- Polymer Property : Melt Flow = 10 g/10 min
Polymer Property : Melt Flow = 10 g/10 min Product List
Physical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Flow | 7.0 - 10 g/10 min @Load 2.16 kg, Temperature 230 °C |
7.0 - 10 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238/L |
| NIZHNEKAMSKNEFTEKHIM PP 4316M (EP1X35AF) Propylene and Ethylene Copolymer Product obtained by copolymerization of propylene with ethylene in presence of complex metalorganic catalysts. It incorporates increased long-term thermal stability, thermal-oxidative degradation r.. |
|||
| Melt Flow | 2.0 - 10 g/10 min @Load 2.16 kg, Temperature 265 °C |
2.0 - 10 g/10 min @Load 4.76 lb, Temperature 509 °F |
ASTM D1238 |
| Polymer Resources PC/TP-GP3-G10 PC/Polyester Alloy, 10% Glass Reinforced Superior Chemical Resistance, 10% Glass ReinforcedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information pr.. |
|||
| Melt Flow | 2.0 - 10 g/10 min @Load 1.20 kg, Temperature 300 °C |
2.0 - 10 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Polymer Resources PC-G40-[color]-1 Polycarbonate, 40% Glass Reinforced with Mold Release Polycarbonate, 40% Glass Reinforced with Mold ReleaseProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information.. |
|||
| Melt Flow | 5.0 - 10 g/10 min @Load 1.20 kg, Temperature 300 °C |
5.0 - 10 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Polymer Resources PC-GP1-D-[color]-5 Polycarbonate, FDA-compliant Feedstocks, Low Flow Polycarbonate, FDA-compliant Feedstocks, Low FlowProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information pro.. |
|||
| Melt Flow | 5.0 - 10 g/10 min @Load 1.20 kg, Temperature 300 °C |
5.0 - 10 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Polymer Resources PC-GP1-TFE5 Polycarbonate, 5% PTFE, Wear Resistant, Low Flow Polycarbonate, 5% PTFE, General Purpose, Wear Resistant, Low FlowProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.. |
|||
| Melt Flow | 5.0 - 10 g/10 min @Load 1.20 kg, Temperature 300 °C |
5.0 - 10 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Polymer Resources PC-UV1-D-[color]-1 Polycarbonate, UV-stabilized, Low Flow with Mold Release Polycarbonate, UV-stabilized, Low Flow with Mold ReleaseProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Informat.. |
|||
| Melt Flow | 2.0 - 10 g/10 min @Load 11.6 kg, Temperature 250 °C |
2.0 - 10 g/10 min @Load 25.6 lb, Temperature 482 °F |
ASTM D1238 |
| Polymer Resources PPX-G5 Modified-PPO, 5% Glass Reinforced Modified-Polyphenylene Oxide, 5% Glass ReinforcedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information pro.. |
|||
| Melt Flow | 1.0 - 10 g/10 min @Load 5.00 kg, Temperature 250 °C |
1.0 - 10 g/10 min @Load 11.0 lb, Temperature 482 °F |
ASTM D1238 |
| Polymer Resources PC/ABS-G30 General Purpose PC/ABS Alloy, 30% Glass Filled PC/ABS Alloy, General Purpose, 30% Glass FilledProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provi.. |
|||
| Melt Flow | 1.0 - 10 g/10 min @Load 5.00 kg, Temperature 250 °C |
1.0 - 10 g/10 min @Load 11.0 lb, Temperature 482 °F |
ASTM D1238 |
| Polymer Resources PC/ABS-G40 General Purpose PC/ABS Alloy, 40% Glass Filled PC/ABS Alloy, General Purpose, 40% Glass FilledProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provi.. |
|||
| Melt Flow | 5.0 - 10 g/10 min @Load 1.20 kg, Temperature 300 °C |
