Physical Properties | Metric | English | Comments |
---|---|---|---|
Melt Flow | 2.5 - 6.0 g/10 min | 2.5 - 6.0 g/10 min | ASTM D1238 |
S&E Specialty Polymers GPE2001F-ROHS PVC Application: GPE2001F-ROHS is flame retardant polyethylene compound designed for wire and cable applications. GPE2001F-ROHS complies with RoHS requirements. GPE2001F-ROHS is suitable for 75°C cont.. |
|||
Melt Flow | 4.0 - 6.0 g/10 min @Load 10.0 kg, Temperature 230 °C |
4.0 - 6.0 g/10 min @Load 22.0 lb, Temperature 446 °F |
ASTM D1238 |
Solvay Specialty Polymers Solef® 6012 Polyvinylidene Fluoride (PVDF)
(Unverified Data**) Solef® 6012 PVDF homopolymer is a high-viscosity PVDF resin and is typically processed by extrusion or compression molding.Information provided by Solvay Specialty Polymers. |
|||
Melt Flow | 4.0 - 6.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
4.0 - 6.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
|
Kazanorgsintez PC-005 Polycarbonate Production Method: Obtained by means of polycondensation method. Application: Intended for product manufacture by method of extrusion and die-casting.Information Provided by Kazanorgsintez |
|||
Melt Flow | 4.0 - 6.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
4.0 - 6.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
FKuR Kunststoff Bio-Flex® F 6611 Compostable PLA Blend The BIO-FLEX® trade name indicates blends of co-polyester and PLA* with, depending on the particular grade, a very high content of natural resource material. BIO-FLEX® does not contain any sta.. |
|||
Melt Flow | 4.0 - 6.0 g/10 min | 4.0 - 6.0 g/10 min | ASTM D1238 |
Micropol Microlin ML27 Linear Polyethylene Rotational Molding Powder Information provided by Micropol Limited |
|||
Melt Flow | 3.0 - 6.0 g/10 min @Load 2.16 kg, Temperature 275 °C |
3.0 - 6.0 g/10 min @Load 4.76 lb, Temperature 527 °F |
ASTM D1238 |
Solvay Specialty Polymers Halar® 930LC Ethylene Chlorotrifluoroethylene Copolymer (ECTFE) Medium ViscosityAdditional Properties: Crystallization Heat - ASTM D3418 40.0 J/g; Heat of Fusion - ASTM D3418 42.0 J/g; Thermal Stability - TGA 405 °CInformation provided by Solvay Specialty Pol.. |
|||
Melt Flow | 4.0 - 6.0 g/10 min @Load 10.0 kg, Temperature 230 °C |
4.0 - 6.0 g/10 min @Load 22.0 lb, Temperature 446 °F |
ASTM D1238 |
Solvay Specialty Polymers Solef® 6012 Polyvinylidene Fluoride (PVDF) Solef® 6012 PVDF homopolymer is a high-viscosity PVDF resin and is typically processed by extrusion or compression molding.Features: High Viscosity; HomopolymerAdditional Properties: Crystallizat.. |
|||
Melt Flow | 1.0 - 6.0 g/10 min @Load 5.00 kg, Temperature 190 °C |
1.0 - 6.0 g/10 min @Load 11.0 lb, Temperature 374 °F |
DIN 53735 |
Stanelco Bioplast® GF 106 Biodegradable Plastic Bioplast 106 is a versatile soft product, suitable for blown film extrusion of completely biodegradable products. Many customers find it is a natural replacement for LDPE. Made from potato starch m.. |
|||
Melt Flow | 2.0 - 6.0 g/10 min | 2.0 - 6.0 g/10 min | ASTM D1238 |
Shuman 710 Utility Black ABS Good impact strength, easy processability, good chemical resistance, good wear and abrasion resistance.Data provided by the manufacturer. |
|||
Melt Flow | 2.0 - 6.0 g/10 min | 2.0 - 6.0 g/10 min | ASTM D1238 |
Shuman 730H White ABS Good impact strength, easy processability, good chemical resistanceInformation provided by Shuman Plastics, Inc. |
|||
Melt Flow | 2.0 - 6.0 g/10 min | 2.0 - 6.0 g/10 min | ASTM D1238 |
Shuman 780 Grey ABS Good impact strength, easy processability, good chemical resistance, good wear and abrasion resistance.Data provided by the manufacturer. |
|||
Melt Flow | 2.0 - 6.0 g/10 min | 2.0 - 6.0 g/10 min | ASTM D1238 |
Shuman 780H Grey ABS Good impact strength, easy processability, good chemical resistanceInformation provided by Shuman Plastics, Inc. |
|||
Melt Flow | 2.0 - 6.0 g/10 min @Load 2.16 kg, Temperature 150 °C |
2.0 - 6.0 g/10 min @Load 4.76 lb, Temperature 302 °F |
|
Taiwan Sheen Soon Sheenthane® AH-571 TPU for Hotmelt Adhesive Thermoplastic polyurethane elastomer for soft hotmelt adhesiveExcellent bonding strength for polyester, TPU, nylon, PVC, leather, fabrics, etc. Melt flow may be customized. Used for hot melt adhes.. |
|||
Melt Flow | 3.0 - 6.0 g/10 min | 3.0 - 6.0 g/10 min | ASTM D1238 |
