Physical Properties | Metric | English | Comments |
---|---|---|---|
Volatile Organic Compounds (VOC) Content | <= 0.30 g/l | <= 0.30 g/l | ISO 1269 |
SolVin 173GB Polyvinyl Chloride Emulsion Polymer Made by emulsion polymerization.
APPLICATIONS
Calendering : plasticized films and sheets
Extrusion : rigid or plasticized pipes and profiles
In most cases, SolVin 173GB resin is used in blends with .. |
|||
Volatile Organic Compounds (VOC) Content | <= 0.30 g/l | <= 0.30 g/l | ISO 1269 |
SolVin 257RF Polyvinyl Chloride General Purpose - Rigid Made by suspension polymerization.
APPLICATIONS
Extrusion : unplasticized PVC
- profile
- foam
- sheet, film
- blow moldings
Calendering : unplasticized PVC
- film : high temperature process
Injecti.. |
|||
Volatile Organic Compounds (VOC) Content | <= 0.30 g/l | <= 0.30 g/l | ISO 1269 |
SolVin 258RD Polyvinyl Chloride General Purpose - Rigid Made by suspension polymerization.
APPLICATIONS
Blow extrusion : opaque or crystal-clear bottles
Injection molding : rigid articles
Calendering : opaque or crystal-clear rigid sheets
Extrusion : rig.. |
|||
Volatile Organic Compounds (VOC) Content | <= 0.30 g/l | <= 0.30 g/l | ISO 1269 |
SolVin 260RF Polyvinyl Chloride General Purpose - Rigid Made by suspension polymerization.
APPLICATIONS
Extrusion : unplasticized PVC
- tubes/pipes
- profile
- foam
- sheet, film
- blow moldings
Calendering : unplasticized PVC
- film : high temperature p.. |
|||
Volatile Organic Compounds (VOC) Content | <= 0.30 g/l | <= 0.30 g/l | ISO 1269 |
SolVin 263RB Polyvinyl Chloride General Purpose - Rigid Made by suspension polymerization.
APPLICATIONS
Blow extrusion : opaque or crystal-clear bottles
Calendering : opaque or crystal-clear rigid sheets
Extrusion : rigid profiles and filmsInformation pr.. |
|||
Volatile Organic Compounds (VOC) Content | <= 0.30 g/l | <= 0.30 g/l | ISO 1269 |
SolVin 264PC Polyvinyl Chloride General Purpose - Plasticized Made by suspension polymerization.
APPLICATIONS
Extrusion :
- plasticized, semi-rigid, and rigid profiles
- plasticized and rigid pipes
- blowing of plasticized and rigid films
- rigid "pressure" p.. |
|||
Volatile Organic Compounds (VOC) Content | <= 0.30 g/l | <= 0.30 g/l | ISO 1269 |
SolVin 266SF Polyvinyl Chloride Pastes - filler Polymers Made by suspension polymerisation.
APPLICATIONS
Filler polymer for plastisols
- Floor covering : hard-wearing top coats, chemically blown and mechanical foams, impregnation layers
- Wall coverings
-.. |
|||
Volatile Organic Compounds (VOC) Content | <= 0.30 g/l | <= 0.30 g/l | ISO 1269 |
SolVin 267RC Polyvinyl Chloride Homopolymer Extrusion Grade Polyvinyl chloride made by suspension polymerization. Uses: Sewage pipes, pressure pipes, rigid profiles, window frames, electrical ductsInformation provided by SolVin. |
|||
Volatile Organic Compounds (VOC) Content | <= 0.30 g/l | <= 0.30 g/l | ISO 1269 |
SolVin 271DF Polyvinyl Chloride General Purpose - Plasticized Made by suspension polymerization.
APPLICATIONS
Extrusion :
- plasticized and semi-rigid profiles and pipes
- blowing of plasticized films
Calendering : opaque or transparent, plasticized and semi-r.. |
|||
Volatile Organic Compounds (VOC) Content | <= 0.30 g/l | <= 0.30 g/l | ISO 1269 |
SolVin 271GA Polyvinyl Chloride General Purpose - Plasticized Made by suspension polymerization.
