - 0.0060 cm/cm @Time 86400 sec	0.0040 - 0.0060 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP DFL22 PC (Asia Pacific) LNP* Lubricomp* DFL22 is a compound based on Polycarbonate resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated.
Linear Mold Shrinkage, Flow	0.0040 - 0.0060 cm/cm @Time 86400 sec	0.0040 - 0.0060 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP LUBRICOMP DFL349 PC (Asia Pacific) LNP LUBRICOMP* DFL349 is a compound based on Polycarbonate resin containing Flame Retardant, Glass Fiber, PTFE. Added features of this material include: Flame Retardant.
Linear Mold Shrinkage, Flow	0.0040 - 0.0060 cm/cm @Time 86400 sec	0.0040 - 0.0060 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP LUBRICOMP DFL349 PC LNP LUBRICOMP* DFL349 is a compound based on Polycarbonate resin containing 20% Glass Fiber, 15% PTFE. Added features of this material include: Flame Retardant, Internally Lubricated.
Linear Mold Shrinkage, Flow	0.0040 - 0.0060 cm/cm @Time 86400 sec	0.0040 - 0.0060 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP RFL36L PA 66 (Asia Pacific) LNP* Lubricomp* RFL36L is a compound based on Nylon 66 resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated, Low Extractible.
Linear Mold Shrinkage, Flow	0.0040 cm/cm @Time 86400 sec	0.0040 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRILOY RF208 PA 66 (Asia Pacific) LNP LUBRILOY* RF208 is a compound based on Nylon 66 resin containing Glass Fiber, Proprietary Lubricant. Added features of this material include: Internally Lubricated.
Linear Mold Shrinkage, Flow	0.0040 - 0.0060 cm/cm @Thickness 3.20 - 4.60 mm	0.0040 - 0.0060 in/in @Thickness 0.126 - 0.181 in	SABIC Method
SABIC Innovative Plastics ValoxÂ® 735 PBT 40% glass/mineral, excellent thermal performance/low shrink. Motorized heating appliances, adaptor rings, oven grills, etc. Black/natural only.This data was supplied by SABIC-IP for the Americas re..
Linear Mold Shrinkage, Flow	0.0040 - 0.0060 cm/cm @Thickness 3.20 - 4.60 mm	0.0040 - 0.0060 in/in @Thickness 0.126 - 0.181 in	SABIC Method
SABIC Innovative Plastics ValoxÂ® 735 PBT (Asia Pacific) 40% glass/mineral, excellent thermal performance/low shrink. Motorized heating appliances, adaptor rings, oven grills, etc. Black/natural only.
Linear Mold Shrinkage, Flow	0.0040 - 0.0060 cm/cm @Thickness 3.20 - 4.60 mm	0.0040 - 0.0060 in/in @Thickness 0.126 - 0.181 in	SABIC Method
SABIC Innovative Plastics ValoxÂ® 735 PBT+PET 40% glass/mineral, excellent thermal performance/low shrink. Motorized heating appliances, adaptor rings, oven grills, etc. Black/natural only.
Linear Mold Shrinkage, Flow	0.0040 - 0.0060 cm/cm @Thickness 1.50 - 3.20 mm	0.0040 - 0.0060 in/in @Thickness 0.0591 - 0.126 in	SABIC Method
SABIC Innovative Plastics ValoxÂ® 855 PBT 15% GR PBTP, UL94 V-0 rated. Improved surface appearance. For external housings: steam irons, appliance housings and lighting parts.
Linear Mold Shrinkage, Flow	0.0040 - 0.0060 cm/cm @Thickness 1.50 - 3.20 mm	0.0040 - 0.0060 in/in @Thickness 0.0591 - 0.126 in	SABIC Method
SABIC Innovative Plastics ValoxÂ® 855 PBT (Asia Pacific) 15% GR PBTP, UL94 V-0 rated. Improved surface appearance. For external housings: steam irons, appliance housings and lighting parts.
Linear Mold Shrinkage, Flow	0.0040 - 0.0060 cm/cm @Thickness 1.50 - 3.20 mm	0.0040 - 0.0060 in/in @Thickness 0.0591 - 0.126 in	SABIC Method
SABIC Innovative Plastics ValoxÂ® DR48 PBT (Asia Pacific) 17% glass reinforced, flame retardant grade UL-94 rated V-0/5VA.
Linear Mold Shrinkage, Flow	0.0040 - 0.0060 cm/cm @Thickness 1.50 - 3.20 mm	0.0040 - 0.0060 in/in @Thickness 0.0591 - 0.126 in	SABIC Method
SABIC Innovative Plastics ValoxÂ® DR51 PBT (Asia Pacific) 15% GR polyester, excellent mechanical, thermal and electrical performance. Non-flame retardant. Spotlights, appliance housings, handles, connectors
Linear Mold Shrinkage, Flow	0.0040 - 0.0060 cm/cm @Thickness 1.50 - 3.20 mm	0.0040 - 0.0060 in/in @Thickness 0.0591 - 0.126 in	SABIC Method
SABIC Innovative Plastics ValoxÂ® DR51M PBT (Asia Pacific) 15% GR; exc. mechanical/thermal/electrical performance; nonflame retardant. For spotlights, appliance housings, handles. Easy flow/int. mold release.This data was supplied by SABIC-IP for the Asia ..
Linear Mold Shrinkage, Flow	0.0040 - 0.0060 cm/cm @Time 86400 sec	0.0040 - 0.0060 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP STAT-KON KEP33 Acetal (Asia Pacific) LNP STAT-KON* KEP33 is a compound based on Acetal resin containing Silicone, Carbon Fiber, PTFE. Added features of this material include: Electrically Conductive.
