Polymer Property : Melt Flow = 0.60 g/10 min Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Physical Properties	Metric	English	Comments
Melt Flow	0.60 g/10 min	0.60 g/10 min	(Condition L) ASTM D-1238
Multibase Multi-Flex® TPE A 8000 BLK Multi-Flex TPE contains Kraton™ G.Data provided by Multibase.
Melt Flow	0.60 g/10 min @Load 2.16 kg, Temperature 190 °C	0.60 g/10 min @Load 4.76 lb, Temperature 374 °F	ISO 1133
Polimeri Europa Riblene® FF 29 Low Density Polyethylene - Blown Film Extrusion Riblene FF 29 is a high molecular weight low density polyethylene (LDPE), suitable for blown film extrusion. Riblene FF 29 is characterized by a good melt strength leading to a good bubble stabilit..
Melt Flow	0.60 g/10 min @Load 3.80 kg, Temperature 200 °C	0.60 g/10 min @Load 8.38 lb, Temperature 392 °F	ASTM D 1238
SABIC Innovative Plastics Geloy FXTW30PE ASA Pearlescent GELOY ASA resin with copper-look for capstock extrusion. Outstanding weatherability.This data was supplied by SABIC-IP for the Americas region.
Melt Flow	0.60 g/10 min @Load 2.16 kg, Temperature 230 °C	0.60 g/10 min @Load 4.76 lb, Temperature 446 °F	Condition L; ASTM D1238
NOVA Chemicals Dylark® 238P20 High Performance Glass Filled Styrenic Very high modulus, High heat resistance, Excellent flow characteristics, Excellent adhesion to urethaneApplications: Instrument panel substrates, consoles, Cluster housing, interior trimInjection Sp..
Melt Flow	0.60 g/10 min @Load 2.16 kg	0.60 g/10 min @Load 4.76 lb	ASTM D1238
Reliance Industries Relene W43006 Polyethylene Relene W43006 is a polyethylene grade recommended for insulation in jelly filled telecommunication cables. This grade contains a special stabilization system for improved thermal resistance. It is..
Melt Flow	0.60 g/10 min @Load 2.16 kg, Temperature 190 °C	0.60 g/10 min @Load 4.76 lb, Temperature 374 °F	ISO 1133
Polimeri Europa Clearflex® FF 106 Hexene Copolymer Linear Low Density Polyethylene Clearflex FF 106 is a hexene copolymer linear low density polyethylene (C6-LLDPE), with antioxidants, suitable for blown film extrusion.Films manufactured with Clearflex FF 106 are characterized by ..
Melt Flow	0.60 g/10 min @Load 2.16 kg, Temperature 230 °C	0.60 g/10 min @Load 4.76 lb, Temperature 446 °F	ISO 1133
Solvay Engineered Polymers DEXFLEX® E756 TPO (discontinued **) Description: DEXFLEX® E756 thermoplastic olefinic elastomer (TPO) is designed for extruded automotive air-bag covers. This material provides excellent rigidity, durability and low-temperature toug..
Melt Flow	0.60 g/10 min @Load 2.16 kg, Temperature 190 °C	0.60 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238
DuPont Bynel® 4006 Anhydride-Modified HDPE Adhesive Resin (discontinued **) Bynel® Series 4000 resins are anhydride-modified, high-density polyethylene resins. They are available in pellet form for use in conventional extrusion and coextrusion equipment designed to process..
Melt Flow	0.60 g/10 min @Load 2.16 kg, Temperature 230 °C	0.60 g/10 min @Load 4.76 lb, Temperature 446 °F	ASTM D1238
NOVA Chemicals Dylark® FG2500 High-Heat Styrenic Copolymer Product Description and Features: Styrenic copolymer with high-heat resistance, high-impact strength and good toughness. Resins used in food grade sheet extrusion and injection molding application..
Melt Flow	0.60 g/10 min	0.60 g/10 min	ASTM D1238
LyondellBasell PlexarÂ® PX2246 Extrudable Tie-Layer Resin - Anhydride Modified HDPE General DescriptionPlexarÂ® tie-layers are chemically modified resins used to bond unlike materials, primarily in packaging and industrial applications. Common adherents include polyethylene resin..
