Physical Properties | Metric | English | Comments |
---|---|---|---|
Melt Flow | 1.2 - 1.5 g/10 min @Load 2.16 kg, Temperature 230 °C |
1.2 - 1.5 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238/L |
NIZHNEKAMSKNEFTEKHIM PP 8300G (EPYS30RE) Propylene and Ethylene Block Polymer Product obtained by copolymerization of propylene with ethylene in presence of complex metalorganic catalysts. It incorporates increased long-term thermal stability, thermal-oxidative degradation r.. |
|||
Melt Flow | 0.50 - 1.5 g/10 min @Load 5.00 kg, Temperature 200 °C |
0.50 - 1.5 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
GRECO ISOPAK 547 ABS Resin High Impact GradeInformation provided by Greater Eastern Resins Industrial Co., Ltd. |
|||
Melt Flow | 0.50 - 1.5 g/10 min @Load 5.00 kg, Temperature 200 °C |
0.50 - 1.5 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
GRECO ISOPAK 569 ABS Resin Extrusion GradeInformation provided by Greater Eastern Resins Industrial Co., Ltd. |
|||
Melt Flow | 1.1 - 1.5 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.1 - 1.5 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238-00 |
Ipiranga Petrochem PH 0130 Polypropylene The production of polypropylene (PP) employs Spheripol technology from Montell / Italy. This technology has been acclaimed all over the world and is known as clean technology, because it does not pr.. |
|||
Melt Flow | 1.1 - 1.5 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.1 - 1.5 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238-00 |
Ipiranga Petrochem PH 0130 Polypropylene The production of polypropylene (PP) employs Spheripol technology from Montell / Italy. This technology has been acclaimed all over the world and is known as clean technology, because it does not pr.. |
|||
Melt Flow | 0.50 - 1.5 g/10 min @Temperature 230 °C |
0.50 - 1.5 g/10 min @Temperature 446 °F |
Condition L; ASTM D1238 |
A. Schulman POLYFORT™ FPP 892E Extrusion and Blow Molding Grade Homopolymer Polypropylene DescriptionPolyfort® FPP 892E is an extrusion and blow molding grade 20% mineral-filled homopolymer polypropylene.Information provided by A. Schulman. |
|||
Melt Flow | 0.50 - 1.5 g/10 min @Temperature 230 °C |
0.50 - 1.5 g/10 min @Temperature 446 °F |
Condition L; ASTM D1238 |
A. Schulman POLYFORT™ FPP 892E Extrusion and Blow Molding Grade Homopolymer Polypropylene DescriptionPolyfort® FPP 892E is an extrusion and blow molding grade 20% mineral-filled homopolymer polypropylene.Information provided by A. Schulman. |
|||
Melt Flow | 0.50 - 1.5 g/10 min @Temperature 230 °C |
0.50 - 1.5 g/10 min @Temperature 446 °F |
Condition L; ASTM D1238 |
A. Schulman POLYFORT™ FPP 892E Extrusion and Blow Molding Grade Homopolymer Polypropylene DescriptionPolyfort® FPP 892E is an extrusion and blow molding grade 20% mineral-filled homopolymer polypropylene.Information provided by A. Schulman. |
|||
Melt Flow | 0.50 - 1.5 g/10 min @Temperature 230 °C |
0.50 - 1.5 g/10 min @Temperature 446 °F |
Condition L; ASTM D1238 |
A. Schulman POLYFORT™ FPP 892E Extrusion and Blow Molding Grade Homopolymer Polypropylene DescriptionPolyfort® FPP 892E is an extrusion and blow molding grade 20% mineral-filled homopolymer polypropylene.Information provided by A. Schulman. |
|||
Melt Flow | 0.50 - 1.5 g/10 min @Temperature 230 °C |
0.50 - 1.5 g/10 min @Temperature 446 °F |
Condition L; ASTM D1238 |
A. Schulman POLYFORT™ FPP 892E Extrusion and Blow Molding Grade Homopolymer Polypropylene DescriptionPolyfort® FPP 892E is an extrusion and blow molding grade 20% mineral-filled homopolymer polypropylene.Information provided by A. Schulman. |
|||
Melt Flow | 0.50 - 1.5 g/10 min @Temperature 230 °C |
0.50 - 1.5 g/10 min @Temperature 446 °F |
Condition L; ASTM D1238 |
A. Schulman POLYFORT™ FPP 892E Extrusion and Blow Molding Grade Homopolymer Polypropylene DescriptionPolyfort® FPP 892E is an extrusion and blow molding grade 20% mineral-filled homopolymer polypropylene.Information provided by A. Schulman. |
|||
Melt Flow | 0.50 - 1.5 g/10 min | 0.50 - 1.5 g/10 min | ISO 1133 |
Chengdu Polyster H3303B Thermoplastic Polyether-ester Elastomer (TPEE) Low modulus molding and extrusion grade. Contains color-stable antioxidants. Excellent low-temperature properties. Excellent flex-fatigue resistance. Excellent creep resistance. CVJ boots, hose jack.. |
|||
Melt Flow | 0.50 - 1.5 g/10 min | 0.50 - 1.5 g/10 min | ISO 1133 |
Chengdu Polyster H4543B Thermoplastic Polyether-ester Elastomer (TPEE) Low modulus molding and extrusion grade. Contains color-stable antioxidants. Good balance of low and high temperature properties. Excellent flex-fatigue resistance. Excellent creep resistance. CVJ b.. |
|||
Melt Flow | 0.50 - 1.5 g/10 min | 0.50 - 1.5 g/10 min | ISO 1133 |
Chengdu Polyster H5550B Thermoplastic Polyether-ester Elastomer (TPEE) Low modulus molding and extrusion grade. Contains color-stable antioxidants. Good balance of low and high temperature properties. Excellent flex-fatigue resistance. Excellent creep resistance. CVJ b.. |
|||
Melt Flow | 0.50 - 1.5 g/10 min | 0.50 - 1.5 g/10 min | ISO 1133 |
Chengdu Polyster H605B Thermoplastic Polyether-ester Elastomer (TPEE) Medium modulus molding and extrusion grade. Contains color-stable antioxidants. Good balance of low and high temperature properties. Good melt stability. CVJ boots, dust cover, bellows, jackets and .. |
|||
Melt Flow | 0.80 - 1.5 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.80 - 1.5 g/10 min @Load 4.76 lb, Temperature 374 °F |
|
Breplast Bretene LD BT Thermoplastic Composite, 50% LD + 50% PP Recovered polypropylene and polyethylene compositeInformation provided by Breplast S.p.A. |