Polymer Property : Melt Flow = 1.8 g/10 min Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Physical Properties	Metric	English	Comments
Melt Flow	1.8 g/10 min	1.8 g/10 min	(Condition L) ASTM D-1238
Multibase Multi-Flex® TPE A 8802 BLK Multi-Flex TPE contains Kraton™ G.Data provided by Multibase.
Melt Flow	1.8 g/10 min @Load 2.16 kg, Temperature 230 °C	1.8 g/10 min @Load 4.76 lb, Temperature 446 °F	Procedure A; ASTM D1238
PolyOne Maxxam™ MAXBATCH YM-618.G001-1000 Polypropylene, Unspecified (PP, Unspecified) PolyOne's Maxxam™ family of polypropylene- and polyethylene-based products covers a wide range of applications, markets and performance requirements. Standard grades are compounded with calcium car..
Melt Flow	1.8 g/10 min @Load 2.16 kg, Temperature 190 °C	1.8 g/10 min @Load 4.76 lb, Temperature 374 °F	Procedure A; ASTM D1238
PolyOne Syncure™ S1006B Polyethylene, Crosslinked (XLPE) Available as Catalyst Masterbatch component for PolyOne Syncure System.Oven Aging values are >75, and were measured on a 95 phr S1025A / 5 phr S1006B Syncure System. Pellet appearance is 1/8 cylindr..
Melt Flow	1.8 g/10 min @Load 5.00 kg, Temperature 230 °C	1.8 g/10 min @Load 11.0 lb, Temperature 446 °F
Polimeri Europa Dutral® PM 06 PLE Ethylene - Propylene Masterbatch Dutral® PM 06 PLE is a masterbatch based on Ethylene - Propylene elastomer produced by suspension polymerization using a Ziegler-Natta Catalyst. A non-staining antioxidant is added during the prod..
Melt Flow	1.8 g/10 min @Load 2.16 kg, Temperature 230 °C	1.8 g/10 min @Load 4.76 lb, Temperature 446 °F	Procedure A Condition L; ASTM D1238
Network Polymers NPP 25-0216 Description: Copolymer PolypropyleneInformation provided by Network Polymers Inc.
Melt Flow	1.8 g/10 min @Load 5.00 kg, Temperature 200 °C	1.8 g/10 min @Load 11.0 lb, Temperature 392 °F	Procedure A Condition G; ASTM D1238
Network Polymers NPP 808 C5WW Description: Polycarbonate AlloyInformation provided by Network Polymers Inc.
Melt Flow	1.8 g/10 min @Load 2.16 kg, Temperature 230 °C	1.8 g/10 min @Load 4.76 lb, Temperature 446 °F	Condition L; ASTM D1238
PolyMirae Moplen EP340G Sheet and Thermoforming Grade Polypropylene Moplen RP340G is the polypropylene random copolymer polymer manufactured by PMC under the license of BASELL using the Spheripol process. Moplen RP340G is a random copolymer particularly suitable for..
Melt Flow	1.8 g/10 min @Load 2.16 kg, Temperature 230 °C	1.8 g/10 min @Load 4.76 lb, Temperature 446 °F	Condition L; ASTM D1238
PolyMirae Moplen RP370G Blow Molding Grade Polypropylene Moplen RP370G is the polypropylene copolymer manufactured by PMC under the license of BASELL using the Spheripol process. Moplen RP370G is a copolymer particularly suitable for blow molding applicat..
Melt Flow	1.8 g/10 min @Load 2.16 kg, Temperature 190 °C	1.8 g/10 min @Load 4.76 lb, Temperature 374 °F	Procedure A; ASTM D1238
PolyOne Syncure™ S1017B Polyethylene, Crosslinked (XLPE) Available as Catalyst Masterbatch component for PolyOne Syncure System.Oven Aging values are >75, and were measured on a 98.5 phr S1025A / 1.5 phr S1017B Syncure System. Torque is >1500. Pellet appe..
