Physical Properties | Metric | English | Comments |
---|---|---|---|
Melt Flow | 4.8 g/10 min @Load 2.16 kg, Temperature 230 °C |
4.8 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
SABIC PP 502P Polypropylene Homopolymer for Raffia Applications Product Description: PP 502P is intended for producing low denier stretched tapes with the following features:Consistent processabilityGood processability at high line speedsLow water carry overGoo.. |
|||
Melt Flow | 4.8 g/10 min @Load 2.16 kg, Temperature 230 °C |
4.8 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
SABIC PP 506P Polypropylene Homopolymer for Raffia Applications Product Description: PP 506P is intended for producing low denier stretched tapes with the following features:Consistent processabilityGood processability at high line speeds and low deniersLow tap.. |
|||
Melt Flow | 4.8 g/10 min @Load 2.16 kg, Temperature 190 °C |
4.8 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
NOVA Chemicals Sclair® 8107 UV8D Butene LLDPE Rotational Molding Resin Excellent ESCR, Excellent low temperature impact properties, Excellent low shrinkage and warpage properties, Very good processability, UL 94-HB listedApplications: Food and laundry materials handlin.. |
|||
Melt Flow | 4.8 g/10 min @Load 5.00 kg, Temperature 200 °C |
4.8 g/10 min @Load 11.0 lb, Temperature 392 °F |
Condition G; ASTM D1238 |
Ineos Nova Zylar® 221 Clear Impact Modified Acrylic Copolymer
(discontinued **) Features: High clarityEnhanced mold releaseGood elongationStyrenic processing advantagesExcellent property retention after ETO and gamma sterilization Applications: DisplaysMedical devicesOffice acc.. |
|||
Melt Flow | 4.8 g/10 min @Load 5.00 kg, Temperature 200 °C |
4.8 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
Ineos Nova Zylar® 220 Clear Impact Modified Acrylic Copolymer
(discontinued **) Features:High clarity Good elongation Styrenic processing advantages Excellent property retention after gamma and ETO sterilization Meets USP XXIII specifications for Class VI plasticsApplications:D.. |
|||
Melt Flow | 4.8 g/10 min @Load 2.16 kg, Temperature 190 °C |
4.8 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
NOVA Chemicals Sclair® 2607 HDPE Injection Molding Resin Features: Excellent stiffness, good impact resistance, low warpage.Applications: Roll-out carts.Data provided by the manufacturer. |
|||
Melt Flow | 4.8 g/10 min @Load 2.16 kg, Temperature 190 °C |
4.8 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
NOVA Chemicals Sclair® 2607-UV14 HDPE Injection Molding Resin Excellent stiffness, Good impact resistance, Low warpageApplications: Roll-out cartsAdditives: Elevated levels of ultraviolet stabilizer packages, Elevated levels of antioxidantsInformation provided.. |
|||
Melt Flow | 4.8 g/10 min @Load 2.16 kg, Temperature 190 °C |
4.8 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
NOVA Chemicals Sclair® 8107G UV8D Butene LLDPE Rotational Molding Resin Excellent ESCR, Excellent low temperature impact properties, Excellent low shrinkage and warpage properties, Very good processability, UL 94-HB listedApplications: Food and laundry materials handlin.. |
|||
Melt Flow | 4.8 g/10 min @Load 2.16 kg, Temperature 190 °C |
4.8 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
NOVA Chemicals Sclair® 14K1 Octene LMDPE Film Resin
(discontinued **) Film Properties. Features: Low gel, excellent optics, good moisture barrier.Applications: Cast overwrap film.Data provided by the manufacturer. |