Linear Mold Shrinkage, Flow	0.0040 - 0.0060 cm/cm @Thickness 6.40 mm	0.0040 - 0.0060 in/in @Thickness 0.252 in	SABIC Method
SABIC Innovative Plastics ValoxÂ® VAC7041 ABS+PBT+PET (Asia Pacific)
Linear Mold Shrinkage, Flow	0.0040 - 0.0050 cm/cm @Thickness 2.30 - 4.60 mm	0.0040 - 0.0050 in/in @Thickness 0.0906 - 0.181 in	SABIC Method
SABIC Innovative Plastics XenoyÂ® 6370 PBT+PC 30% glass-reinforced, impact modified thermoplastic alloy. Improved toughness and ductility.
Linear Mold Shrinkage, Flow	0.0040 - 0.0060 cm/cm @Time 86400 sec	0.0040 - 0.0060 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP STAT-KON WE002 PBT (Asia Pacific) LNP STAT-KON* WE002 is a compound based on Polybutylene Terephalate resin containing Carbon Fiber. Added features of this material include: Electrically Conductive.
Linear Mold Shrinkage, Flow	0.0040 cm/cm @Time 86400 sec	0.0040 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP STAT-LOY A3000 ABS LNP STAT-LOY* A3000 is a compound based on ABS resin. Added feature of this material is: Antistatic.
Linear Mold Shrinkage, Flow	0.0040 cm/cm @Time 86400 sec	0.0040 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP THERMOCOMP AF002 ABS LNP THERMOCOMP* AF002 is a compound based on ABS resin containing 10% Glass Fiber.
Linear Mold Shrinkage, Flow	0.0040 cm/cm @Time 86400 sec	0.0040 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP THERMOCOMP DX06408 PC LNP THERMOCOMP* DX06408 is a compound based on Polycarbonate resin containing 20% Glass Fiber. Added features of this material include: Easy Molding, Mold Release.
Linear Mold Shrinkage, Flow	0.0040 - 0.0060 cm/cm @Time 86400 sec	0.0040 - 0.0060 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP THERMOCOMP JF003XXZ PES (Asia Pacific) LNP* Thermocomp* JF003XXZ is a compound based on Polyethersulfone resin containing Glass Fiber.
Linear Mold Shrinkage, Flow	0.0040 - 0.0070 cm/cm @Time 86400 sec	0.0040 - 0.0070 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP THERMOCOMP WF006L PBT LNP* THERMOCOMP* WF006L is a compound based on PBT resin containing 30% Glass Fiber. Added feature of this material is: Low Extractible.
Linear Mold Shrinkage, Flow	0.0040 cm/cm @Time 86400 sec	0.0040 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP QCP36 PA6.10 LNP* LUBRICOMP* QCP36 is a compound based on Nylon 6/10 resin containing 15% PTFE/Silicone, 30% Carbon Fiber. Added features of this material include: Wear Resistant. Electrically Conductive
Linear Mold Shrinkage, Flow	0.0040 - 0.0060 cm/cm @Thickness 3.20 - 4.60 mm	0.0040 - 0.0060 in/in @Thickness 0.126 - 0.181 in	SABIC Method
SABIC Innovative Plastics ValoxÂ® 732E PBT 30% glass/mineral reinforced, excellent thermal performance, low shrinkage and warp. Easy flow.This data was supplied by SABIC-IP for the Americas region.
Linear Mold Shrinkage, Flow	0.0040 - 0.0070 cm/cm @Time 86400 sec	0.0040 - 0.0070 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP THERMOCOMP MF004AS PP LNP THERMOCOMP* MF004AS is a compound based on Polypropylene resin containing 20% Glass Fiber. Added features of this material include: Heat Stabilized.
Linear Mold Shrinkage, Flow	0.0040 cm/cm @Time 86400 sec	0.0040 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP THERMOCOMP NF004 PC+ABS (Asia Pacific) LNP* Thermocomp* NF004 is a compound based on PC+ABS Blend resin containing Glass Fiber.
Linear Mold Shrinkage, Flow	0.0040 - 0.0060 cm/cm @Time 86400 sec	0.0040 - 0.0060 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP DBL349E PC (Asia Pacific) LNP* Lubricomp* DBL349E is a compound based on Polycarbonate resin containing Glass Bead, PTFE, Flame Retardant. Added features of this material include:LNP* Lubricomp* DBL349E is a compound based ..
Linear Mold Shrinkage, Flow	0.0040 cm/cm @Time 86400 sec	0.0040 in/in @Time 24.0 hour	ASTM D 955
SABIC Innovative Plastics LNP Verton RX93407D PA 66 LNP* Verton* RX93407D is a compound based on Nylon 66 resin.This data was supplied by SABIC-IP for the Americas region.
Linear Mold Shrinkage, Flow	0.0040 - 0.0060 cm/cm @Time 86400 sec	0.0040 - 0.0060 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP DBL349E PC LNP* Lubricomp* DBL349E is a compound based on Polycarbonate resin containing 20% Glass Bead, 15% PTFE, Flame Retardant. Added features of this material include: Internally Lubricated, Flame Retard..
Linear Mold Shrinkage, Flow	0.0040 cm/cm @Time 86400 sec	0.0040 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP QCP36 PA 6/10 (Asia Pacific) LNP* Lubricomp* QCP36 is a compound based on Nylon 6/10 resin containing PTFE, Flame Retardant, Carbon Fiber. Added features of this material include: Internally Lubricated, , Electrically Conducti..