Physical Properties | Metric | English | Comments |
---|---|---|---|
Melt Flow | 1.0 - 3.0 g/10 min | 1.0 - 3.0 g/10 min | (Condition L) ASTM D-1238 |
Multibase Multi-Flex® TPE G 7680 NAT The burn rate is 1.2 in/min (30 mm/min) based on ASTM FM VSS 302. Multi-Flex TPE contains Kraton™ G.Data provided by Multibase. |
|||
Melt Flow | 1.0 - 3.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.0 - 3.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
Polyplastic Armobond® PE 2K Polyethylene Adhesive Compound Information provided by PolyPlastic Group. |
|||
Melt Flow | 2.0 - 3.0 g/10 min @Load 5.00 kg, Temperature 200 °C |
2.0 - 3.0 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
NIZHNEKAMSKNEFTEKHIM 825E High Impact Polystyrene Grade 825E is a high impact polystyrene designed specifically for extrusion and thermoforming. It is used for production of industrial packaging via deep draw thermoforming and custom multilayer sh.. |
|||
Melt Flow | 1.0 - 3.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.0 - 3.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
Polymer Resources AH-GP1 Acetal Homopolymer, Low Flow, High Melt Strength, Heat Stabilized Process: Molding or ExtrusionNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resources Corporation. |
|||
Melt Flow | 1.0 - 3.0 g/10 min | 1.0 - 3.0 g/10 min | ASTM D1238 |
Polymer Resources AH-GP1-[color]-H Acetal Homopolymer, Low Flow, High Melt Strength, Heat Stabilized Process: Molding or ExtrusionNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation. |
|||
Melt Flow | 2.0 - 3.0 g/10 min | 2.0 - 3.0 g/10 min | ASTM D1238 |
Plaskolite West Optix® CA-81 UVA-7 UV-Absorbing Acrylic Resin Special UV-absorption grade, extrusion and injection moldingApplications: A special UV-absorption acrylic resin for extrusion and injection molding. It is slightly lubricated for ease of processing.. |
|||
Melt Flow | 0.30 - 3.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.30 - 3.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
Polymer Resources AC-G25 Acetal Copolymer, 25% Glass Reinforced Process: Molding or ExtrusionNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resources Corporation. |
|||
Melt Flow | 0.20 - 3.0 g/10 min | 0.20 - 3.0 g/10 min | on the basis of basic grades 10703-020, 10803-020, and 18503-020, for masterbatches of other applications (coloring general purpose products, coloring toys, coloring food containers |
Kazanorgsintez P2KP Polyethylene Pigment Masterbatches Production Method: P2KP polyethylene pigment masterbatches are produced on the basis of low density polyethylene with high content of masterbatches. Application: P2KP polyethylene pigment masterbatc.. |
|||
Melt Flow | 1.0 - 3.0 g/10 min | 1.0 - 3.0 g/10 min | on the basis of basic grades 10703-020, 10803-020, and 18503-020, for cable masterbatches |
Kazanorgsintez P2KP Polyethylene Pigment Masterbatches Production Method: P2KP polyethylene pigment masterbatches are produced on the basis of low density polyethylene with high content of masterbatches. Application: P2KP polyethylene pigment masterbatc.. |
|||
Melt Flow | 2.0 - 3.0 g/10 min @Load 5.00 kg, Temperature 190 °C |
2.0 - 3.0 g/10 min @Load 11.0 lb, Temperature 374 °F |
ISO 1133 |
FKuR Kunststoff Fibrolon® P 8540 Wood-Plastic Compound, Fiber Reinforced FIBROLON® are fiber reinforced compounds. Fibrolon® P 8540 has a polypropylene base. With the brand name of FIBROLON® FKuR has developed natural fiber reinforced compounds (Wood-Plastics-C.. |
|||
Melt Flow | 2.4 - 3.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.4 - 3.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
FKuR Kunststoff Terralene® LL 1303 Biobased Polyethylene With the brand name Terralene® FKuR offers biobased polyethylene compounds made using Braskem's Green PE. When compared to conventional polyethylene (PE), the main difference is that the ethanol.. |
|||
Melt Flow | 1.5 - 3.0 g/10 min @Load 5.00 kg, Temperature 372 °C |
1.5 - 3.0 g/10 min @Load 11.0 lb, Temperature 702 °F |
ASTM D1238 |
Solvay Specialty Polymers Hyflon® PFA 125 Perfluoroalkoxy (PFA) Hyflon® PFA is a unique family of semi-crystalline, melt processable perfluoropolymers which combine excellent mechanical characteristics to unique properties such as chemical inertness, heat res.. |