Melt Flow	0.60 g/10 min @Load 2.16 kg, Temperature 230 Â°C	0.60 g/10 min @Load 4.76 lb, Temperature 446 Â°F	ASTM D1238
Ineos T00G-00 Polypropylene Impact Copolymer This is a fractional MFR polypropylene impact copolymer designed for the roofing membrane market. Its blend of impact resistance and flexural modulus is designed to provide an excellent balance bet..
Melt Flow	0.60 - 0.90 g/10 min @Load 2.16 kg, Temperature 190 Â°C	0.60 - 0.90 g/10 min @Load 4.76 lb, Temperature 374 Â°F	ASTM D1238-00
Ipiranga Petrochem LB 0117 LLDP IPQ produces Linear Low Density Polyethylene (LLDPE) for use by plastics molding industry segments that employ extrusion processes in the manufacturing of films destined for producing bobbins and ba..
Melt Flow	0.60 - 0.90 g/10 min @Load 2.16 kg, Temperature 190 Â°C	0.60 - 0.90 g/10 min @Load 4.76 lb, Temperature 374 Â°F	ASTM D1238-00
Ipiranga Petrochem LB 0120 BP LLDP IPQ produces Linear Low Density Polyethylene (LLDPE) for use by plastics molding industry segments that employ extrusion processes in the manufacturing of films destined for producing bobbins and ba..
Melt Flow	0.60 - 0.90 g/10 min @Load 2.16 kg, Temperature 190 Â°C	0.60 - 0.90 g/10 min @Load 4.76 lb, Temperature 374 Â°F	ASTM D1238-00
Ipiranga Petrochem LB 0120 BPS LLDP IPQ produces Linear Low Density Polyethylene (LLDPE) for use by plastics molding industry segments that employ extrusion processes in the manufacturing of films destined for producing bobbins and ba..
Melt Flow	0.60 g/10 min @Load 2.16 kg, Temperature 190 Â°C	0.60 g/10 min @Load 4.76 lb, Temperature 374 Â°F	ASTM D1238
Iran Petrochemical (PCC) 12XF6 Linear Low Density Polyethylene 12XF6 is a high performance LLDPE (HP-LLDPE) blown film grade for high film strength applications.Information provided by Iran Petrochemical Commercial Co.
Melt Flow	0.60 - 0.90 g/10 min @Load 5.00 kg, Temperature 230 Â°C	0.60 - 0.90 g/10 min @Load 11.0 lb, Temperature 446 Â°F	ASTM D1238
Kureha KF Polymer 1300 PVDF Homopolymer KF Polymer is a fire-resistant engineering plastic which maintains the excellent performance of a fluoropolymer. It shows well-balanced molding processability similar to general-purpose resins. KF p..
Melt Flow	0.60 g/10 min @Load 2.16 kg, Temperature 190 Â°C	0.60 g/10 min @Load 4.76 lb, Temperature 374 Â°F	ASTM D1238
Multibase Multi-Flamâ„¢ 0901 HDPE Polyethylene Features:Flame RetardantHalogen Content, Low to None Forms:PelletsProcessing Methods:Blow MoldingExtrusionCoextrusionUses:TubingFurniturePipingInformation provided by Multibase
Melt Flow	0.60 g/10 min @Load 2.16 kg, Temperature 230 Â°C	0.60 g/10 min @Load 4.76 lb, Temperature 446 Â°F	ASTM D1238
LyondellBasell Astryn SB572C Polypropylene Copolymer Key Features: fractional melt flow, medium modulus, extrusion grade polypropylene copolymer, good melt strength, good processabilityApplications: solar panelsDescription: Astryn SB572C fractional me..
Melt Flow	0.60 g/10 min @Load 2.16 kg, Temperature 230 Â°C	0.60 g/10 min @Load 4.76 lb, Temperature 446 Â°F	Condition L; ISO 1133
LyondellBasell Hifaxâ„¢ A Thermoplastic Polyolefin Elastomer Description: Hifaxâ„¢ CA 10 A is a thermoplastic polyolefin which has been developed for the extrusion and calendering of soft film and sheet. Thanks to its high rubber content "Hifax" CA 10 A fe..