|||
Melt Flow | 4.8 g/10 min @Load 2.16 kg, Temperature 190 °C |
4.8 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
NOVA Chemicals Sclair® 14K3 Octene LMDPE Film Resin
(discontinued **) Film Properties. Features: Low gel, excellent optics, good moisture barrier.Applications: Cast overwrap film.Data provided by the manufacturer. |
|||
Melt Flow | 4.8 g/10 min @Load 2.16 kg, Temperature 190 °C |
4.8 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
Braskem LH 437 LMDPE Cast Film Extrusion Polyethylene
(discontinued **) Applications: Diapers (back sheet); Absorbent pads (back sheet). Information provided by Braskem |
|||
Melt Flow | 4.8 g/10 min | 4.8 g/10 min | ISO 1133 |
Lucite International Diakon® MG100 Acrylic Bead Polymer, High Transparency PMMA beads offer an exceptional transmission level of 92.5%, an increase of +0.5% in light transmission vs. granular grades - ideal for medical diagnostic devices.Information provided by Lucite Inte.. |
|||
Melt Flow | 4.8 g/10 min | 4.8 g/10 min | ISO 1133 |
Lucite International Diakon® ST25G7 Toughened Acrylic Compound The Diakon® impact PMMA series offer the best combination of impact, chemical and heat resistance and provide rigidity and surface hardness.The grades in the Diakon® series can be processed by.. |
|||
Melt Flow | 4.8 g/10 min | 4.8 g/10 min | ASTM D1238 |
KKPC Kuhmo HI 425EH Extrusion Molding HIPS Key features: ESCR Common Uses: Refrigerator inner liners, door liners, disposable cups, food packaging sheet, wrapping films, trays, washing machinesHIPS is a functional resin made by copolymerizat.. |
|||
Melt Flow | 4.8 g/10 min @Load 21.6 kg, Temperature 190 °C |
4.8 g/10 min @Load 47.6 lb, Temperature 374 °F |
ASTM D1238 |
Solvay Specialty Polymers Cogegum® GFR/320 Polyolefin Cogegum® XLPO-HFFR - Crosslinkable Halogen Free Fire Retardant compound. Silane grafted compound moisture curable by addition of a catalyst masterbatch (Sioplas® method). It consists of a poly.. |
|||
Melt Flow | 4.8 g/10 min @Load 2.16 kg, Temperature 230 °C |
4.8 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
Teknor Apex TEKRON® 4000-25 Thermoplastic Elastomer Information provided by Teknor Apex Company |
|||
Melt Flow | 4.8 g/10 min | 4.8 g/10 min | ASTM D1238L |
Total PPH 3480Z Polypropylene, Extrusion Grade Homopolymer Profile Extrusion GradeProcess Stability --FINA 3480Z is formulated specifically to give excellent process stability in high profile extrusion.High Purity - Low catalyst residues in FINA.. |
|||
Melt Flow | 4.8 g/10 min @Load 2.16 kg, Temperature 330 °C |
4.8 g/10 min @Load 4.76 lb, Temperature 626 °F |
ISO 1133 |
Covestro Apec® DP1-9389/5 Polycarbonate Developmental producteasy flowingeasy to demoldsoftening temperature (VST/B 120)=218 °CPreprocessingMax. Water content |
|||
Melt Flow | 4.8 g/10 min @Load 2.16 kg, Temperature 190 °C |
4.8 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
Entec Hypel® PEHD4/.955 HDPE Available in North America Features: Food Contact Acceptable and High DensityAgency Ratings: FDA 21 CFR 177.1520RoHS Compliant Form: Pellets Information provided by Entec |
|||
Melt Flow | 4.8 g/10 min @Load 5.00 kg, Temperature 260 °C |
4.8 g/10 min @Load 11.0 lb, Temperature 500 °F |
ISO 1133 |
Covestro Bayblend® KU 1-1446* Polycarbonate + ABS Developmental productGrade with improved low-temperature impact strength and petrol resistance for automotive partsin version BBS904 suitable for extrusion/extrusion blow molding and electroplating .. |
