Physical Properties | Metric | English | Comments |
---|---|---|---|
Melt Flow | 35 - 45 g/10 min @Load 2.16 kg, Temperature 230 °C |
35 - 45 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238/L |
NIZHNEKAMSKNEFTEKHIM PP 1365S (H22S) Propylene Homopolymer Product obtained by polymerization of propylene in presence of complex metalorganic catalysts. It incorporates increased long-term thermal stability, thermal-oxidative degradation resistance when P.. |
|||
Melt Flow | 40 - 45 g/10 min @Load 2.16 kg, Temperature 230 °C |
40 - 45 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238/L |
NIZHNEKAMSKNEFTEKHIM PP 4341S Propylene and Ethylene Copolymer Product obtained by copolymerization of propylene with ethylene in presence of complex metalorganic catalysts. It incorporates increased long-term thermal stability, thermal-oxidative degradation r.. |
|||
Melt Flow | 25 - 45 g/10 min | 25 - 45 g/10 min | ASTM D1238 |
Polymer Resources PC/ABS-FR1-[color]-3 PC Blend, Flame Retardant, Standard Flow, UV Stabilized Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation. |
|||
Melt Flow | 25 - 45 g/10 min @Load 11.6 kg, Temperature 250 °C |
25 - 45 g/10 min @Load 25.6 lb, Temperature 482 °F |
ASTM D1238 |
Polymer Resources PPX-SF2 Modified-PPO, Structural Foam Grade, Flame Retardant Modified-Polyphenylene Oxide, Structural Foam Grade, Standard FlowFeatures: • Flame Retardant • Bromine Free • Chlorine Free • Self ExtinguishingProcess: Foam MoldingNotes: All physical, mec.. |
|||
Melt Flow | 30 - 45 g/10 min @Load 2.16 kg, Temperature 250 °C |
30 - 45 g/10 min @Load 4.76 lb, Temperature 482 °F |
ISO 1133 |
PTS PBT-1100 PBT Resin Information provided by PTS LLC. |
|||
Melt Flow | 25 - 45 g/10 min | 25 - 45 g/10 min | ASTM D1238 |
Polymer Resources PPX-SF2 Modified PPO, Structural Foam Grade, Standard Flow
(Unverified Data**) Process: Foam MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Foam grades tested with foamed parts with a 10% weight reduction rel.. |
|||
Melt Flow | 18 - 45 g/10 min @Load 2.16 kg, Temperature 230 °C |
18 - 45 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
Shanghai Ofluorine T-2 PVDF for Powder Coatings Description: T-2 PVDF belong to thermoplastic fluorocarbon resin, which has high melt flow rate, low melt viscosity. T-2 PVDF has characteristic of chemical resistance, heat resistance, high mechani.. |
|||
Melt Flow | 25 - 45 g/10 min @Load 2.16 kg, Temperature 190 °C |
25 - 45 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 - ISO 1133 |
DuPont Elvaloy® 741 Ethylene/Vinyl Acetate/Carbon Monoxide Copolymer Specialized copolymers deliver flexibility, toughness and weatherability to adhesives, plastics, highways and roofing.Availability: GloballyInformation provided by DuPont. |
|||
Melt Flow | 25 - 45 g/10 min @Load 2.16 kg, Temperature 190 °C |
25 - 45 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 - ISO 1133 |
DuPont Elvaloy® 742 Ethylene/Vinyl Acetate/Carbon Monoxide Copolymer Specialized copolymers deliver flexibility, toughness and weatherability to adhesives, plastics, highways and roofing.Availability: GloballyInformation provided by DuPont. |
|||
Melt Flow | 35 - 45 g/10 min @Load 5.00 kg, Temperature 235 °C |
35 - 45 g/10 min @Load 11.0 lb, Temperature 455 °F |
3 min; ASTM D1238 |
ALM PA-616-GS Filled Nylon 12 Prototyping Polymer 50% glass sphere filled material for improved dimensional stability, increased stiffness, and higher temperature applications when compared to unfilled PA.The PA 616-GS can be processed on any laser.. |
|||
Melt Flow | 30 - 45 g/10 min @Load 2.16 kg, Temperature 250 °C |
30 - 45 g/10 min @Load 4.76 lb, Temperature 482 °F |
ISO 1133 |
BLUESTAR PBT 1100 PBT resin is polymerized by pure terephthalic acid (PTA) and 1,4-butanediol (1,4-BDO) through direct esterification. With well-distributed molecular weight and stable quality, PBT resin possesses go.. |