Physical Properties | Metric | English | Comments |
---|---|---|---|
Melt Flow | 9.5 g/10 min @Load 21.6 kg, Temperature 190 °C |
9.5 g/10 min @Load 47.6 lb, Temperature 374 °F |
ISO 1133 |
Iran Petrochemical (PCC) BL 4M HM 8355 High Density Polyethylene BL4M is a high density polyethylene with 1-Butene as co monomer. It is high molar mass, easily processable, high stiffness and strength, good SCR, very good molding surface finish.Applications: jer.. |
|||
Melt Flow | 9.5 g/10 min @Load 1.20 kg, Temperature 250 °C |
9.5 g/10 min @Load 2.65 lb, Temperature 482 °F |
ASTM D 1238 |
SABIC Innovative Plastics PC6300 PC PC6300 resin is a very high flow (MFR = 9.5 at 250ºC/1.2kg) polycarbonate product designed for use in the optical media market.This data was supplied by SABIC-IP for the Americas region. |
|||
Melt Flow | 9.5 g/10 min @Load 1.20 kg, Temperature 250 °C |
9.5 g/10 min @Load 2.65 lb, Temperature 482 °F |
ASTM D 1238 |
SABIC Innovative Plastics PC6300 PC (Asia Pacific) PC6300 resin is a very high flow (MFR = 9.5 at 250ºC/1.2kg) polycarbonate product designed for use in the optical media market.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
Melt Flow | 9.5 g/10 min @Load 1.20 kg, Temperature 250 °C |
9.5 g/10 min @Load 2.65 lb, Temperature 482 °F |
ASTM D 1238 |
SABIC Innovative Plastics PC6300 PC (Europe-Africa-Middle East) PC6300 resin is a very high flow (MFR = 9.5 at 250ºC/1.2kg) polycarbonate product designed for use in the optical media market.This data was supplied by SABIC-IP for the Europe-Africa-Middle East.. |
|||
Melt Flow | 9.5 g/10 min @Load 6.60 kg, Temperature 337 °C |
9.5 g/10 min @Load 14.6 lb, Temperature 639 °F |
ASTM D 1238 |
SABIC Innovative Plastics Ultem 2412EPR PEI 40% Milled glass filled, high flow Polyetherimide (Tg 217C) with internal mold release and enhanced electroplatability. ECO Conforming, UL94 V0 listing.This data was supplied by SABIC-IP for the Am.. |
|||
Melt Flow | 9.5 g/10 min @Load 6.60 kg, Temperature 337 °C |
9.5 g/10 min @Load 14.6 lb, Temperature 639 °F |
ASTM D 1238 |
SABIC Innovative Plastics Ultem 2412EPR PEI (Asia Pacific) 40% Milled glass filled, high flow Polyetherimide (Tg 217C) with internal mold release and enhanced electroplatability. ECO Conforming, UL94 V0 listing.This data was supplied by SABIC-IP for the As.. |
|||
Melt Flow | 9.5 g/10 min @Load 6.60 kg, Temperature 337 °C |
9.5 g/10 min @Load 14.6 lb, Temperature 639 °F |
ASTM D 1238 |
SABIC Innovative Plastics Ultem 2412EPR PEI (Europe-Africa-Middle East) 40% Milled glass filled, high flow Polyetherimide (Tg 217C) with internal mold release and enhanced electroplatability. ECO Conforming, UL94 V0 listing.This data was supplied by SABIC-IP for the Eu.. |
|||
Melt Flow | 9.5 g/10 min @Load 5.00 kg, Temperature 250 °C |
9.5 g/10 min @Load 11.0 lb, Temperature 482 °F |
ISO 1133 |
Styron Pulse® A20-95 PC/ABS A medium impact strength PC/ABS blend with high heat distortion and excellent processability.Information provided by DowThis product line was spun off from Dow Chemical to Styron in 2010. |
|||
Melt Flow | 9.5 g/10 min @Load 5.00 kg, Temperature 230 °C |
9.5 g/10 min @Load 11.0 lb, Temperature 446 °F |
ISO 1133 |
Borealis Borclean™ HB311BF Polypropylene Homopolymer for Capacitor Film Borclean HB311BF is a homopolymer film resin developed for use in the manufacture of the highest quality films for dielectric applications. Borclean HB311BF does not contain slip, antiblock, antist.. |
|||
Melt Flow | 9.5 g/10 min @Load 3.80 kg, Temperature 230 °C |
9.5 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D1238 |
Diamond Polymers SAN 263 Styrene Acrylonitrile, Transparent Engineering Thermoplastic Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc. |
|||
Melt Flow | 9.5 g/10 min @Load 10.0 kg, Temperature 230 °C |
9.5 g/10 min @Load 22.0 lb, Temperature 446 °F |
ISO 1133 |
DuPont Performance Polymers Hytrel® HTR8223 BK320 Polyester Elastomer TPC-ET
(Unverified Data**) 42 Shore D High Viscosity Polyester Elastomer Developed for Blow MoldingInformation provided by DuPont Performance Polymers |