Physical Properties | Metric | English | Comments |
---|---|---|---|
Brookfield Viscosity | 75 - 600 cP | 75 - 600 cP | #2/20 rpm |
Mallard Creek Polymers ROVENE® 4106 SBR Latex ROVENE® 4106 is a carboxylated styrene-butadiene emulsion that has a very stiff or "boardy" hand. This binder is recommended as a modifier for other SBR non-woven binders to increase strength and.. |
|||
Brookfield Viscosity | 75 - 500 cP | 75 - 500 cP | #20/200 |
Mallard Creek Polymers Rovene® 4125 Styrene-Butadiene Emulsion Applications: Rovene® 4125 is recommended for applications where a primer-sealer that provides adhesion between asphalt and other various surface treatments is needed. Rovene® 4125 has been us.. |
|||
Brookfield Viscosity | 75 - 500 cP | 75 - 500 cP | #2/20 rpm |
Mallard Creek Polymers ROVENE® 6140 SBR Latex ROVENE® 6140 is a carboxylated styrene-butadiene emulsion that has a very soft and resilient hand that can be used for upholstery backcoating to produce fabrics showing high seam strengths. Due t.. |
|||
Brookfield Viscosity | 75 cP @Temperature 25.0 °C |
75 cP @Temperature 77.0 °F |
ASTM D2196-86; LVT |
Lord Adhesives Aeroglaze® Z302 Absorptive Polyurethane Aeroglaze® Z302 absorptive polyurethane is primarily for application to substrates used in space operations. These operations include those where coatings must exhibit low outgassing characterist.. |
|||
Brookfield Viscosity | 75 - 300 cP @Temperature 25.0 °C |
75 - 300 cP @Temperature 77.0 °F |
LVT, Spindle #1 @ 60rpm |
Lord Adhesives HPC-3C Fluoroelastomer Coating LORD HPC-3B and HPC-3C are two-part, room temperature curing fluoroelastomer coatings which feature robust adhesion and exceptional mechanical properties. These coatings greatly enhance fuel and flu.. |
|||
Brookfield Viscosity | 75 - 300 cP @Temperature 25.0 °C |
75 - 300 cP @Temperature 77.0 °F |
LVT, Spindle #1 @ 60rpm |
Lord Adhesives HPC-3B Fluoroelastomer Coating LORD HPC-3B and HPC-3C are two-part, room temperature curing fluoroelastomer coatings which feature robust adhesion and exceptional mechanical properties. These coatings greatly enhance fuel and flu.. |
|||
Brookfield Viscosity | 75 cP | 75 cP | #1 spindle; 6 rpm. |
DuPont Performance Polymers Neoprene 654 Polychloroprene
(discontinued **) Main feature: DPHS. Principal uses include: Dipped goods, Coatings, Adhesives (Lamination, Heat reactivated).Solids content: 59%. Initial pH: 12. Surface tension: 40 dyne/cm. Polymer type: Low g.. |
|||
Brookfield Viscosity | 75 cP | 75 cP | #1 spindle; 30 rpm. |
DuPont Performance Polymers Neoprene 654 Polychloroprene
(discontinued **) Main feature: DPHS. Principal uses include: Dipped goods, Coatings, Adhesives (Lamination, Heat reactivated).Solids content: 59%. Initial pH: 12. Surface tension: 40 dyne/cm. Polymer type: Low g.. |