A. Schulman POLYFLAM™ E-15086-1B Mineral Impact Modified, Low Warp Polypropylene Black DescriptionPolyfort® E-15086-1B is a mineral impact modified low warp polypropylene black.Information provided by A. Schulman. |
|||
Melt Flow | 3.0 - 6.0 g/10 min | 3.0 - 6.0 g/10 min | ASTM D1238 |
A. Schulman POLYFLAM™ E-15086-1B Mineral Impact Modified, Low Warp Polypropylene Black DescriptionPolyfort® E-15086-1B is a mineral impact modified low warp polypropylene black.Information provided by A. Schulman. |
|||
Melt Flow | 4.5 - 6.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
4.5 - 6.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
die 8/2; ISO 1133 |
Addcomp PRIEX® 15005 Maleic Anhydride modified LDPE Functionalised low density polyethylene to be used as compatibiliser for polymer blends or coupling agent for wood flour, natural fibres, or mineral filled polyolefins. Also suitable to reduce pigme.. |
|||
Melt Flow | 4.0 - 6.0 g/10 min @Load 10.0 kg, Temperature 230 °C |
4.0 - 6.0 g/10 min @Load 22.0 lb, Temperature 446 °F |
ASTM D1238 |
3M Dyneon™ PVDF 2066_0002 Fluoroplastic 3M™ Dyneon™ PVDF 2066/0002, a fluoropolymer material, provides an excellent balance of physical properties, processability, surface smoothness, flexibility, and refractive index, allowing for a wi.. |
|||
Melt Flow | 2.0 - 6.0 g/10 min @Load 12.5 kg, Temperature 232 °C |
2.0 - 6.0 g/10 min @Load 27.6 lb, Temperature 450 °F |
ASTM D1238 |
Arkema Group KYNAR® 760 Polyvinylidene Fluoride Homopolymer - Extrusion Characteristics: Natural resin - translucent, off-white hemispheres. High stability in harsh thermal, chemical and ultraviolet environments. High toughness and mechanical strength, low permeabili.. |
|||
Melt Flow | 1.5 - 6.0 g/10 min @Load 2.16 kg, Temperature 200 °C |
1.5 - 6.0 g/10 min @Load 4.76 lb, Temperature 392 °F |
ASTM D1238 |
BecauseWeCare BF90 Biodegradable Plastic Biodegradable and compostable product produced from corn and developed to break down within weeks in a compost environment, without leaving any harmful residues in the process. Certified to the vari.. |
|||
Melt Flow | 1.0 - 6.0 g/10 min @Load 5.00 kg, Temperature 232 °C |
1.0 - 6.0 g/10 min @Load 11.0 lb, Temperature 450 °F |
ASTM D1238 |
Arkema Group KYNAR® 2821-00 Polyvinylidene Fluoride Powder Characteristics: White, non-hygroscopic powder. Flexible. High stability in harsh thermal, chemical and ultraviolet environments. High toughness and mechanical strength, low permeability, abrasi.. |
|||
Melt Flow | 2.0 - 6.0 g/10 min @Load 21.6 kg, Temperature 232 °C |
2.0 - 6.0 g/10 min @Load 47.6 lb, Temperature 450 °F |
ASTM D1238 |
Arkema Group KYNAR® 301-F Polyvinylidene Fluoride Powder Characteristics: Fine milled, white, non-hygroscopic powder. High stability in harsh thermal, chemical and ultraviolet environments. High toughness and mechanical strength, low permeability, abra.. |
|||
Melt Flow | 3.0 - 6.0 g/10 min | 3.0 - 6.0 g/10 min | ASTM D1238 |
A. Schulman POLYFLAM™ E-15086-1B Mineral Impact Modified, Low Warp Polypropylene Black DescriptionPolyfort® E-15086-1B is a mineral impact modified low warp polypropylene black.Information provided by A. Schulman. |
|||
Melt Flow | 1.0 - 6.0 g/10 min | 1.0 - 6.0 g/10 min | ASTM D1238 |
Polymer Resources PPX-FRG10 Modified PPO, UL 94 V-1, 10% Glass Reinforced
(Unverified Data**) Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation. |
|||
Melt Flow | 3.0 - 6.0 g/10 min | 3.0 - 6.0 g/10 min | ASTM D1238 |
A. Schulman POLYFLAM™ E-15086-1B Mineral Impact Modified, Low Warp Polypropylene Black DescriptionPolyfort® E-15086-1B is a mineral impact modified low warp polypropylene black.Information provided by A. Schulman. |
|||
Melt Flow | 2.0 - 6.0 g/10 min @Load 21.6 kg, Temperature 232 °C |
2.0 - 6.0 g/10 min @Load 47.6 lb, Temperature 450 °F |
ASTM D1238 |
Arkema Group KYNAR® 201 Polyvinylidene Fluoride Powder Characteristics: White, non-hygroscopic powder. High stability in harsh thermal, chemical and ultraviolet environments. High toughness and mechanical strength, low permeability, abrasion resistan.. |
|||
Melt Flow | 2.0 - 6.0 g/10 min @Load 12.5 kg, Temperature 232 °C |
2.0 - 6.0 g/10 min @Load 27.6 lb, Temperature 450 °F |
ASTM D1238 |
Arkema Group KYNAR® 761 Polyvinylidene Fluoride Powder Characteristics: White, non-hygroscopic powder. High stability in harsh thermal, chemical and ultraviolet environments. High toughness and mechanical strength, low permeability, abrasion resistan.. |