Melt Flow	0.60 g/10 min @Load 2.16 kg, Temperature 190 °C	0.60 g/10 min @Load 4.76 lb, Temperature 374 °F	ISO 1133
Borealis VL4580 High Density Polyethylene VL4580 is a high density polyethylene. This grade is especially designed for monofilament production. Applications: ropes, twines, nets, straps and brushes.Information provided by Borealis AG
Melt Flow	0.60 g/10 min	0.60 g/10 min	ASTM D1238
Westlake Hifor Clear SC74580 Linear Low Density Polyethylene WESTLAKE Hifor Clear Polyethylene SC74580 polymer is a high strength and high clarity linear low density polyethylene designed for blown film extrusion that contains no slip and no antiblock. It doe..
Melt Flow	0.60 g/10 min	0.60 g/10 min	ASTM D1238
Westlake Hifor Xtreme SC74836 Linear Low Density Polyethylene WESTLAKE HIFOR Xtreme Polyethylene SC74836 is a high strength linear low density polyethylene designed for blown film extrusion. This resin contains no slip, no antiblock and processing aid. Films..
Melt Flow	0.60 g/10 min @Load 2.16 kg, Temperature 190 °C	0.60 g/10 min @Load 4.76 lb, Temperature 374 °F	ISO 1133
Fainplast Compounds Ethylplus 625 MD Polyethylene Cable Compound Polyethelene, halogen-free cable compound with superior thermo-mechanical properties, outstanding heat resistance, and high electrical propertiesBlack MDPE SheathingInformation provided by Fainplast..
Melt Flow	0.60 g/10 min @Load 2.16 kg, Temperature 190 °C	0.60 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM-D1238
Braskem TS7006 LDPE Blown Film Extrusion Polyethylene TS7006 is a low-density polyethylene (LDPE) specially developed for coextruded films and lamination. The resin presents a combination of mechanical, optical, and stiffness properties. TS7006 has a l..
Melt Flow	0.60 - 0.80 g/10 min @Load 2.16 kg, Temperature 190 °C	0.60 - 0.80 g/10 min @Load 4.76 lb, Temperature 374 °F
Breplast Bretene TS COR HF Film Light High Density Polyethylene Recovered polyethylene compositeInformation provided by Breplast S.p.A.
Melt Flow	0.60 g/10 min	0.60 g/10 min	ASTM D1238
Aclo Accucomp ABS ABS892EL High Heat Grade
Melt Flow	0.60 - 0.80 g/10 min @Load 2.16 kg, Temperature 190 °C	0.60 - 0.80 g/10 min @Load 4.76 lb, Temperature 374 °F
Breplast Bretene TS COR HF Dark High Density Polyethylene Recovered polyethylene compositeInformation provided by Breplast S.p.A.
Melt Flow	0.60 - 0.80 g/10 min @Load 2.16 kg, Temperature 190 °C	0.60 - 0.80 g/10 min @Load 4.76 lb, Temperature 374 °F
Breplast Bretene TS COR HF Film Dark High Density Polyethylene Recovered polyethylene compositeInformation provided by Breplast S.p.A.
Melt Flow	0.60 g/10 min @Load 2.16 kg, Temperature 230 °C	0.60 g/10 min @Load 4.76 lb, Temperature 446 °F	ISO 1133
Lucobit Lucopren® 1500H Soft Polyolefin Granules Lucopren is a novel, super-soft and highly elastic raw material based on polyolefins. Lucopren displays excellent flexibility and elasticity. It can be converted into products with an excellent touc..
Melt Flow	0.60 g/10 min @Load 2.16 kg, Temperature 190 °C	0.60 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238 - ISO 1133
DuPont Elvaloy® 1126 AC Ethylene and 25% Methyl Acrylate Copolymer (discontinued **) Elvaloy® 1126 AC is intended for coextrusion and molding. It can be recommended for blow molding of parts requiring permanent flexibility, stress cracking resistance and softness. Excellent fill..