APPLICATIONS
Extrusion :
- plasticized and semi-rigid pipes for medical applications
- plasticized film for blood bags
Injection molding : plasticized and semi-rig.. |
|||
Volatile Organic Compounds (VOC) Content | <= 0.30 g/l | <= 0.30 g/l | ISO 1269 |
SolVin 360NA Polyvinyl Chloride Low Viscosity Paste Made by microsuspension polymerization for plastisol preparation.
MAIN APPLICATIONS
Spread coating :
- artificial leather compact layer
- artificial leather foam layer
- flooring backing foam .
Mold.. |
|||
Volatile Organic Compounds (VOC) Content | <= 0.30 g/l | <= 0.30 g/l | ISO 1269 |
SolVin 367NC Polyvinyl Chloride Low Viscosity Paste Made by emulsion polymerization for plastisol preparation.
MAIN APPLICATIONS
Spread coating :
- artificial leather compact layer
- artificial leather foam layer
- artificial leather automotive.
ADVA.. |
|||
Volatile Organic Compounds (VOC) Content | <= 0.30 g/l | <= 0.30 g/l | ISO 1269 |
SolVin 367NK Polyvinyl Chloride Medium Viscosity Paste Made by microsuspension polymerization for plastisol preparation.
MAIN APPLICATIONS
Spread coating :
- artificial leather compact layer
- artificial leather foam layer.
Molding and dipping.
Spraying.. |
|||
Volatile Organic Compounds (VOC) Content | <= 0.30 g/l | <= 0.30 g/l | ISO 1269 |
SolVin 370HD Polyvinyl Chloride High Viscosity Paste Made by emulsion polymerization for plastisol preparation.
MAIN APPLICATIONS
Spread coating :
- artificial leather compact layer
- artificial leather foam layer
- artificial leather automotive
Mold.. |
|||
Volatile Organic Compounds (VOC) Content | <= 0.30 g/l | <= 0.30 g/l | ISO 1269 |
SolVin 372HA Polyvinyl Chloride High Viscosity Paste Made by emulsion polymerization for plastisol preparation.
MAIN APPLICATIONS
Spread coating :
- artificial leather compact layer
- artificial leather foam layer
- tarpaulins
Molding and dipping.
Sp.. |
|||
Volatile Organic Compounds (VOC) Content | <= 0.30 g/l | <= 0.30 g/l | ISO 1269 |
SolVin 372NA Polyvinyl Chloride Low Viscosity Paste Made by emulsion polymerization for plastisol preparation.
MAIN APPLICATIONS
Spread coating :
- flooring foam layer
- flooring impregnation layer
- flooring backing foam
- tarpaulins
- coil coating... |
|||
Volatile Organic Compounds (VOC) Content | <= 0.30 g/l | <= 0.30 g/l | ISO 1269 |
SolVin 373MC Polyvinyl Chloride Medium Viscosity Paste Made by emulsion polymerization for plastisol preparation.
MAIN APPLICATIONS
Spread coating :
- artificial leather compact layer
- artificial leather foam layer
- artificial leather automotive.
ADVA.. |
|||
Volatile Organic Compounds (VOC) Content | <= 0.30 g/l | <= 0.30 g/l | ISO 1269 |
SolVin 373MH Polyvinyl Chloride Medium Viscosity Paste Made by emulsion polymerization for plastisol preparation.
MAIN APPLICATIONS
Spread coating :
- artificial leather compact layer
- artificial leather foam layer
- artificial leather automotive.
ADVA.. |
|||
Volatile Organic Compounds (VOC) Content | <= 0.30 g/l | <= 0.30 g/l | ISO 1269 |
SolVin 373ND Polyvinyl Chloride Low Viscosity Paste Made by emulsion polymerization for plastisol preparation.
MAIN APPLICATIONS
Spread coating :
- artificial leather compact layer
- artificial leather foam layer
- artificial leather automotive.
ADVA.. |
|||
Volatile Organic Compounds (VOC) Content | <= 0.30 g/l | <= 0.30 g/l | ISO 1269 |
SolVin 376NB Polyvinyl Chloride Low Viscosity Paste Made by emulsion polymerization for plastisol preparation.
MAIN APPLICATIONS
Spread coating :
- artificial leather compact layer
- flooring top coat
- tarpaulins .
