Physical Properties | Metric | English | Comments |
---|---|---|---|
Melt Flow | 0.30 - 0.60 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.30 - 0.60 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
Polyplastic Torlen® PE 2K 901 High Density Polyethylene, Carbon Filled Information provided by PolyPlastic Group. |
|||
Melt Flow | 0.30 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.30 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
Polimeri Europa Eraclene® FC 82 High Density Polyethylene - Blown Film Extrusion Eraclene FC 82 is a high density polyethylene resin (HDPE), hexene copolymer, with antioxidants, suitable for blown film extrusion.Its broad molecular weight distribution and density successfully co.. |
|||
Melt Flow | 0.30 g/10 min @Load 2.16 kg, Temperature 230 °C |
0.30 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
Premix Thermoplastics PRE-ELEC® PP 1373 PRE-ELEC PP 1373 is a conductive thermoplastic compound based on polypropylene. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PRE-ELE.. |
|||
Melt Flow | 0.30 g/10 min @Load 2.16 kg, Temperature 230 °C |
0.30 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
Premix Thermoplastics PRE-ELEC® PP 1385 PRE-ELEC PP 1385 is a conductive thermoplastic compound based on polypropylene. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PRE-ELE.. |
|||
Melt Flow | 0.30 - 0.50 g/10 min @Load 5.00 kg, Temperature 190 °C |
0.30 - 0.50 g/10 min @Load 11.0 lb, Temperature 374 °F |
ASTM D1283/L |
NIZHNEKAMSKNEFTEKHIM PE 6250D (506H4) High Density Polyethylene Product obtained by gas phase polymerization of ethylene in presence of complex metalorganic catalysts.Information provided by manufacturer |
|||
Melt Flow | 0.30 - 0.50 g/10 min @Load 2.16 kg, Temperature 230 °C |
0.30 - 0.50 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1283/L |
NIZHNEKAMSKNEFTEKHIM PP 8332C (EPD60R) Propylene and Ethylene Block Polymer Product obtained by copolymerization of propylene with ethylene in presence of complex metalorganic catalysts. It incorporates increased long-term thermal stability, thermal-oxidative degradation r.. |
|||
Melt Flow | 0.30 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.30 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
DSM Arnitel® EB500 Polyether Ester Elastomer (European and Asian Grade)
(discontinued **) Product description: Arnitel® combines the advantages of engineering thermoplastics, being easy to process with excellent mechanical properties, at the same time with the flexibility of rubbers.Arn.. |
|||
Melt Flow | 0.30 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.30 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
SABIC B5429/B5429A High Density Polyethylene for Blow Molding Product Description: B5429 Series grades are medium molecular weight High Density Polyethylene copolymer. They are primarily intended for blow molding articles of small sizes. B5429 series grades.. |
|||
Melt Flow | 0.30 g/10 min @Load 2.16 kg, Temperature 230 °C |
0.30 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
SABIC PP 651H Polypropylene Random Copolymer for PIPE Product Description: PP 651H is specially designed for transport of hot and cold drinking water. This grade is highly heat stabilized and specially formulated for extraction resistance.Typical App.. |
|||
Melt Flow | 0.30 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.30 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
Premix Thermoplastics PRE-ELEC® PE 1304
(discontinued **) PRE-ELEC PE 1304 is a conductive thermoplastic compound based on a blend of PE-LD/PE-LLD. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivi.. |
|||
Melt Flow | 0.30 g/10 min @Load 2.16 kg |
0.30 g/10 min @Load 4.76 lb |
ISO 1133 |
Total Finathene® 6002 HDPE, blow molding, pipe
(discontinued **) FINATHENE® 6002 is a high density polyethylene produced by the slurry loop low pressure polymerization process. FINATHENE® 6002 has been especially developed for the manufacturing of toys and of b.. |
|||
Melt Flow | 0.30 g/10 min @Load 2.16 kg |
0.30 g/10 min @Load 4.76 lb |
ISO 1133 |
Total Lacqtene® 2005 TN 59 HDPE pipe
(discontinued **) LACQTENE® 2005 TN 59 is a high density polyethylene produced by the gas phase polymerization process with hexene as comonomer. LACQTENE® 2005 TN 59 is best processed between 190 and 230°C.Informa.. |
|||
Melt Flow | 0.30 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.30 g/10 min @Load 4.76 lb, Temperature 374 °F |
|
Imerys ImerPlast™ 10WPC Recycled Polyolefin Resin ImerPlast 10WPC is a black, UV stabilized, recycled resin with no significant odor, for compounding with wood flour for extruded decking applications. Melt filtered to 250 µm to ensure no particu.. |
|||
Melt Flow | 0.30 g/10 min @Load 2.16 kg, Temperature 230 °C |
0.30 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
Borealis BE50-7032 Polypropylene Homopolymer for Non-Pressure pipes and extruded sheets BE50-7032 is a high molecular weight, low melt flow rate polypropylene homopolymer characterized by high stiffness, high heat distortion temperature and high resistance to thermal aging.
