Physical Properties | Metric | English | Comments |
---|---|---|---|
Melt Flow | 60 g/10 min @Load 2.16 kg, Temperature 230 °C |
60 g/10 min @Load 4.76 lb, Temperature 446 °F |
Condition L; ASTM D1238 |
PolyMirae Moplen HP740T Injection Molding (Thin Wall) Grade Polypropylene Moplen HP740T is a nucleated polypropylene HOMO polymer manufactured by PMC under the license of BASELL using the Spheripol process. Moplen HP740T is a homopolymer selected by customers for use in t.. |
|||
Melt Flow | 60 g/10 min @Pressure 0.655 MPa |
60 g/10 min @Pressure 95.0 psi |
Severs Efflux; Geon® 1010 |
PolyOne Geon™ 120 Series 121AR Polyvinyl Chloride Homopolymer (PVC Homopolymer) Note: The value set forth represent typical values and PolyOne Corporation, therefore, makes no representation that the material in any particular shipment will conform to the listed properties. Pac.. |
|||
Melt Flow | 60 g/10 min @Load 2.16 kg, Temperature 190 °C |
60 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
M. Holland Company LD800 LDPE
(discontinued **) Features: High Clarity, High Flow, Narrow Molecular Wt. Dist., Good Processability, Warp ResistantUses: Closure Caps, Drink LidsApprovals: FDA 21 CFR 177.1520(c) 2.2 and ASTM D 1248, I, Class A, Cat.. |
|||
Melt Flow | <= 60 g/10 min @Load 10.0 kg, Temperature 380 °C |
<= 60 g/10 min @Load 22.0 lb, Temperature 716 °F |
|
Lehmann & Voss LUVOCOM® 1105-8422 PEEK, with carbon fiber, PTFE, lubricant modified Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Strong, stiff parts; low thermal coefficient of expansion.Dynamic stressed parts at high m.. |
|||
Melt Flow | 60 g/10 min @Load 2.16 kg, Temperature 230 °C |
60 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
Inno-Comp INNOPOL® CS 2-9514 10% Talc-Filled, Elastomer Modified Polypropylene Block-Copolymer INNOPOL® CS 2-9514 is a 10% talc-filled, elastomer modified compound based on polypropylene block-copolymer. This grade is available in nature and custom colored form.INNOPOL® CS 2-9514 is dev.. |
|||
Melt Flow | 60 - 100 g/10 min @Load 2.16 kg, Temperature 170 °C |
60 - 100 g/10 min @Load 4.76 lb, Temperature 338 °F |
ISO 1133 |
Lubrizol Advanced Materials PEARLBOND® 523 Linear Thermoplastic Polyurethane Pearlbond™ 523 is a linear, polycaprolactone-copolyester polyurethane, supplied in form of white spherical granules with a very high crystallization rate and a very high thermoplasticity level... |
|||
Melt Flow | 60 g/10 min @Load 5.00 kg, Temperature 275 °C |
60 g/10 min @Load 11.0 lb, Temperature 527 °F |
ISO 1133 |
Gromax BFG30-AH00B2 Nylon 6 30% Glass Filled (Dry) Information provided by Gromax Enterprises Corp. |
|||
Melt Flow | 60 - 100 g/10 min @Load 2.16 kg, Temperature 170 °C |
60 - 100 g/10 min @Load 4.76 lb, Temperature 338 °F |
ISO 1133 |
Lubrizol Advanced Materials PEARLBOND® 503 Linear Thermoplastic Polyurethane Pearlbond™ 503 is a linear, polycaprolactone-copolyester polyurethane, supplied in form of white spherical granules with a high crystallization rate and a very high thermoplasticity level.Appli.. |
|||
Melt Flow | 60 g/10 min @Load 10.0 kg, Temperature 250 °C |
60 g/10 min @Load 22.0 lb, Temperature 482 °F |
ASTM D1238 |
Samsung Cheil Industries Infino® HR-1008B PC/ABS, Unreinforced PC/ABS material that can be used for hand phone and car phoneInformation provided by Samsung Cheil Industries. |
|||