|||
Melt Flow | 4.8 g/10 min @Load 2.16 kg, Temperature 230 °C |
4.8 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
DuPont Performance Polymers Hytrel® HTR8241 TPC-ET
(Unverified Data**) Hytrel® HTR8241 is a 65 nom.Shore D, non discoloring stabilizer, plasticiser free high performance resin for extrusion; high viscosity; outstanding mechanical properties up to 120°C and excellent .. |
|||
Melt Flow | 4.8 g/10 min @Load 2.16 kg, Temperature 235 °C |
4.8 g/10 min @Load 4.76 lb, Temperature 455 °F |
|
Arkema Group Rilsan® AZM 30 NOIR T6LD Nylon 12, 30% Glass Fiber Filled (Conditioned) Designation ISO 1874-PA12,MHLR,16-060,GF30Rigid grade with glass fiber (30%) for injection molding. Available color: black. Reinforced light and heat stabilizing agent. Mold-release agent.High rigid.. |
|||
Melt Flow | 4.8 g/10 min @Load 2.16 kg, Temperature 235 °C |
4.8 g/10 min @Load 4.76 lb, Temperature 455 °F |
|
Arkema Group Rilsan® MA 4420 Nylon 12, Flexible Tubing Grade (Conditioned) Designation ISO 1874-PA12-HI,EHL,22-003Flexible grade for tubes extrusion. Available color: black. Light and heat stabilized.Flexibility. High burst pressure and impact strength. Fit for use in a wi.. |
|||
Melt Flow | 4.8 g/10 min @Load 2.16 kg, Temperature 235 °C |
4.8 g/10 min @Load 4.76 lb, Temperature 455 °F |
|
Arkema Group Rilsan® MA 4420 Nylon 12, Flexible Tubing Grade (Dry) Designation ISO 1874-PA12-HI,EHL,22-003Flexible grade for tubes extrusion. Available color: black. Light and heat stabilized.Flexibility. High burst pressure and impact strength. Fit for use in a wi.. |
|||
Melt Flow | 4.8 g/10 min @Load 2.16 kg, Temperature 190 °C |
4.8 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM-D1238 |
Braskem LH537 LLDPE Cast Film Extrusion Polyethylene LH537 is a LLDPE Hexene produced by Braskem. It offers an excellent processability, stiffness, and soft touch for flat die films. It has very low gel contents. It contains slip absent and antiblock .. |
|||
Melt Flow | 4.8 g/10 min @Load 5.00 kg, Temperature 200 °C |
4.8 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
Americas Styrenics EA3130 High Heat Crystal Polystyrene Product CharacteristicsAdditive FreeFood Contact CompliantTypical ApplicationsMedical PartsColor Concentrate CarrierLow Profile AdditivesInformation provided by AmericasStyrenics LLC. |
|||
Melt Flow | 4.8 g/10 min @Load 2.16 kg, Temperature 235 °C |
4.8 g/10 min @Load 4.76 lb, Temperature 455 °F |
|
Arkema Group Rilsan® AZM 30 NOIR T6LD Nylon 12, 30% Glass Fiber Filled (Dry) Designation ISO 1874-PA12,MHLR,16-060,GF30Rigid grade with glass fiber (30%) for injection molding. Available color: black. Reinforced light and heat stabilizing agent. Mold-release agent.High rigid.. |
|||
Melt Flow | 4.8 g/10 min @Load 2.16 kg, Temperature 190 °C |
4.8 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
NOVA Chemicals Sclair® 2607-UV9 HDPE Injection Molding Resin
(discontinued **) Features: Excellent stiffness, good impact resistance, low warpage.Applications: Roll-out carts.Data provided by the manufacturer. |
|||
Melt Flow | 4.8 g/10 min @Load 2.16 kg, Temperature 250 °C |
4.8 g/10 min @Load 4.76 lb, Temperature 482 °F |
ASTM D1238 |
LG Chemical LUPOY NS5000C PC/ABS, High Impact Description: Injection Molding, PC/ABS, Heat Resistance, High Flow, High ImpactApplication: Automotive (Interior)CAS: 103598-77-2 and 9003-56-9Information provided by LG Chemical |