- Polymer Property : Melt Flow = 2.8 g/10 min
Polymer Property : Melt Flow = 2.8 g/10 min Product List
Physical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Flow | 2.8 g/10 min | 2.8 g/10 min | (Condition L) ASTM D-1238-94a |
| Multibase Multi-Flex® TPO DEFA 1047 The burn rate is 0.53 in/min; ASTM FM VSS 302.Data provided by Multibase. |
|||
| Melt Flow | 2.8 g/10 min @Load 3.80 kg, Temperature 230 °C |
2.8 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D-1238 |
| Plaskolite Optix® CA - 1000 I High Impact Grade Acrylic Resin OPTIX® impact-modified grades offer 7 to 10 times the impact resistance of general purpose polymers while maintaining optical clarity.Information provided by Plaskolite, Inc. |
|||
| Melt Flow | 2.8 g/10 min @Load 3.80 kg, Temperature 230 °C |
2.8 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D-1238 |
| Plaskolite West Optix® CA - 1000 I High Impact Acrylic Resin Optix® impact-modified grades exhibit 7 to 10 times the impact strength of general purpose grades and maintaining the superior optical properties. Each grade is offered in a grade(G) that resists g.. |
|||
| Melt Flow | 2.8 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.8 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| SABIC 318B Linear Low Density Polyethylene for Cast Film Product Description: 318B is a Linear Low Density Polyethylene grade designed to provide easy processability and specially formulated for optimum thermal stability at high processing temperatures u.. |
|||
| Melt Flow | 2.8 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.8 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Yparex 8403 S Polyolefin Adhesive Resin The Yparex range provides outstanding adhesion for all forms of polyethylene including cross-linked PE to: barrier plastics like EVOH and Polyamidemetals like aluminum, steel and copper.Yparex offer.. |
|||
| Melt Flow | 2.8 g/10 min | 2.8 g/10 min | Exxon Method |
| ExxonMobil Escorene® LD-400 LDPE Medium/High Voltage Insulation
(discontinued **) Data provided by the manufacturer, Exxon Chemical.A crosslinkable polyethylene homopolymer resin designed for electrical applications.Applications: Base resin for medium voltage power cable insulati.. |
|||
| Melt Flow | 2.8 g/10 min @Load 1.20 kg, Temperature 300 °C |
2.8 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| SABIC Innovative Plastics Lexan® ML4249 PC Polycarbonate for aircraft applications requiring FAR 25.853a compliance. Transparent, transluscent and opaque colors. For blow molding. |
|||
| Melt Flow | 2.8 g/10 min @Load 3.80 kg, Temperature 230 °C |
2.8 g/10 min @Load 8.38 lb, Temperature 446 °F |
|
| Arkema Group Oroglas® MI-4T Acrylic, Heat Resistant
(discontinued **) OROGLAS MI-4T is an acrylic grade that associates improved impact resistance with high heat resistance.Key features improved impact resistance: up to 4 times more impact resistant than standard acr.. |
|||
| Melt Flow | 2.8 - 4.6 g/10 min @Load 21.6 kg, Temperature 230 °C |
2.8 - 4.6 g/10 min @Load 47.6 lb, Temperature 446 °F |
ASTM D1238 |
| Solvay Specialty Polymers Solef® 1015 Polyvinylidene Fluoride (PVDF)
(Unverified Data**) Solef® 1015 PVDF homopolymer has very high viscosity, suitable for membrane manufacturing. It is available exclusively as powder.Information provided by Solvay Specialty Polymers. |
|||
| Melt Flow | 2.8 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.8 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| DuPont™ Surlyn® 1605SBR Sodium Ionomer Resin for Extrusion Coating
(discontinued **) Surlyn® 1605SBR is an ionomer resin available for use in conventional extrusion coating and coextrusion coating equipment designed to process polyethylene resins. Applications: Medical/pharmaceuti.. |
|||
| Melt Flow | 2.8 g/10 min | 2.8 g/10 min | ASTM D1238 |
| LyondellBasell Alathon® M6028 High Density Polyethylene ApplicationsM 6028 is a homopolymer that is warp resistant, exhibits excellent toughness, stiffness and color as well as low odor and good processing stability. Typical applications include safety .. |
|||
| Melt Flow | 2.8 g/10 min @Load 5.00 kg, Temperature 200 °C |
2.8 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| IRPC Polimaxx Polene 121PC Styrene Acrylonitrile APPLICATIONS: INJECTION MOLDING, HOUSEHOLD PRODUCTS : SANITARY WARE, AUTOPART APPLICATION : LAMP ELECTRICAL APPLIANCES : ELECTRICAL FAN |
|||
| Melt Flow | 2.8 g/10 min @Load 5.00 kg, Temperature 200 °C |
2.8 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| IRPC Polimaxx Polene 320PC Styrene Acrylonitrile APPLICATIONS: INJECTION MOLDING, HOUSEHOLD PRODUCTS : SANITARY WARE, AUTOPART APPLICATION : LAMP ELECTRICAL APPLIANCES : ELECTRICAL FAN |
|||
| Melt Flow | 2.8 g/10 min @Load 2.16 kg, Temperature 230 °C |
