- Polymer Property : Melt Flow = 8.0 g/10 min
Polymer Property : Melt Flow = 8.0 g/10 min Product List
Physical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Flow | 8.0 g/10 min @Load 0.325 kg, Temperature 270 °C |
8.0 g/10 min @Load 0.716 lb, Temperature 518 °F |
|
| Plastcom SLOVALEN PC 63 T 15-1M PP, 15% mineral filling FeaturesModified PP copolymer for injection moulding with the content of 15 % mineral filler, uv stabilized, good scratch resistance, low odor and very good flowability with good dimensional stabili.. |
|||
| Melt Flow | 8.0 g/10 min @Load 0.325 kg, Temperature 270 °C |
8.0 g/10 min @Load 0.716 lb, Temperature 518 °F |
|
| Plastcom SLOVAMID 6 GF 7 T 13 PA6, 7% glass fibre, 13% mineral filling FeaturesGood anisotropy of the manufacturing shrinkage. The talc is added to get the material shrinkage identical in both directions. Application for flat products in disc form /no screw after cooli.. |
|||
| Melt Flow | 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
8.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| NCMT NanoPAC™ S212 High Performance Polypropylene Nanocomposite Characteristics: High stiffness Supplementary of ABS Good impact resistant Less shrinkage Good thermal conductivity Applications: Toys Industry AutomobileInformation provided by Nano Composite Mater.. |
|||
| Melt Flow | 8.0 - 16 g/10 min @Load 1.20 kg, Temperature 300 °C |
8.0 - 16 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Polymer Resources PC-HM-FR2-[color]-4 Polycarbonate, 10% Glass Reinforced, Flame Retardant, UV-stabilized with Mold Release Polycarbonate, 10% Glass Reinforced, Flame Retardant, UV-stabilized with Mold ReleaseProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pig.. |
|||
| Melt Flow | 8.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
8.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| SABIC Innovative Plastics Lexan® EXL6414 PC PC-Siloxane copolymer with excellent processability. Impact modified, medium flow, extreme low temp. ductility. |
|||
| Melt Flow | 8.0 g/10 min | 8.0 g/10 min | ASTM D1238 |
| I. Stern HIPS 8 High Impact Polystyrene Injection Grade Features:Good processing characteristicsComplies with FDA requirements as described in Title 21 CFR 177.1640ApplicationsDisplaysHouse waresStructural FoamInformation provided by I. Stern & Co. Inc. |
|||
| Melt Flow | 8.0 g/10 min | 8.0 g/10 min | |
| Global TPO-55D TPO Grade Data provided by Global Polymers Corporation. |
|||
| Melt Flow | 8.0 g/10 min @Load 5.00 kg, Temperature 260 °C |
8.0 g/10 min @Load 11.0 lb, Temperature 500 °F |
ASTM D1238 |
| Lucent Polymers PC/ABS-1208 Polycarbonate+ABS, General Purpose, Injection Grade Add "R" for Added ReleaseAdd "U" for UV StabilizerInformation provided by Lucent Polymers, Inc. |
|||
| Melt Flow | 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
8.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Lucobit Lucopren® 1500M Soft Polyolefin Granules Lucopren is a novel, super-soft and highly elastic raw material based on polyolefins. Lucopren displays excellent flexibility and elasticity. It can be converted into products with an excellent touc.. |
|||
| Melt Flow | 8.0 - 10 g/10 min @Load 5.00 kg, Temperature 200 °C |
8.0 - 10 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| Lavergne VYSTYRENE PS 3904 High Impact Polystyrene Vystyrene PS 3904 is a black impact modified polystyrene compound with balanced impact/stiffness properties designed for injection molding applicationsFeatures: -High resilience -Excellent process.. |
|||
| Melt Flow | 8.0 g/10 min @Load 5.00 kg, Temperature 266 °C |
8.0 g/10 min @Load 11.0 lb, Temperature 511 °F |
ASTM D1238 |
| SABIC Innovative Plastics Xenoy® X4870HH PC+PET (Europe-Africa-Middle East) Xenoy X4870HH is a high heat, very high modulus and ductile PC/PET blend. Furthermore this resin provides chemical resistance, very low creep, low CTE, excellent fatique and high heat dimensional st.. |
|||
| Melt Flow | 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
8.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Borealis HD621CF Polypropylene HD621CF is a polypropylene homopolymer This grade is suitable for the manufacturing of unoriented films on cast and tubular quench film lines. Applications: food packaging, lamination films, statio.. |
|||
| Melt Flow | 8.0 g/10 min | 8.0 g/10 min | ASTM D1238 |
| A. Schulman POLYFORT™ FPP 1605 Glass Reinforced Chemically Coupled Copolymer DescriptionPolyfort® FPP 1605 is a 10% glass reinforced chemically coupled copolymer. It has good impact and heat resistance. Information provided by A. Schulman. |
|||
| Melt Flow | 8.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
8.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| A. Schulman POLYBATCH™ Green 30394 Concentrate Based In LDPE DescriptionPOLYBATCH® 30394 is a green color concentrate based in LDPE. This concentrate was designed to provide color in blow molding applications. POLYBATCH® 30394 is typically recommended for.. |
|||
| Melt Flow | 8.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
8.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| A. Schulman POLYBATCH™ White P8555 T2 Concentrate Based In Homopolymer Polypropylene DescriptionPOLYBATCH® P8555 T2 is a premium white masterbatch containing 50% TiO2 based in homopolymer polypropylene. This product is processed through 300x300 mesh screens and offers premium disp.. |