Melt Flow | 60 g/10 min @Load 1.20 kg, Temperature 300 °C |
60 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
Samsung Cheil Industries Infino® TK-2046H PCT, Glass Filled Information provided by Samsung Cheil Industries. |
|||
Melt Flow | 60 g/10 min @Load 10.0 kg, Temperature 250 °C |
60 g/10 min @Load 22.0 lb, Temperature 482 °F |
ASTM D1238 |
Samsung Cheil Industries Infino® TN-1200 PC, Unreinforced FR Information provided by Samsung Cheil Industries. |
|||
Melt Flow | 60 g/10 min @Load 10.0 kg, Temperature 250 °C |
60 g/10 min @Load 22.0 lb, Temperature 482 °F |
ASTM D1238 |
Samsung Cheil Industries Infino® HR-1008B PC/ABS, Unreinforced PC/ABS material that can be used for hand phone and car phoneInformation provided by Samsung Cheil Industries. |
|||
Melt Flow | 60 g/10 min @Load 2.16 kg, Temperature 235 °C |
60 g/10 min @Load 4.76 lb, Temperature 455 °F |
ASTM D1238 |
Samyang Tribit® 1501N PBT, Flame Retardancy Crystallization is fast, formability is excellent and thermal resistance, chemical resistance, electrical properties and abrasion resistance are excellent.1501N is a V-2 flame retardancy grade.Appli.. |
|||
Melt Flow | 60 g/10 min @Load 5.00 kg, Temperature 266 °C |
60 g/10 min @Load 11.0 lb, Temperature 511 °F |
ASTM D1238 |
SABIC Innovative Plastics Valox® 4512 PBT+PC (Europe-Africa-Middle East) 10% GF FR PBT/PC Blend |
|||
Melt Flow | 60 g/10 min @Load 2.16 kg, Temperature 230 °C |
60 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
Borealis BJ360MO Polypropylene Copolymer BJ360MO is a heterophasic copolymer. This grade provides unique combination of very high melt flow rate, high impact strength and stiffness. and is designed for high-speed injection molding and cont.. |
|||
Melt Flow | 60 g/10 min | 60 g/10 min | ASTM D1238L |
Total PPH 3925WZ Polypropylene, Injection Molding Grade Easy flow injection molding homopolymerNucleation - FINA 3925WZ is nucleated to provide fast cycle time and improve contact clarity.Antistat - FINA 3925WZ contains an antistat that will help protect.. |
|||
Melt Flow | 60 g/10 min @Load 2.16 kg, Temperature 230 °C |
60 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
Total PPR 12222 Random Copolymer Polypropylene Total Petrochemicals PPR 12222 is a high melt flow index, clarified random copolymer. Its high transparency makes it particularly suitable for the production of household articles and packaging. It.. |
|||
Melt Flow | 60 g/10 min | 60 g/10 min | ASTM D1238 |
ExxonMobil Escorene™ UL 05540EH2 Ethylene Vinyl Acetate Copolymer (European Grade) Product Description: UL 05540EH2 is a copolymer of ethylene and vinyl acetate.Availability: Africa & Middle East, Asia Pacific and Europe Additive: Antiblock: NoSlip: No Thermal Stabilizer: Yes Fre.. |
|||
Melt Flow | 60 g/10 min @Load 2.16 kg |
60 g/10 min @Load 4.76 lb |
Melt flow ratio I10/I2 is 8.5. |
Dow DOWLEX™ IP-60 High Density Polyethylene DOWLEX® IP-60 resin is an improved processing high density polyethylene resin designed to offer excellent processability, good impact and top load strength required in thin wall injection molding. .. |
|||
Melt Flow | 60 g/10 min @Load 2.16 kg, Temperature 230 °C |
60 g/10 min @Load 4.76 lb, Temperature 446 °F |
|
Clariant Renol CPPR02096 Color concentrate of Titanium Oxide Application to PolypropyleneData provided by Clariant Masterbatches |
|||
Melt Flow | 60 g/10 min @Load 5.00 kg, Temperature 275 °C |
