Physical Properties | Metric | English | Comments |
---|---|---|---|
Melt Flow | 0.400 - 50.0 g/10 min | 0.400 - 50.0 g/10 min | Average value: 12.2 g/10 min Grade Count:117 |
Overview of materials for Polyester Thermoplastic Elastomer This property data is a summary of similar materials in the MatWeb database for the category "Polyester Thermoplastic Elastomer". Each property range of values reported is minimum and maximum values.. |
|||
Melt Flow | 0.400 - 43.0 g/10 min | 0.400 - 43.0 g/10 min | Average value: 10.9 g/10 min Grade Count:52 |
Overview of materials for Ethylene Vinyl Acetate Copolymer (EVA), Extrusion/Coating Grade This property data is a summary of similar materials in the MatWeb database for the category "Ethylene Vinyl Acetate Copolymer (EVA), Extrusion/Coating Grade". Each property range of values reported.. |
|||
Melt Flow | 0.400 - 200 g/10 min | 0.400 - 200 g/10 min | Average value: 32.4 g/10 min Grade Count:8 |
Overview of materials for Polybutene This property data is a summary of similar materials in the MatWeb database for the category "Polybutene". Each property range of values reported is minimum and maximum values of appropriate MatWeb .. |
|||
Melt Flow | 0.400 - 31.0 g/10 min | 0.400 - 31.0 g/10 min | Average value: 3.61 g/10 min Grade Count:71 |
Overview of materials for Anhydride-Modified Polyethylene This property data is a summary of similar materials in the MatWeb database for the category "Anhydride-Modified Polyethylene". Each property range of values reported is minimum and maximum values o.. |
|||
Melt Flow | 0.400 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.400 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
ExxonMobil Escorene® LD 705.MJ Molding, extrusion and compounding resin Escorene Ultra LD 705.MJ is a fraction melt index, 13.3 wt% vinyl acetate copolymer suitable for use in making blow molded articles, extruded profiles and compounds.Information provided by ExxonMobi.. |
|||
Melt Flow | 0.400 - 135 g/10 min | 0.400 - 135 g/10 min | Average value: 12.7 g/10 min Grade Count:17 |
Overview of materials for Ethylene-Methyl Acrylate Copolymer, Molding Grade This property data is a summary of similar materials in the MatWeb database for the category "Ethylene-Methyl Acrylate Copolymer, Molding Grade". Each property range of values reported is minimum an.. |
|||
Melt Flow | 0.400 - 9.00 g/10 min | 0.400 - 9.00 g/10 min | Average value: 2.97 g/10 min Grade Count:14 |
Overview of materials for Ethylene-Methyl Acrylate Copolymer, Film Grade This property data is a summary of similar materials in the MatWeb database for the category "Ethylene-Methyl Acrylate Copolymer, Film Grade". Each property range of values reported is minimum and m.. |
|||
Melt Flow | 0.400 - 26.9 g/10 min | 0.400 - 26.9 g/10 min | Average value: 4.70 g/10 min Grade Count:13 |
Overview of materials for Styrene/Methyl Methacrylate Copolymer (SMMA) This property data is a summary of similar materials in the MatWeb database for the category "Styrene/Methyl Methacrylate Copolymer (SMMA)". Each property range of values reported is minimum and max.. |
|||
Melt Flow | 0.400 - 25.0 g/10 min | 0.400 - 25.0 g/10 min | Average value: 6.85 g/10 min Grade Count:182 |
Overview of materials for Polypropylene with 30% Glass Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 30% Glass Fiber Filler". Specific grades with glass content between 25% and 34% are i.. |
|||
Melt Flow | 0.400 - 35.0 g/10 min | 0.400 - 35.0 g/10 min | Average value: 8.14 g/10 min Grade Count:9 |
Overview of materials for Polypropylene with Carbon Black Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with Carbon Black Filler". Each property range of values reported is minimum and maximum v.. |