|||
Melt Flow | 1.5 - 3.0 g/10 min @Load 5.00 kg, Temperature 372 °C |
1.5 - 3.0 g/10 min @Load 11.0 lb, Temperature 702 °F |
ASTM D1238 |
Solvay Specialty Polymers Hyflon® PFA 420 Perfluoroalkoxy (PFA) Hyflon® PFA is a family of semi-crystalline, melt processable perfluoropolymers which combine excellent mechanical characteristics to unique properties such as chemical inertness, heat resistance.. |
|||
Melt Flow | 1.0 - 3.0 g/10 min | 1.0 - 3.0 g/10 min | 190/2.16; May be specified; ASTM D1238 |
Plastics Group Polifil® RP-LDPE Low Density Polyethylene Polifil® RP-Low Density Polyethylene is a soft, tough material with good clarity and high chemical resistance. LDPE remains flexible and retains impact strength at very low temperatures. High melt .. |
|||
Melt Flow | 1.0 - 3.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.0 - 3.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
|
Unitika TERRAMAC HV-6250H Polylactic Acid (PLA) Foam, Extrusion, blow, and foam sheet grades. Bio-based materials produced from annually renewable raw materials.Information provided by Unitika Ltd. |
|||
Melt Flow | 2.0 - 3.0 g/10 min @Load 5.00 kg, Temperature 372 °C |
2.0 - 3.0 g/10 min @Load 11.0 lb, Temperature 702 °F |
|
Daikin NEOFLON NP-130 FEP Pellets NEOFLON FEP molding materials are supplied as translucent white pellets for melt flow processes.Processing Methods: Extrusion.Applications: Heavy wall wire insulation, cable jacketing, pipe, shrinka.. |
|||
Melt Flow | 2.0 - 3.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.0 - 3.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
|
Breplast Bretene HD Caps Flakes High Density Polyethylene Recovered polyethylene compositeInformation provided by Breplast S.p.A. |
|||
Melt Flow | 2.0 - 3.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.0 - 3.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
|
Breplast Bretene HDT High Density Polyethylene Recovered polyethylene compositeInformation provided by Breplast S.p.A. |
|||
Melt Flow | 1.0 - 3.0 g/10 min | 1.0 - 3.0 g/10 min | |
Asahi Glass Fluon® P-66P PFA Perfluoropolymer Fluon® PFA is a copolymer of tetrafluoroethylene (C2F4) and perfluoroalkoxyethylene, which has excellent chemical, electrical, mechanical and surface properties. PFA retains many inherent character.. |
|||
Melt Flow | 1.0 - 3.0 g/10 min | 1.0 - 3.0 g/10 min | |
Asahi Glass Fluon® P-802UP PFA Perfluoropolymer Fluon® PFA is a copolymer of tetrafluoroethylene (C2F4) and perfluoroalkoxyethylene, which has excellent chemical, electrical, mechanical and surface properties. PFA retains many inherent character.. |
|||
Melt Flow | 1.5 - 3.0 g/10 min @Load 5.00 kg, Temperature 372 °C |
1.5 - 3.0 g/10 min @Load 11.0 lb, Temperature 702 °F |
ASTM D1238 |
Solvay Specialty Polymers Hyflon® PFA 420 Perfluoroalkoxy (PFA)
(Unverified Data**) Hyflon® PFA is a family of semi-crystalline, melt processable perfluoropolymers which combine excellent mechanical characteristics to unique properties such as chemical inertness, heat resistance, .. |
|||
Melt Flow | 1.0 - 3.0 g/10 min | 1.0 - 3.0 g/10 min | ASTM D1238 |
Polymer Resources AH-GP1 Acetal Homopolymer, Low Flow, High Melt Strength
(Unverified Data**) Process: Molding or ExtrusionNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation. |
|||
Melt Flow | 2.5 - 3.0 g/10 min | 2.5 - 3.0 g/10 min | |
Ashley Polymers Ashlene® RH180 Acetal Extrusion grade reprocessed homopolymer, excellent toughness, strength, stiffness and lubricity. Available in Natural and Black. Natural is designated RH180; Black is designated RH180B.Data provid.. |
|||
Melt Flow | 1.0 - 3.0 g/10 min | 1.0 - 3.0 g/10 min | ASTM D1238 |
Polymer Resources PPX-FR6 Modified PPO, UL 94 V-0 with HDT of 300 F
(Unverified Data**) Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation. |
|||
Melt Flow | 2.0 - 3.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.0 - 3.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
|
Breplast Bretene HDT Light High Density Polyethylene Recovered polyethylene compositeInformation provided by Breplast S.p.A. |