Physical Properties | Metric | English | Comments |
---|---|---|---|
Melt Flow | 5.8 g/10 min @Load 3.80 kg, Temperature 230 °C |
5.8 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D-1238 |
Plaskolite Optix® CP - 61 General Purpose Acrylic Resin OPTIX® general purpose acrylics are available in a variety of performance grades that offer varying melt flow rates, heat resistance, color/opacity and gloss levels.Information provided by Plaskoli.. |
|||
Melt Flow | 5.8 g/10 min @Load 3.80 kg, Temperature 230 °C |
5.8 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D-1238 |
Plaskolite West Optix® CP - 61 General Purpose Acrylic Resin Generally unaffected by alkalis, hydrocarbons, non-oxidizing acids, and salt water. Transparent, translucent, opaque, and custom colors in various grades of melt flow rate and heat resistance are av.. |
|||
Melt Flow | 5.8 g/10 min @Load 3.80 kg, Temperature 230 °C |
5.8 g/10 min @Load 8.38 lb, Temperature 446 °F |
|
Polycasa Acryl® G 77 Acrylic, Injection Molding Grade Injection molding grade for record player covers, optical fibers, display windows, logos, condiment containers, desk organizers.Data was collected by ISO methods.Quinn Manufacturing Group rebranded .. |
|||
Melt Flow | 5.8 g/10 min | 5.8 g/10 min | Condition E; ASTM D 1238 |
Chevron Phillips HiD® 9605D HDPE Cast Film Resin
(discontinued **) Characteristics: Very Low Gel Levels, Produces Very "Clear" Film, Draws to Thin Gauges, Low Taste and Odor Transfer, Excellent MVTR for a Chill Cast Film, Excellent Processability, Excellent Optical.. |
|||
Melt Flow | 5.8 g/10 min | 5.8 g/10 min | ISO 1133 |
Lucite International Diakon® Frost 902 70 Acrylic Polymer Information provided by Lucite International |
|||
Melt Flow | 5.8 g/10 min | 5.8 g/10 min | ASTM D1238 |
Lucky CG-920 Acrylic May be UV stabilized. General Lucky PMMA qualities: Transparent/elegant appearance, high heat and weather resistance, excellent chemical resistance and coloring capability. |
|||
Melt Flow | 5.8 g/10 min | 5.8 g/10 min | ASTM D1238 |
Lucky IG-840 Acrylic, Injection Grade General purpose injection molding grade. May be UV stabilized. General Lucky PMMA qualities: Transparent/elegant appearance, high heat and weather resistance, excellent chemical resistance and col.. |
|||
Melt Flow | 5.8 g/10 min @Load 2.16 kg, Temperature 230 °C |
5.8 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
Multibase Multi-Flex® D 5308 Platinum TPO Thermoplastic Polyolefin Elastomer Forms: PelletsInformation provided by Multibase |
|||
Melt Flow | 5.8 g/10 min @Load 5.00 kg, Temperature 200 °C |
5.8 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
LG Chemical 20HRE GPPS High strength, Superior transparency and processability, good appearance, non-toxicity (Conforming to FDA CFR 177.1640), Excellent electrical properties, Heat resistance and chemical resistance, Sup.. |
|||
Melt Flow | 5.8 g/10 min @Load 5.00 kg, Temperature 280 °C |
5.8 g/10 min @Load 11.0 lb, Temperature 536 °F |
ASTM D1238 |
SABIC Innovative Plastics NORYL NH7114 PPE+HIPS Noryl* NH7114 resin is a 20% glass reinforced, modified PPE-PS blend. The material uses non-halogenated flame retardants to achieve UL94 flame ratings while offering an exceptional balance of streng.. |
|||
Melt Flow | 5.8 g/10 min @Load 5.00 kg, Temperature 280 °C |
5.8 g/10 min @Load 11.0 lb, Temperature 536 °F |
ASTM D1238 |
SABIC Innovative Plastics NORYL NH7114 PPE+HIPS (Asia Pacific) Noryl* NH7114 resin is a 20% glass reinforced, modified PPE-PS blend. The material uses non-halogenated flame retardants to achieve UL94 flame ratings while offering an exceptional balance of streng.. |
|||
Melt Flow | 5.8 g/10 min @Load 5.00 kg, Temperature 280 °C |
5.8 g/10 min @Load 11.0 lb, Temperature 536 °F |
ASTM D1238 |
SABIC Innovative Plastics NORYL NH7114 PPE+HIPS (Europe-Africa-Middle East) Noryl* NH7114 resin is a 20% glass reinforced, modified PPE-PS blend. The material uses non-halogenated flame retardants to achieve UL94 flame ratings while offering an exceptional balance of streng.. |
|||
Melt Flow | 5.8 - 20 g/10 min | 5.8 - 20 g/10 min | |
Tempia Polylactic acid (PLA) Resin A bio-degradable plastic, Polylactic acid (PLA) is made from corn. Products produced are compostable within 45 – 120 days. The degradation process of the item is temperature, humidity and thicknes.. |
|||
Melt Flow | 5.8 g/10 min @Load 3.80 kg, Temperature 230 °C |
5.8 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D-1238-94a |
Multibase Multi-ABS 3525 Black Moisture content is 0.08%.Data provided by Multibase. |
|||
Melt Flow | 5.8 g/10 min | 5.8 g/10 min | ISO 1133 |
Lucite International Diakon® Frost 902 80 Acrylic Polymer Information provided by Lucite International |