Physical Properties | Metric | English | Comments |
---|---|---|---|
Melt Flow | 8.0 - 12 g/10 min @Load 2.16 kg, Temperature 230 °C |
8.0 - 12 g/10 min @Load 4.76 lb, Temperature 446 °F |
Procedure A Condition L; ASTM D1238 |
Network Polymers NPP 30-1200 TF33 Description: 33% Talc Filled Homopolymer PolypropyleneInformation provided by Network Polymers Inc. |
|||
Melt Flow | 8.0 - 12 g/10 min @Load 2.16 kg, Temperature 230 °C |
8.0 - 12 g/10 min @Load 4.76 lb, Temperature 446 °F |
Procedure A Condition L; ASTM D1238 |
Network Polymers NPP 30-1200 TF40 Description: 40% Talc Filled Homopolymer PolypropyleneInformation provided by Network Polymers Inc. |
|||
Melt Flow | 6.0 - 12 g/10 min @Load 2.16 kg, Temperature 190 °C |
6.0 - 12 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
Polymer Resources AC-GP2 Acetal Copolymer, Medium Flow Process: Molding or ExtrusionNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resources Corporation. |
|||
Melt Flow | 6.0 - 12 g/10 min @Load 2.16 kg, Temperature 190 °C |
6.0 - 12 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
Polymer Resources AC-GP2-UV Acetal Copolymer, Medium Flow, UV-stabilized Process: Molding or ExtrusionNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resources Corporation. |
|||
Melt Flow | 2.0 - 12 g/10 min @Load 5.00 kg, Temperature 250 °C |
2.0 - 12 g/10 min @Load 11.0 lb, Temperature 482 °F |
ASTM D1238 |
Polymer Resources PC/ABS-G20 General Purpose PC/ABS Alloy, 20% Glass Filled PC/ABS Alloy, General Purpose, 20% Glass FilledProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provi.. |
|||
Melt Flow | 5.0 - 12 g/10 min @Load 1.20 kg, Temperature 300 °C |
5.0 - 12 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
Polymer Resources PC-G10 Polycarbonate, 10% Glass Reinforced Polycarbonate, 10% Glass ReinforcedFeatures: • Flame Retardant • Self ExtinguishingProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-p.. |
|||
Melt Flow | 5.0 - 12 g/10 min @Load 1.20 kg, Temperature 300 °C |
5.0 - 12 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
Polymer Resources PC-G10-IM Polycarbonate, 10% Glass Reinforced, Impact Modified Polycarbonate, 10% Glass Reinforced, Impact ModifiedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information .. |
|||
Melt Flow | 5.0 - 12 g/10 min @Load 1.20 kg, Temperature 300 °C |
5.0 - 12 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
Polymer Resources PC-HM-FR1-[color]-3 Polycarbonate, 10% Glass Reinforced, Flame Retardant, UV-stabilized Polycarbonate, 10% Glass Reinforced, Flame Retardant, UV-stabilizedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test sampl.. |
|||
Melt Flow | 3.0 - 12 g/10 min @Load 1.20 kg, Temperature 300 °C |
3.0 - 12 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
Polymer Resources PCSF-FRG30 Polycarbonate, 30% Glass Reinforced Structural Foam Grade Polycarbonate, 30% Glass Reinforced Structural Foam GradeFeatures: • Flame Retardant • Foamable • Self ExtinguishingProcess: Foam MoldingNotes: All physical, mechanical and thermal testing con.. |
|||
Melt Flow | 9.0 - 12 g/10 min | 9.0 - 12 g/10 min | 230/2.16 (typical); ASTM D1238 |
Fiberfil® J-60/GB/20 Polypropylene Homopolymer, 20% Glass beads Information provided by FIBERFIL Engineered Plastics |
|||
Melt Flow | 8.0 - 12 g/10 min | 8.0 - 12 g/10 min | ASTM D1238 |
Kolon KOCETAL® TF302 Wear Modified Acetal Resin PTFE powder added, improved wear property. Applications: High speed, high load and wear resistant products. Information provided by API-Kolon. |
|||
Melt Flow | 8.1 - 12 g/10 min | 8.1 - 12 g/10 min | B |
Shandong Dongyue Shenzhou New Material Co DS600 Perfluorinated Ethylene-Propylene Copolymer Conformable with: Q/DYS 003-2007Fluorinated Ethylene Propylene resin is the copolymer of the TFE and HFP, with good thermal stability, outstanding chemical inertness, good electrical insulation, and.. |
|||
Melt Flow | 6.0 - 12 g/10 min @Temperature 230 °C |
6.0 - 12 g/10 min @Temperature 446 °F |
Condition L; ASTM D1238 |
A. Schulman PP 1349 Polypropylene Medium Impact Copolymer Polypropylene DescriptionPolypropylene PP 1349 is a medium impact copolymer polypropylene.Information provided by A. Schulman. |
|||
Melt Flow | 8.0 - 12 g/10 min | 8.0 - 12 g/10 min | 230/2.16; May be specified; ASTM D1238 |
Plastics Group Polifil® RMC-30 30% Calcium Carbonate-Reinforced Polypropylene, High Impact Polifil® RMC series compounds are high impact polypropylenes reinforced with fine particle size calcium carbonate. In addition to the highest impact possible, they possess good stiffness, heat agin.. |
|||
Melt Flow | 8.0 - 12 g/10 min | 8.0 - 12 g/10 min | 230/2.16; May be specified; ASTM D1238 |
Plastics Group Polifil® RMC-40 40% Calcium Carbonate-Reinforced Polypropylene, High Impact Polifil® RMC series compounds are high impact polypropylenes reinforced with fine particle size calcium carbonate. In addition to the highest impact possible, they possess good stiffness, heat agin.. |