Melt Flow	1.8 g/10 min @Load 2.16 kg, Temperature 230 °C	1.8 g/10 min @Load 4.76 lb, Temperature 446 °F	ISO 1133
NOVA Chemicals DYLARK® 238 Impact Grade Engineering Resin Features:High heat resistance Good chemical resistance High impact strength Excellent flow characteristicsApplications:Automotive interior trim applications Automotive consoles Structural HousingsIn..
Melt Flow	1.8 g/10 min @Load 2.16 kg, Temperature 190 °C	1.8 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238
NOVA Chemicals Sclair® 94E Butene LMDPE Film and Extrusion Resin Features: Excellent processabilityGood stiffness and strengthHigh stretchability Applications: Overwrap filmNettingBlend resinInformation provided by Nova Chemicals
Melt Flow	1.8 g/10 min	1.8 g/10 min	ASTM D1238
LyondellBasell PetrotheneÂ® NA345009 Low Density Polyethylene (Blow Molding) ApplicationsPETROTHENE NA 345-009 is a low density homopolymer resin designed for blow molding applications. Excellent clarity combined with strength and high stiffness makes NA 345-009 an ideal ch..
Melt Flow	1.8 g/10 min	1.8 g/10 min	ASTM D1238
LyondellBasell PetrotheneÂ® NA345013 Low Density Polyethylene (Film Extrusion) ApplicationsPETROTHENE NA 345 is a series of homopolymer resins combining premium clarity with strength and stiffness. In addition, NA 345 exhibits good impact strength on both flat and creased fil..
Melt Flow	1.8 g/10 min	1.8 g/10 min	ASTM D1238
LyondellBasell PetrotheneÂ® NA345196 Low Density Polyethylene (Film Extrusion) ApplicationsPETROTHENE NA 345 is a series of homopolymer resins combining premium clarity with strength and stiffness. In addition, NA 345 exhibits good impact strength on both flat and creased fil..
Melt Flow	1.8 g/10 min	1.8 g/10 min	ASTM D1238
Hyosung Topilene F300 PP F300 Film Grade HomopolymerApplications: OPPCharacteristics:ProcessabilityTransparencyInformation provided by Hyosung Corporation
Melt Flow	1.8 g/10 min	1.8 g/10 min	ISO 1133
Lucite International DiakonÂ® TD735 Toughened Acrylic Compound The DiakonÂ® impact PMMA series offer the best combination of impact, chemical and heat resistance and provide rigidity and surface hardness.The grades in the DiakonÂ® series can be processed by..
Melt Flow	1.8 g/10 min @Load 2.16 kg, Temperature 190 Â°C	1.8 g/10 min @Load 4.76 lb, Temperature 374 Â°F	ISO 1133
Lucobit LucofinÂ® 1494H Chemically Modified Polyethylene LucofinÂ® 1492 is a chemically modified polyethylene, i.e. EBA grafted with maleic anhydride (MA). LucofinÂ® 1492 can be used pure or as a component in mixtures applications where improved polar..
Melt Flow	1.8 g/10 min	1.8 g/10 min	ISO 1133
Iran Petrochemical (PCC) S 30 G Polypropylene The grade has combined excellent process ability with high stiffness.Applications: bags, mats, packing twines and ropes, drinking beakers packaging for dairy products.Information provided by Iran Pe..
Melt Flow	1.8 g/10 min @Load 5.00 kg, Temperature 200 Â°C	1.8 g/10 min @Load 11.0 lb, Temperature 392 Â°F	Condition G; ASTM D1238
Spartech Royalite R59M Hi-Impact ABS/PVC Resin Data provided by the manufacturer. A unique ABS/PVC resin that meets the flammability standards of many industries and is a cost-effective alternative to standard fire-rated ABS. High rigidity in t..
Melt Flow	1.8 g/10 min @Load 2.16 kg, Temperature 190 Â°C	1.8 g/10 min @Load 4.76 lb, Temperature 374 Â°F
Silon Tabond 3045 Adhesive Resin TABOND 3045 is LLDPE modified with maleic anhydride functional groups which promote bonding with different materials like polar polymers, metals and surface treated glass.Characteristics: â€¢ Str..