The materia.. |
|||
Melt Flow | 0.30 g/10 min @Load 2.16 kg, Temperature 230 °C |
0.30 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
Borealis BEC5012 Polypropylene Block Copolymer for Non-Pressure Pipes BEC5012 is a high molecular weight, low flow rate polypropylene block copolymer with very high impact strength. Applications: BEC5012 is recommended for non-pressure pipes and fittings, structured.. |
|||
Melt Flow | 0.30 g/10 min @Load 2.16 kg, Temperature 230 °C |
0.30 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
Borealis Beta (ß)-PP™ BE60-7032 Grey Polypropylene Homopolymer for Pressure Pipes, Fittings and Sheets Beta(ß)-PP BE60-7032 is a high molecular weight, low melt flow rate polypropylene homopolymer with fine grained ß-modification crystalline structure leading to excellent impact strength even at lo.. |
|||
Melt Flow | 0.30 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.30 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
Borealis Borstar® FB3450 HDPE for Film Extrusion Borstar® FB3450 is a high density polyethylene. Borstar® FB3450 is well suited for multilayer coextruded films where higher stiffness and toughness than in standard LDPE and LLDPE is required. Ap.. |
|||
Melt Flow | 0.30 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.30 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
Borealis BS2581 High Density Polyethylene for Blow Molding BS2581 is a high density polyethylene intended for blow molding products with high stiffness and very good environmental stress crack resistance (ESCR). Applications: industrial chemicals, househol.. |
|||
Melt Flow | 0.30 g/10 min @Load 5.00 kg, Temperature 190 °C |
0.30 g/10 min @Load 11.0 lb, Temperature 374 °F |
ISO 1133 |
Borealis FS1560 High Density Polyethylene FS1560 is a high density polyethylene film grade which combine excellent extrusion behavior with superior mechanical properties. Films made of FS1560 have high impact and tensile strength, and bala.. |
|||
Melt Flow | 0.30 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.30 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
Borealis BS2541 High Density Polyethylene BS2541 is a high density polyethylene with very high ESCR This product is intended for blow molding. Applications: household and chemical containers such as detergents, cleaners, and motor oils, an.. |
|||
Melt Flow | 0.30 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.30 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
Total HDPE 5802 High Density Polyethylene - Blow Molding HDPE 5802 is a high density polyethylene with excellent compromise between stiffness and Environmental Stress Crack Resistance. It has been specifically designed for the manufacture of blow molded .. |
|||
Melt Flow | 0.30 g/10 min @Load 5.00 kg, Temperature 200 °C |
0.30 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
Chi Mei Polylac® PA-747R ABS - Extrusion Attach case and refrigerator |
|||
Melt Flow | 0.30 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.30 g/10 min @Load 4.76 lb, Temperature 374 °F |
ExxonMobil Method |
ExxonMobil Pax-Plus™ 3204 Blown Film Resin Pax-Plus 3204 is a rubber modified high density polyethylene film resin which is used primarily in film requiring good impact strength. It is specially formulated to provide easy tear in the machin.. |
|||
Melt Flow | 0.30 g/10 min @Load 5.00 kg, Temperature 200 °C |
0.30 g/10 min @Load 11.0 lb, Temperature 392 °F |
Procedure A Condition G; ASTM D1238 |
Diamond Polymers ASA T-115 Description: ASA Weatherable Polymer, Injection Molding Grade, High Heat ResistanceInformation provided by Diamond Polymers, Inc. |
|||
Melt Flow | 0.30 g/10 min @Load 5.00 kg, Temperature 200 °C |
0.30 g/10 min @Load 11.0 lb, Temperature 392 °F |
Procedure A; ASTM D1238 |
Diamond Polymers ASA TW-18B1 Description: ASA Weatherable Polymer, Injection Molding Grade, Very High HeatInformation provided by Diamond Polymers, Inc. |
|||
Melt Flow | 0.30 g/10 min @Load 5.00 kg, Temperature 200 °C |
0.30 g/10 min @Load 11.0 lb, Temperature 392 °F |
Procedure A; ASTM D1238 |
Diamond Polymers ASA TW-18B2 Description: ASA Weatherable Polymer, Injection Molding Grade, Very High HeatInformation provided by Diamond Polymers, Inc. |
|||
Melt Flow | 0.30 g/10 min @Load 5.00 kg, Temperature 200 °C |
0.30 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
Chi Mei Polylac® PA-747F ABS - Extrusion Refrigerator |
|||
Melt Flow | 0.30 g/10 min @Load 5.00 kg, Temperature 200 °C |
0.30 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
Diamond Polymers DIAMALOY VP22 NATURAL 1001B Blow Molding Grade, Flame Retardant ABS Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc. |
|||
Melt Flow | 0.30 g/10 min @Load 5.00 kg, Temperature 190 °C |
0.30 g/10 min @Load 11.0 lb, Temperature 374 °F |
ISO 1133 |
Total XSene® HD55110 High Density Polyethylene - Blown Film HDPE HD55110 is a bimodal high density polyethylene with a particular molecular design developed with Total Petrochemicals Double Loop Technology™.HDPE HD55110 has been especially designed for appl.. |
|||
Melt Flow | 0.30 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.30 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
Borealis Bormed™ HE2581-PH HDPE for Healthcare Applications Bormed HE2581-PH is a high-density polyethylene intended for blow molding of products with high stiffness and very good environmental stress crack resistance (ESCR). Bormed HE2581-PH can as well be .. |