|||
| Melt Flow | 8.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
8.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| A. Schulman POLYBATCH™ Silver 7002/5 Concentrate Based In LDPE DescriptionPOLYBATCH® 70022/5 is a silver color concentrate based in LLDPE. This concentrate was designed to provide opacity and color in polyolefin film and molding applications. POLYBATCH® 70.. |
|||
| Melt Flow | 8.0 - 12 g/10 min @Load 2.16 kg, Temperature 190 °C |
8.0 - 12 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D 1238 |
| Cossa Polimeri ESTALENE EN 10 EC Modified Polyolefin Blend Formulated for injection molding or extrusion of synthetic corksCertified according to FDA standardsInformation provided by Cossa Polimeri S.r.l. |
|||
| Melt Flow | 8.0 g/10 min @Load 2.16 kg, Temperature 330 °C |
8.0 g/10 min @Load 4.76 lb, Temperature 626 °F |
|
| Covestro Apec® HT KU 1-9354/1 High-Heat Polycarbonate Transparent and opaque shades possible.Applications: Lighting, electrical parts.Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and officially.. |
|||
| Melt Flow | 8.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
8.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| ELASTO UK Dryflex® 402801S SBS Based Material, 80A Hardness, Black The 400S-series is a good alternative for indoor applications and disposable articles that do not have high requirements for ageing and heat resistance. The raw materials are specially selected for.. |
|||
| Melt Flow | 8.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
8.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| ExxonMobil HDPE HMA 025 High Density Polyethylene Resin Product Description: HMA 025 is a HDPE grade, characterized by excellent dimensional stability, impact strength and very high stiffness. Availability: Africa & Middle East, Asia Pacific and Europe A.. |
|||
| Melt Flow | 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
8.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| ExxonMobil PP1063L1 Polypropylene Homopolymer Product Description: A homopolymer resin designed for general use. It is suitable for masterbatch carrier and other compounding applications and for the molding of caps, cups, containers and other .. |
|||
| Melt Flow | 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
8.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
|
| Arkema Group Orevac® 18732 RBP Maleic Anhydride modified Polypropylene PP base Structure: Repairing and joint Applications: Pipe CoatingInformation provided by Arkema Group |
|||
| Melt Flow | 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
8.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
|
| BASF Novolen® 2309 L Polypropylene Cast film and thermoformed partsData was collected by ISO methods and provided by BASF. |
|||
| Melt Flow | 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
8.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
|
| BASF Novolen® 2700 L Polypropylene UV stabilized grade for injection molded parts.Data was collected by ISO methods and provided by BASF. |
|||
| Melt Flow | 8.0 g/10 min @Load 5.00 kg, Temperature 275 °C |
8.0 g/10 min @Load 11.0 lb, Temperature 527 °F |
ISO 1133 |
| BASF Ultramid® B50L 01 PA6 (Dry) Ultramid B50L 01 is a high-viscosity, lubricated, general-purpose extrusion PA6 grade. It conforms to FDA requirements including, 21 CFR 177.1500,EU Directive 2002/72/EC, the German BfR recommendat.. |
|||
| Melt Flow | 8.0 - 12 g/10 min @Load 2.16 kg, Temperature 230 °C |
8.0 - 12 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Aaron Industries AAROPRENE® TFPP 2020 Talc Filled Polypropylene AAROPRENE® TFPP 2000 Series Talc Reinforced CompoundsMelt flow index may be specified. Color may be specified. |
|||
| Melt Flow | 8.0 - 12 g/10 min @Load 2.16 kg, Temperature 230 °C |
8.0 - 12 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Aaron Industries AAROPRENE® GFPP 2020 Glass Filled Polypropylene AAROPRENE® GFPP 2000 Series Glass Reinforced CompoundsMelt flow index may be specified. Color may be specified. |
|||
| Melt Flow | 8.0 - 12 g/10 min @Load 2.16 kg, Temperature 230 °C |
8.0 - 12 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Aaron Industries AAROPRENE® GFPP 2040 Glass Filled Polypropylene AAROPRENE® GFPP 2000 Series Glass Reinforced CompoundsMelt flow index may be specified. Color may be specified. |
|||
| Melt Flow | 8.0 - 12 g/10 min | 8.0 - 12 g/10 min | 230/2.16; May be specified; ASTM D1238 |
| Plastics Group Polifil® T-20 20% Talc-Reinforced Polypropylene Polifil® T series compounds are homopolymer polypropylene resins reinforced with asbestos-free talc. They possess high flex modulus, high deflection temperature, good chemical resistance and colora.. |
|||
| Melt Flow | 8.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
8.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
cm³/10 min. |
| Ineos ABS Centrex® 825 ASA+AES Blend
(discontinued **) Key Features:UnfilledHigh impact or high impact modifiedLight stabilized or stable to lightU.V. stabilized or stable to weatherSuitable processing methods:Profile extrusionSheet extrusionThermoformi.. |
|||