Physical Properties | Metric | English | Comments |
---|---|---|---|
High Load Melt Index | 12 g/10 min @Load 21.6 kg |
12 g/10 min @Load 47.6 lb |
ISO 1133 |
Total Lacqtene® 2001 PBK 44 HDPE pipe
(discontinued **) LACQTENE® 2001 PBK 44 is a high density polyethylene produced by the gas phase polymerization process with hexene as comonomer. LACQTENE® 2001 PBK 44 is a black compound especially developed for s.. |
|||
High Load Melt Index | 12 g/10 min @Load 21.6 kg, Temperature 190 °C |
12 g/10 min @Load 47.6 lb, Temperature 374 °F |
ASTM D1238 |
Formosa Plastics Formolene® HL3712 Sheet and Thermoforming HDPE
(discontinued **) Medium Density Hexene CopolymerApplications: Gas and chemical tank containment liners, pond liners, landfill liners, tunnel liners.Formolene HL3712 has good processability, excellent melt strength, .. |
|||
High Load Melt Index | 12 g/10 min @Load 21.6 kg, Temperature 190 °C |
12 g/10 min @Load 47.6 lb, Temperature 374 °F |
ASTM D1238 |
Chevron Phillips Marlex® HHM TR-400G Medium density hexene copolymer
(discontinued **) Benefits: good processability, excellent melt strength, broad fusion range, outstanding stress cracking resistanceApplications: pond liners, gas and chemical tank containment liners, landfill liner.. |
|||
High Load Melt Index | 12 g/10 min | 12 g/10 min | ASTM D1238 |
Ineos K44-11-128 HDPE Ineos K44-11-128 is a high molecular weight, high density polyethylene copolymer intended for large part blow molding where the finished product demands good physical performance and low color. Thi.. |
|||
High Load Melt Index | 12 g/10 min @Load 21.6 kg, Temperature 190 °C |
12 g/10 min @Load 47.6 lb, Temperature 374 °F |
ASTM D 1238 |
Total 50100.1 HDPE blow molding Applications: Agricultural chemical tanks, portable fuel containers, industrial parts, pallets, large foam parts, food packaging. Blow Molding Stock Temperature 370 – 450 ºF Extrusion melt tempera.. |
|||
High Load Melt Index | 12 g/10 min @Load 21.6 kg, Temperature 190 °C |
12 g/10 min @Load 47.6 lb, Temperature 374 °F |
ASTM D1238 |
Total L425 HDPE Film Blown film polyethylene grade. Provides excellent bubble stability, exceptional tear strength, high impact and puncture resistance, outstanding clarity and gloss, good stiffness, excellent compatibi.. |
|||
High Load Melt Index | 12 g/10 min @Load 21.6 kg, Temperature 190 °C |
12 g/10 min @Load 47.6 lb, Temperature 374 °F |
ASTM D1238 |
Formosa Plastics Formolene® HL3812 Film (Hexene) HDPE Medium Density Polyethylene Formolene® HL3812 is a high molecular weight hexene copolymer resin that is tailored specifically for geomembrane applications. The resin provides an excellent balance o.. |
|||
High Load Melt Index | 12 g/10 min @Load 21.6 kg, Temperature 190 °C |
12 g/10 min @Load 47.6 lb, Temperature 374 °F |
Condition F; ASTM D1238 |
Formosa Plastics Formolene® HP4401 Pipe HDPE High Density Hexene CopolymerApplications: Potable water, industrial mining, oil and gas gatheringsFormolene HP4401 is a high performance copolymer that is designed for the most demanding requiremen.. |
|||
High Load Melt Index | 12 g/10 min @Load 21.6 kg, Temperature 190 °C |
12 g/10 min @Load 47.6 lb, Temperature 374 °F |
ASTM D1238 |
Chevron Phillips Marlex® HXM 50100-01 Extra high molecular weight hexene copolymer Benefits: excellent balance of stress cracking resistance, good melt strength, excellent stress cracking resistance, good rigidity, excellent impact strength even at low temperaturesApplications: 55.. |
|||
High Load Melt Index | 12 g/10 min @Load 21.6 kg |
12 g/10 min @Load 47.6 lb |
ISO 1133 |
Total Lacqtene® 2001 TBK 46 HDPE pipe
(discontinued **) LACQTENE® 2001 TBK 46 is a high density polyethylene produced by the gas phase polymerization process. LACQTENE® 2001 TBK 46 is a black compound especially developed for pressure pipe for gas and .. |
|||
High Load Melt Index | 12 g/10 min @Load 21.6 kg, Temperature 190 °C |
12 g/10 min @Load 47.6 lb, Temperature 374 °F |
ASTM D1238 |
Braskem HF 0144 HDPE Blown Film Extrusion Polyethylene 38µm film gauge, obtained in 75mm extruder, die gap 1.0mm, output 1.75 kg/h-cm with 2:1 BUR. Applications: Grocery and T-shirt bags; merchandise bags; frozen-food bags. Information provided by Bras.. |
|||
High Load Melt Index | 12 g/10 min @Load 21.6 kg, Temperature 190 °C |
12 g/10 min @Load 47.6 lb, Temperature 374 °F |
Condition F; ASTM D1238 |
Formosa Plastics Formolene® E927 Film HDPE High Density Polyethylene High Molecular Weight Bi-Modal Resin For Thin Film Applications Formolene® E927 is a high molecular weight grade of HDPE designed for high drawdown to produce thin films w.. |
|||
High Load Melt Index | 12 g/10 min @Load 21.6 kg, Temperature 190 °C |
12 g/10 min @Load 47.6 lb, Temperature 374 °F |
Condition F; ASTM D1238 |
Formosa Plastics Formolene® E927ND Film HDPE High Molecular Weight High Density Polyethylene (HMW-HDPE) for Film Extrusion Formolene® E927ND is a bi-modal HMW-HDPE resin designed for high dart impact strength and good processing characteristi.. |