Physical Properties | Metric | English | Comments |
---|---|---|---|
Melt Flow | 8.1 g/10 min @Load 2.16 kg, Temperature 190 °C |
8.1 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
DuPont Bynel® E326 Acid-/Acrylate-Modified EVA Adhesive Resin
(discontinued **) Bynel® Series 3100 resins are acid/acrylate-modified ethylene vinyl acetate polymers. They are available in pellet form for use in conventional extrusion and coextrusion equipment designed to proce.. |
|||
Melt Flow | 8.1 g/10 min @Load 1.20 kg, Temperature 300 °C |
8.1 g/10 min @Load 2.65 lb, Temperature 572 °F |
|
Lehmann & Voss LUVOCOM® 50-7856/FR/BK Polycarbonate, with carbon fiber Applications: Data processing machinery, precision engineering, film and photo industry, sporting and leisure goods, medical enineering.High-strength and high-stiff parts; low coefficient of expansi.. |
|||
Melt Flow | 8.1 g/10 min @Load 1.20 kg, Temperature 300 °C |
8.1 g/10 min @Load 2.65 lb, Temperature 572 °F |
Calculated from Volume Flow Rate of 6 cm<sup>3</sup>/10min.; ISO 1133 |
Mitsubishi Xantar® G4F 23 R Polycarbonate-20% Glass Reinforced Xantar® materials are engineered for performance, consistency and reliability. This makes Xantar® resins ideal for interior automotive components, electrical equipment and consumer appliances .. |
|||
Melt Flow | 8.1 g/10 min @Load 1.20 kg, Temperature 300 °C |
8.1 g/10 min @Load 2.65 lb, Temperature 572 °F |
Calculated from Volume Flow Rate of 6 cm<sup>3</sup>/10min.; ISO 1133 |
Mitsubishi Xantar® G4F 23 UR Polycarbonate-20% Glass Reinforced Xantar® materials are engineered for performance, consistency and reliability. This makes Xantar® resins ideal for interior automotive components, electrical equipment and consumer appliances .. |
|||
Melt Flow | 8.1 g/10 min @Load 1.20 kg, Temperature 300 °C |
8.1 g/10 min @Load 2.65 lb, Temperature 572 °F |
Calculated from Volume Flow Rate of 6 cm<sup>3</sup>/10min.; ISO 1133 |
Mitsubishi Xantar® SF 2220 Polycarbonate-20% Glass Reinforced Xantar® materials are engineered for performance, consistency and reliability. This makes Xantar® resins ideal for interior automotive components, electrical equipment and consumer appliances .. |
|||
Melt Flow | 8.1 g/10 min @Load 1.20 kg, Temperature 300 °C |
8.1 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
SABIC Innovative Plastics LNP LUBRICOMP Lexan_LF1510A PC LNP* Lubricomp* Lexan_LF1510A compound is a 10% glass reinforced, 15% PTFE filled PC. Flame retardant and wear resistant. Tight tolerances. |
|||
Melt Flow | 8.1 g/10 min @Load 1.20 kg, Temperature 300 °C |
8.1 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
SABIC Innovative Plastics LNP LUBRICOMP Lexan_LF1510A PC (Asia Pacific) 10% glass reinforced/15% PTFE filled PC. Flame retardant and wear resistant. Tight tolerances. |
|||
Melt Flow | 8.1 g/10 min @Load 1.20 kg, Temperature 300 °C |
8.1 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
SABIC Innovative Plastics LNP LUBRICOMP Lexan_LF1510A PC (Europe-Africa-Middle East) LNP* Lubricomp* Lexan_FL1510 compound is a 10% glass reinforced, 15% PTFE filled PC. Flame retardant and wear resistant. Tight tolerances. |
|||
Melt Flow | 8.1 g/10 min @Load 6.60 kg, Temperature 295 °C |
8.1 g/10 min @Load 14.6 lb, Temperature 563 °F |
ASTM D1238 |
SABIC Innovative Plastics ULTEM 1285 PEI Transparent Polyetherimide blend. ECO Conforming. US FDA and EU Food Contact Compliant in recognized colors. |
|||
Melt Flow | 8.1 g/10 min @Load 6.60 kg, Temperature 295 °C |
8.1 g/10 min @Load 14.6 lb, Temperature 563 °F |
ASTM D1238 |
SABIC Innovative Plastics ULTEM 1285 PEI (Asia Pacific) Transparent Polyetherimide blend. ECO Conforming. US FDA and EU Food Contact compliant in recognized colors. |
|||
Melt Flow | 8.1 g/10 min @Load 6.60 kg, Temperature 295 °C |
8.1 g/10 min @Load 14.6 lb, Temperature 563 °F |
ASTM D1238 |
SABIC Innovative Plastics ULTEM DU319 PEI Transparent Polyetherimide blend. ECO Conforming. US FDA and EU Food Contact Compliant in recognized colors. |
|||
Melt Flow | 8.1 - 12 g/10 min | 8.1 - 12 g/10 min | B |
Shandong Dongyue Shenzhou New Material Co DS600 Perfluorinated Ethylene-Propylene Copolymer Conformable with: Q/DYS 003-2007Fluorinated Ethylene Propylene resin is the copolymer of the TFE and HFP, with good thermal stability, outstanding chemical inertness, good electrical insulation, and.. |
|||
Melt Flow | 8.1 g/10 min @Load 2.16 kg, Temperature 190 °C |
8.1 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
DuPont Bynel® 3126 Adhesive Resin Bynel® Series 3100 resins are acid/acrylate-modified ethylene vinyl acetate polymers. They are available in pellet form for use in conventional extrusion and coextrusion equipment designed to proce.. |
|||
Melt Flow | 8.1 g/10 min @Load 2.16 kg, Temperature 190 °C |
8.1 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
Braskem BC818 Extrusion Coating Low Density Polyethylene Description: BC818 is a grade produced under high pressure in an autoclave reactor. In the coating process it presents very good optical properties, low neck-in, good film stability, and good adhesi.. |
|||
Melt Flow | 8.1 g/10 min @Load 2.16 kg, Temperature 190 °C |
8.1 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
BASF Ultraform® N2650 Z4 (LEV) POM Description: Is a POM + PUR, elastomer-modified injection-molding grades with high impact strength for clips, snap and fastening elements, also for components subject to impact stress.Information pr.. |
|||
Melt Flow | 8.1 g/10 min @Load 2.16 kg, Temperature 190 °C |
8.1 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
BASF Ultraform® N2650 Z6 (LEV) POM Description: Is a POM + PUR, elastomer-modified injection-molding grade for applications requiring the highest impact strength together with low stiffness.Information provided by BASF |