2.8 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Multibase Multi-Flex® A 9402 AH Black TPE Thermoplastic Elastomer Forms: PelletsProcessing Methods:Injection Molding Information provided by Multibase |
|||
| Melt Flow | 2.8 g/10 min @Load 2.16 kg, Temperature 230 °C |
2.8 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Multibase Multi-Flex® RP 6568 B2 Black TPE Thermoplastic Elastomer Forms: PelletsProcessing Methods:Injection Molding Information provided by Multibase |
|||
| Melt Flow | 2.8 g/10 min @Load 5.00 kg, Temperature 200 °C |
2.8 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| LG Chemical 25SPE GPPS Heat resistance, Chemical resistance, Superior transparency and processability, good appearance, non-toxicity (Conforming to FDA CFR 177.1640), Excellent electrical properties, Superior extrusion pr.. |
|||
| Melt Flow | 2.8 g/10 min | 2.8 g/10 min | ISO 1133 |
| Solvay Specialty Polymers Polidan® S/I 20 Polyethylene, Crosslinked (XLPE) POLIDAN® S/I 20 is a silane crosslinkable PE compound which is used together with a catalyst masterbatch to accelerate the crosslinking reaction. It is used for injection molding.Features: Crossl.. |
|||
| Melt Flow | 2.8 g/10 min | 2.8 g/10 min | |
| UBE B (Low-Cis) HIPS (n-DM = 0.03 wt % and PH-3H = 0.03 wt %) Description: UBE high impact polystyrene (HIPS).Information provided by UBE. |
|||
| Melt Flow | 2.8 g/10 min | 2.8 g/10 min | |
| UBE C (Low-Cis) HIPS (n-DM = 0.03 wt % and PH-3H = 0.03 wt %) Description: UBE high impact polystyrene (HIPS).Information provided by UBE. |
|||
| Melt Flow | 2.8 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.8 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Polyram RamTal PMH2003 Polyacetal Homopolymer for Injection Molding General purpose polyacetal homopolymer for injection molding applications, MFI 3.Information provided by Polyram. |
|||
| Melt Flow | 2.8 g/10 min @Load 5.00 kg, Temperature 200 °C |
2.8 g/10 min @Load 11.0 lb, Temperature 392 °F |
ISO 1133 H |
| Total Polystyrene Impact 8260 Improved Environmental Stress Crack Resistance High Impact Polystyrene POLYSTYRENE IMPACT 8260 is a high impact polystyrene for extrusion and injection applications. This grade has an improved environmental stress crack resistance in comparison with standard high impa.. |
|||
| Melt Flow | 2.8 g/10 min | 2.8 g/10 min | ASTM D1238L |
| Total PPH 3371 Polypropylene, Oriented Film Extrusion Grade Homopolymer film gradeLow Residuals - Fina 3371 utilizes the new Fina proprietary process technology to provide extremely low residuals for improved color stability and clarity.Slip/Antiblock - Fina.. |
|||
| Melt Flow | 2.8 g/10 min | 2.8 g/10 min | ISO 1133 D |
| Asahi Kasei Tenac®-C 3510 Copolymer Acetal Resin High-impact, high elongation grade, with increased molecular weightInformation provided by Asahi Kasei Corporation. |
|||
| Melt Flow | 2.8 g/10 min @Load 5.00 kg, Temperature 200 °C |
2.8 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| Americas Styrenics STYRON® 484 High Impact Polystyrene Product CharacteristicsToughnessHeat resistanceGood stiffnessFood Contact CompliantUL Classification 94HBTypical ApplicationsLidsAppliances/RefrigerationPackaging/disposablesHousewaresInformation pr.. |
|||
| Melt Flow | 2.8 g/10 min @Load 5.00 kg, Temperature 230 °C |
2.8 g/10 min @Load 11.0 lb, Temperature 446 °F |
|
| Arkema Group Kynar® FLEX 2822 PVDF
(discontinued **) Designation ISO 12086-VDF/HFP-K, EDN, N. ?E5.C.H.B.C,, ? (4-8)Kynar FLEX PVDF are fluorinated thermoplastic copolymers.Outstanding characteristics of Kynar FLEX: chemical resistance, imperviousness .. |
|||
| Melt Flow | 2.8 g/10 min | 2.8 g/10 min | |
| UBE UBEPOL BR15HB HIPS (n-DM = 0.03 wt % and PH-3H = 0.03 wt %) Description: UBEPOL-BR15HB is characterized by the highest branching of these 3 grades and is adapted by many PS manufacturers.Information provided by UBE. |
|||
| Melt Flow | 2.8 g/10 min @Load 3.80 kg, Temperature 230 °C |
2.8 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D-1238 |
| Plaskolite West Optix® CP - 1000 I High Impact Acrylic Resin Optix® impact-modified grades exhibit 7 to 10 times the impact strength of general purpose grades and maintaining the superior optical properties. Each grade is offered in a grade(G) that resists g.. |
|||
| Melt Flow | 2.8 g/10 min | 2.8 g/10 min | melt index; ASTM D1238 |
| Asahi Kasei Tenac®-C EX351 Acetal Copolymer, Extrusion Grade
(discontinued **) High-viscosity grade amenable to extrusion.Applications: Extruded rods and sheets.This product is not a part of the standard product line dated 2003. |
|||
| Melt Flow | 2.8 g/10 min @Load 2.16 kg, Temperature 230 °C |
2.8 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| ExxonMobil PP6262 Polypropylene Homopolymer Product Description: A clarified homopolymer resin designed for production of extruded sheet and thermoformed containers. It exhibits excellent processing characteristics even in deep drawn applica.. |
|||