60 g/10 min @Load 11.0 lb, Temperature 527 °F |
ISO 1133 |
Azoty Tarnow™ Tarnamid® T-27 CF10 Polyamide 6 10% Carbon Fiber - Antistatic and Electroconductive Medium viscosity injection molding grade, also used for compounding, for production of monofilament, bristles and fibers.Electroconductive grade based on carbon fiber reinforcement, very high stiffn.. |
|||
Melt Flow | 60 g/10 min @Load 5.00 kg, Temperature 275 °C |
60 g/10 min @Load 11.0 lb, Temperature 527 °F |
ISO 1133 |
Azoty Tarnow™ Tarnamid® T-27 GF15 MW25 Polyamide 6 - Mineral Reinforced 15% Glass fiber reinforced and 25% Mineral filled, medium viscosity injection molding grade, also used for compounding, for production of monofilament, bristles and fibers.Tarnamid® has the followi.. |
|||
Melt Flow | 60 g/10 min @Load 5.00 kg, Temperature 275 °C |
60 g/10 min @Load 11.0 lb, Temperature 527 °F |
ISO 1133 |
Azoty Tarnow™ Tarnamid® T-27 TF10 Polyamide 6 - Improved Slip Properties Medium viscosity injection molding grade, also used for compounding, for production of monofilament, bristles and fibers.Low wear and low friction grade, contains molybdenum disulfide, PTFE.Tarnamid.. |
|||
Melt Flow | 60 g/10 min @Load 5.00 kg, Temperature 275 °C |
60 g/10 min @Load 11.0 lb, Temperature 527 °F |
ISO 1133 |
Azoty Tarnow™ Tarnamid® T-27 GF15 Polyamide 6 - Glass Fiber Reinforced 15% Glass fiber reinforced, medium viscosity injection molding grade, also used for compounding, for production of monofilament, bristles and fibers.Tarnamid® has the following main properties:High.. |
|||
Melt Flow | 60 g/10 min | 60 g/10 min | ASTM D1238 |
Huntsman PE2072 Injection Molding Polyethylene
(discontinued **) Homopolymer and FDA compliant.Features: Very high flow rapid set-up characteristics, excellent clarity, gloss, and stiffness.Applications: Injection molding: lids and difficult to fill applications... |
|||
Melt Flow | 60 - 100 g/10 min @Load 2.16 kg, Temperature 170 °C |
60 - 100 g/10 min @Load 4.76 lb, Temperature 338 °F |
DDIN 53.735 |
Lubrizol Advanced Materials Pearlbond® D183 Thermoplastic Polyurethane
(discontinued **) The Pearlbond® grades are aromatic crystalline TPUs used for the production of heat activated shoe counters and toe puffs, and orthopedic products. The Pearlbond® grades are supplied in pellet fo.. |
|||
Melt Flow | 60 - 100 g/10 min @Load 2.16 kg, Temperature 170 °C |
60 - 100 g/10 min @Load 4.76 lb, Temperature 338 °F |
ISO 1133 |
Lubrizol Advanced Materials PEARLBOND® 103 Linear Thermoplastic Polyurethane Pearlbond™ 103 is a linear, polycaprolactone-based polyurethane, supplied in form of small white granules, which combines a very high crystallization rate with a very high thermoplasticity level. I.. |
|||
Melt Flow | 60 g/10 min @Load 5.00 kg, Temperature 270 °C |
60 g/10 min @Load 11.0 lb, Temperature 518 °F |
Estimated using room temperature density; ISO 1133 |
Lanxess Pocan® A 3131 000000 PBT+ASA, 30% glass fibers PBT+ASA, 30% glass fibers, injection molding, low tendency to warp, improved surface finish |
|||
Melt Flow | 60 g/10 min @Load 2.16 kg, Temperature 300 °C |
60 g/10 min @Load 4.76 lb, Temperature 572 °F |
ASTM D570 |
LG Chemical LUCON CP6067 PC+CNT+CF Description: Injection Molding, PC+CNT+CF, Electrostatic Dissipation, High Strength, High Flow & Good ProcessabilityApplication: Wafer Carrier Box, Conveyor belt bearing blockCAS No. 103598-77-2, 74.. |