Molding and dipping.
ADVANTAGES
- .. |
|||
Volatile Organic Compounds (VOC) Content | <= 0.30 g/l | <= 0.30 g/l | ISO 1269 |
SolVin 382NG Polyvinyl Chloride Homopolymer Polyvinyl chloride made by microsuspension polymerization. Uses: Spread coating - flooring top coat. Attributes: High filler acceptance; Matte appearance in flooring top coat; Good viscosity stabil.. |
|||
Volatile Organic Compounds (VOC) Content | <= 0.30 g/l | <= 0.30 g/l | ISO 1269 |
SolVin 386NB Polyvinyl Chloride Low Viscosity Paste Made by emulsion polymerization for plastisol preparation.
MAIN APPLICATION
Spread coating :
- flooring top coat.
ADVANTAGES
- Matt appearance in flooring to coat.
- Good viscosity stability on stor.. |
|||
Volatile Organic Compounds (VOC) Content | <= 0.30 g/l | <= 0.30 g/l | ISO 1269 |
SolVin 557RA Copolymer of Vinyl Chloride and Vinyl Acetate Made by suspension polymerization.
APPLICATIONS
Extrusion : sheets for vacuum-forming, for deformations of over 500 %
Calendering : rigid sheets for deep thermoformingInformation provided by SolVin... |
|||
Volatile Organic Compounds (VOC) Content | <= 0.30 g/l | <= 0.30 g/l | ISO 1269 |
SolVin 557RB Copolymer of Vinyl Chloride and Vinyl Acetate Made by suspension polymerization.
APPLICATIONS
Extrusion : sheets for vacuum-forming, for deformations of over 500 %
Calendering : rigid sheets for deep thermoformingInformation provided by SolVin... |
|||
Volatile Organic Compounds (VOC) Content | <= 0.30 g/l | <= 0.30 g/l | ISO 1269 |
SolVin 560RA Copolymer of Vinyl Chloride and Vinyl Acetate Made by suspension polymerization.
APPLICATIONS
Extrusion : sheets for vacuum-forming, for deformations of over 500 %
Calendering : rigid sheets for deep thermoformingInformation provided by SolVin... |
|||
Volatile Organic Compounds (VOC) Content | <= 0.30 g/l | <= 0.30 g/l | ISO 1269 |
SolVin 561SF Vinyl Chloride - Vinyl Acetate copolymer Paste - filler Made by suspension polymerization.
APPLICATIONS
This resin has been especially developed for automotive mastics.Information provided by SolVin. |
|||
Volatile Organic Compounds (VOC) Content | <= 0.30 g/l | <= 0.30 g/l | ISO 1269 |
SolVin Vinidur® 464SZ Polyvinyl Chloride grafted copolymer TYPE
Suspension graft copolymer of vinylchloride and an acrylate elastomer. Vinidur 464SZ has been developed for the extrusion of window profiles with high impact strength and good weathering proper.. |
|||
Volatile Organic Compounds (VOC) Content | <= 0.30 g/l | <= 0.30 g/l | ISO 1269 |
SolVin 275SC Polyvinyl Chloride General Purpose - Plasticized Made by suspension polymerization.
APPLICATIONS
Extrusion :
- plasticized and semi-rigid profiles and pipes
Calendering : opaque or transparent, plasticized and semi-rigid films and sheets.Informati.. |
|||
Volatile Organic Compounds (VOC) Content | <= 0.30 g/l | <= 0.30 g/l | ISO 1269 |
SolVin 374MB Polyvinyl Chloride Medium Viscosity Paste Made by emulsion polymerization for plastisol preparation.
MAIN APPLICATIONS
Spread coating :
- artificial leather compact layer
- artificial leather foam layer
- tarpaulins.
Molding and dipping.
Sp.. |
|||
Volatile Organic Compounds (VOC) Content | <= 0.30 g/l | <= 0.30 g/l | ISO 1269 |
SolVin 460SL Polyvinyl Chloride grafted copolymer Made by suspension polymerization. Special product for calendered film from the high temperature process.
APPLICATIONS
Calendering : unplasticized PVC
- film : high temperature process
Extrusion : u.. |