|||
Melt Flow | 8.0 - 12 g/10 min | 8.0 - 12 g/10 min | 230/2.16; May be specified; ASTM D1238 |
Plastics Group Polifil® T-40 40% Talc-Reinforced Polypropylene Polifil® T series compounds are homopolymer polypropylene resins reinforced with asbestos-free talc. They possess high flex modulus, high deflection temperature, good chemical resistance and colora.. |
|||
Melt Flow | 8.0 - 12 g/10 min | 8.0 - 12 g/10 min | 8-12 g/10min; Cond L; ASTM D1238 |
Washington Penn PPH3TF4-BLK Polypropylene, 40% Talc Filled Homopolymer. Meets GMP.PP.030 spec.Applications: Fan shrouds, heater housings, various under hood uses.Data provided by Washington Penn Plastic Co., Inc. |
|||
Melt Flow | 6.0 - 12 g/10 min @Temperature 230 °C |
6.0 - 12 g/10 min @Temperature 446 °F |
Condition L; ASTM D1238 |
A. Schulman PP 1349 Polypropylene Medium Impact Copolymer Polypropylene DescriptionPolypropylene PP 1349 is a medium impact copolymer polypropylene.Information provided by A. Schulman. |
|||
Melt Flow | 8.0 - 12 g/10 min @Load 2.16 kg, Temperature 230 °C |
8.0 - 12 g/10 min @Load 4.76 lb, Temperature 446 °F |
Condition L; ASTM D1238 |
A. Schulman PP 984 Polypropylene Medium Impact Polypropylene DescriptionPolypropylene PP 984 is a medium impact polypropylene used primarily for automotive parts subjected to impact.Information provided by A. Schulman. |
|||
Melt Flow | 8.0 - 12 g/10 min | 8.0 - 12 g/10 min | ISO 1133 |
Chengdu Polyster H3303 Thermoplastic Polyether-ester Elastomer (TPEE) Low modulus molding and injection grade. Contains improved color- stable antioxidants. Excellent flex resistance at low temperatures. Moldable even in thin sections. Can be used in light-colored pro.. |
|||
Melt Flow | 8.0 - 12 g/10 min @Load 0.325 kg, Temperature 190 °C |
8.0 - 12 g/10 min @Load 0.716 lb, Temperature 374 °F |
die 8/2; ISO 1133 |
Addcomp PRIEX® 25093 Maleic Anhydride Grafted PP random copolymer Functionalised polypropylene to be used as compatibiliser for polymer blends or coupling agent for glass fibre, wood flour, natural fibres, multilayer films, aluminium foils, or mineral filled polyp.. |
|||
Melt Flow | 8.0 - 12 g/10 min | 8.0 - 12 g/10 min | ASTM D1238 |
Buckeye Polymers BP FLEX D4107 C BLK Thermoplastic Polyolefin Product Information: TPO's are a family of thermoplastic elastomers which exhibit rubber-like properties and are processable on conventional thermoplastic equipment.Product Features:High tear resist.. |
|||
Melt Flow | 8.0 - 12 g/10 min @Load 2.16 kg, Temperature 230 °C |
8.0 - 12 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
Aaron Industries AAROLENE® ARPP C 200-3 Polypropylene Compounded Resin AAROLENE® ARPP 200 Series Polypropylene Compounded ResinColor may be specified. Melt Flow Index may be specified. |
|||
Melt Flow | 8.0 - 12 g/10 min | 8.0 - 12 g/10 min | ASTM D1238 |
Buckeye Polymers BP RPP 1012 T BLK Polypropylene, Talc Filled Product Information: Our Talc filled product lines exhibit excellent properties such as high stiffness, surface aesthetics, low coefficient of thermal expansion, low shrinkage, improved scratch and .. |
|||
Melt Flow | 3.0 - 12 g/10 min @Load 5.00 kg, Temperature 200 °C |
3.0 - 12 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
Aaron Industries AAROLENE® ARPS HI-100-4 Polystyrene Compounded Resin AAROLENE® ARPS 100 Series Polystyrene Compounded ResinColor may be specified. Melt Flow Index may be specified. |
|||
Melt Flow | 8.0 - 12 g/10 min @Load 2.16 kg, Temperature 230 °C |
8.0 - 12 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
Aaron Industries AAROPRENE® CFIPP 2030 High Impact Calcium Carbonate Filled Polypropylene AAROPRENE® CFIPP 2000 Series Reinforced CompoundsMelt flow index may be specified. Color may be specified. |
|||
Melt Flow | 5.0 - 12 g/10 min @Load 1.20 kg, Temperature 300 °C |
5.0 - 12 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
Polymer Resources PCSF-FR1 Polycarbonate, 10% Glass Reinforced Structural Foam Grade Polycarbonate, 10% Glass Reinforced Structural Foam GradeFeatures: • Flame Retardant • Foamable • Self ExtinguishingProcess: Foam MoldingNotes: All physical, mechanical and thermal testing con.. |
|||
Melt Flow | 6.0 - 12 g/10 min | 6.0 - 12 g/10 min | ASTM D1238 |
Buckeye Polymers BP RPP 4008 TR BLK Polypropylene, Talc Filled Product Information: Our Talc filled product lines exhibit excellent properties such as high stiffness, surface aesthetics, low coefficient of thermal expansion, low shrinkage, improved scratch and .. |
|||
Melt Flow | 8.0 - 12 g/10 min | 8.0 - 12 g/10 min | ASTM D1238 |
Buckeye Polymers BP RPP 4010 TW Polypropylene, Talc Filled Product Information: Our Talc filled product lines exhibit excellent properties such as high stiffness, surface aesthetics, low coefficient of thermal expansion, low shrinkage, improved scratch and .. |