5.0 - 10 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Polymer Resources PC-FR1A-D-[color]-3 Polycarbonate, Flame Retardant, Low Flow, UV-stabilized Polycarbonate, Flame Retardant, Low Flow, UV-stabilizedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Informati.. |
|||
| Melt Flow | 8.0 - 10 g/10 min @Load 2.16 kg, Temperature 190 °C |
8.0 - 10 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| FKuR Kunststoff Bio-Flex® S 5630 Compostable PLA Blend The BIO-FLEX® trade name indicates blends of co-polyester and PLA* with, depending on the particular grade, a very high content of natural resource material. BIO-FLEX® does not contain any sta.. |
|||
| Melt Flow | 7.0 - 10 g/10 min | 7.0 - 10 g/10 min | ASTM D1238 |
| Kolon KOCETAL® LF302 Wear Modified Acetal Resin Improved wear property and dimensional stability. Applications: Products for low noise and precision gear. Information provided by API-Kolon. |
|||
| Melt Flow | 3.0 - 10 g/10 min | 3.0 - 10 g/10 min | ASTM D 1238 |
| Karina 920-10/156-Y-IS-BZ White PVC Compound Information provided by Karina Indústria e Comércio de Plásticos Ltda. |
|||
| Melt Flow | 4.0 - 10 g/10 min | 4.0 - 10 g/10 min | ASTM D1238 |
| Shuman FR380 Grey PC/ABS Alloy, Flame Retardant Excellent flame retardancy, good impact strength, easy processability, good surface gloss, good chemical resistance, self extinguishing Formerly Shuman FR705 ABS/PC AlloyInformation provided by Shum.. |
|||
| Melt Flow | 5.0 - 10 g/10 min | 5.0 - 10 g/10 min | 230/2.16; May be specified; ASTM D1238 |
| Plastics Group Polifil® GFRMPPCC-30 30% Glass Reinforced Polypropylene, High Impact Polifil® GFRMPPCC series compounds are high impact polypropylenes reinforced with chemically coupled glass fibers. This combination provides higher impact strength while retaining high stiffness.Ap.. |
|||
| Melt Flow | 6.0 - 10 g/10 min @Temperature 230 °C |
6.0 - 10 g/10 min @Temperature 446 °F |
ASTM D1238 |
| A. Schulman PP 1259 Polypropylene Medium Impact Polypropylene DescriptionPolypropylene PP 1259 is a medium impact polypropylene with easier molding characteristics for thinner parts and longer flow distances. Lower molding pressures and heats often reduce war.. |
|||
| Melt Flow | 6.0 - 10 g/10 min @Temperature 230 °C |
6.0 - 10 g/10 min @Temperature 446 °F |
ASTM D1238 |
| A. Schulman PP 1259 Polypropylene Medium Impact Polypropylene DescriptionPolypropylene PP 1259 is a medium impact polypropylene with easier molding characteristics for thinner parts and longer flow distances. Lower molding pressures and heats often reduce war.. |
|||
| Melt Flow | 5.0 - 10 g/10 min | 5.0 - 10 g/10 min | ASTM D1238 |
| A. Schulman POLYFORT™ FPP 1182 Talc Fortified Impact Resistant Polypropylene DescriptionPolyfort® FPP 1182 is a 20% talc fortified impact resistant polypropylene.Information provided by A. Schulman. |
|||
| Melt Flow | 5.0 - 10 g/10 min | 5.0 - 10 g/10 min | 230/2.16; May be specified; ASTM D1238 |
| Plastics Group Polifil® GFPPCC-10 10% Glass Reinforced Polypropylene Polifil® GFPPCC series compounds are homopolymer polypropylenes reinforced with chemically coupled glass fibers. These compounds offer superior strength and stiffness, improved elevated temperature.. |
|||
| Melt Flow | 5.0 - 10 g/10 min | 5.0 - 10 g/10 min | 230/2.16; May be specified; ASTM D1238 |
| Plastics Group Polifil® GFRMPPCC-20 20% Glass Reinforced Polypropylene, High Impact Polifil® GFRMPPCC series compounds are high impact polypropylenes reinforced with chemically coupled glass fibers. This combination provides higher impact strength while retaining high stiffness.Ap.. |