Melt Flow	1.8 g/10 min	1.8 g/10 min	ASTM D1238
A. Schulman PP 1116-01 Polypropylene Molding Grade Copolymer Polypropylene DescriptionPolypropylene PP 1116-01 is a molding grade copolymer polypropylene with improved low temperature toughness and good room temperature toughness. Information provided by A. Schulman.
Melt Flow	1.8 g/10 min @Load 2.16 kg, Temperature 190 °C	1.8 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238 - ISO 1133
DuPont Elvaloy® 3217 AC Ethylene and 17% Butyl Acrylate Copolymer Elvaloy® 3217 AC contains antioxidant, slip and antiblock additives.Elvaloy® 3217 AC has been developed for film applications requiring a combination of softness, toughness and low friction. Typi..
Melt Flow	1.8 g/10 min @Load 2.16 kg, Temperature 230 °C	1.8 g/10 min @Load 4.76 lb, Temperature 446 °F	ISO 1133
Total PPM R021 Polypropylene, Random Copolymer for Medical Grade Polypropylene PPM R021 is a random copolymer polypropylene with a Melt Flow Index of 1.8 g/10 min specially developed for the extrusion blow molding of medical containers and medical devices, to the..
Melt Flow	1.8 g/10 min @Load 2.16 kg, Temperature 230 °C	1.8 g/10 min @Load 4.76 lb, Temperature 446 °F	ISO 1133
Total PPR 3221 Random Copolymer Polypropylene, Blow Molding and Sheet Extrusion Polypropylene PPR 3221 is a high clarity, high impact resistance random copolymer especially designed for blow molding applications (mono and multi-layers) for food and non-food packaging of sauces,..
Melt Flow	1.8 g/10 min	1.8 g/10 min	ASTM D1238L
Total PPR 3230XZ Polypropylene, Blow Molding Grade Homopolymer Blow Molding GradeLubricated – FINA 3230XZ offers superior core road release, eliminating the need for additional lubricant.Antistat – FINA 3230XZ contains antistat to minimize dust ac..
Melt Flow	1.8 g/10 min	1.8 g/10 min	ASTM D1238
ExxonMobil Polybilt™ Bitumen Modifier 106 Low Density Polyethylene Resin Polybilt 106 is compatible with a large variety of bitumens. For optimum results are preliminary study is recommended to determine the base bitumen grade and optimum Polybilt 106 content to achieve ..
Melt Flow	1.8 g/10 min @Load 2.16 kg, Temperature 235 °C	1.8 g/10 min @Load 4.76 lb, Temperature 455 °F
Arkema Group Rilsan® BZM 30 TL Nylon 11, 30% Glass Fiber Filled (Dry) Designation ISO 1874-PA11,MHL,18-050,GF30Rigid grade with glass fiber (30%) filler for injection molding. Available colors: black and natural. Light and heat stabilized.Rigidity. High compressive st..
Melt Flow	1.8 g/10 min @Load 2.16 kg, Temperature 235 °C	1.8 g/10 min @Load 4.76 lb, Temperature 455 °F
Arkema Group Rilsan® BZM 30 TL Nylon 11, 30% Glass Fiber Filled (Conditioned) Designation ISO 1874-PA11,MHL,18-050,GF30Rigid grade with glass fiber (30%) filler for injection molding. Available colors: black and natural. Light and heat stabilized.Rigidity. High compressive st..
Melt Flow	1.8 g/10 min @Load 5.00 kg, Temperature 200 °C	1.8 g/10 min @Load 11.0 lb, Temperature 392 °F	ASTM D1238
Samsung Cheil Industries Starex® HF-5661H ASA, Unreinforced (discontinued **) Amorphous Styrene Acrylonitrile (SAN)Characteristics: High Flow: Impact, Heat and Chemical Resistance and Surface GlossApplications: Pens, TV Components, Refrigerator and Appliance ComponentsProcess..