|||
| Melt Flow | 6.0 - 10 g/10 min @Temperature 230 °C |
6.0 - 10 g/10 min @Temperature 446 °F |
ASTM D1238 |
| A. Schulman PP 1259 Polypropylene Medium Impact Polypropylene DescriptionPolypropylene PP 1259 is a medium impact polypropylene with easier molding characteristics for thinner parts and longer flow distances. Lower molding pressures and heats often reduce war.. |
|||
| Melt Flow | 5.0 - 10 g/10 min | 5.0 - 10 g/10 min | ISO 1133 |
| Chengdu Polyster FH5550 Thermoplastic Polyether-ester Elastomer (TPEE) Blend of H5550 and self-made flame retardant material. Flame retardant, good balance of low and high temperature properties. Applications requiring flame retardancy, such as wires, cables and optica.. |
|||
| Melt Flow | 7.0 - 10 g/10 min | 7.0 - 10 g/10 min | ISO 1133 |
| Chengdu Polyster H7560 Thermoplastic Polyether-ester Elastomer (TPEE) High modulus molding and injection grade. Contains improved color- stable antioxidants. Good balance of modulus and toughness. Parts and components of automobile, wires, cables and optical fiber, ho.. |
|||
| Melt Flow | 7.0 - 10 g/10 min | 7.0 - 10 g/10 min | ISO 1133 |
| Chengdu Polyster H9275Y Thermoplastic Polyether-ester Elastomer (TPEE) High modulus molding and injection grade. Contains improved color- stable antioxidants. Excellent heat-ageing resistance and toughness. Applications requiring high strength, high toughness and good .. |
|||
| Melt Flow | 6.0 - 10 g/10 min | 6.0 - 10 g/10 min | ASTM D1238 |
| Buckeye Polymers BP HDPE 9610 R RLK High Density Polyethylene Product Information: Our HDPE grade of materials are designed to offer excellent physical properties while providing cost savings versus higher cost prime equivalents. Buckeye Polymers HDPE materia.. |
|||
| Melt Flow | 6.0 - 10 g/10 min | 6.0 - 10 g/10 min | ASTM D1238 |
| Buckeye Polymers BP RPP 2008 T NAT Polypropylene, Talc Filled Product Information: Our Talc filled product lines exhibit excellent properties such as high stiffness, surface aesthetics, low coefficient of thermal expansion, low shrinkage, improved scratch and .. |
|||
| Melt Flow | 5.0 - 10 g/10 min | 5.0 - 10 g/10 min | ASTM D1238 |
| Aaron Industries AAROPRENE® GFABS 4020 Glass Filled Acrylonitrile-Butadiene Styrene AAROPRENE® GFABS 4000 Series Reinforced CompoundsMelt flow index may be specified. Color may be specified. |
|||
| Melt Flow | 5.0 - 10 g/10 min | 5.0 - 10 g/10 min | ASTM D1238 |
| Aaron Industries AAROPRENE® GFABS 4030 Glass Filled Acrylonitrile-Butadiene Styrene AAROPRENE® GFABS 4000 Series Reinforced CompoundsMelt flow index may be specified. Color may be specified. |
|||
| Melt Flow | 4.0 - 10 g/10 min @Load 1.20 kg, Temperature 300 °C |
4.0 - 10 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Polymer Resources PCSF-FRG20 Polycarbonate, 20% Glass Reinforced Structural Foam Grade Polycarbonate, 20% Glass Reinforced Structural Foam GradeFeatures: • Flame Retardant • Foamable • Self ExtinguishingProcess: Foam MoldingNotes: All physical, mechanical and thermal testing con.. |
|||
| Melt Flow | 3.0 - 10 g/10 min | 3.0 - 10 g/10 min | ASTM D1238 |
| Polymer Resources PPX-MF-FR3 Modified PPO, UL 94 V-0 with HDT of 230 F, Mineral Reinforced
(Unverified Da Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation. |
|||