Physical Properties | Metric | English | Comments |
---|---|---|---|
Melt Flow | 0.45 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.45 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D 1238 |
NOVA Chemicals Sclair® 17A Butene HDPE Film Resin 17A complies with the U.S. FDA specifications for olefin polymers and may thus be used in the United States as an article or component of an article intended for use in contact with food, without te.. |
|||
Melt Flow | 0.45 g/10 min @Load 2.16 kg, Temperature 230 °C |
0.45 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
LyondellBasell Pro-fax 7823 Polypropylene Impact Copolymer, Fractional Melt Flow Key Features: high extrudate melt strength, good cold impact resistance, good stiffness and impact balance, FDA acceptableApplications: pipe, tubing, sheet, profiles, netting, blown containers and i.. |
|||
Melt Flow | 0.45 g/10 min | 0.45 g/10 min | ASTM D1238 |
LyondellBasell Alathon® L5045 High Density Polyethylene ApplicationsALATHON L 5045 is a medium molecular weight high density polymer for use in blown film extrusion applications. Typical applications include millinery bags, coextrusions and plastic nett.. |
|||
Melt Flow | 0.45 g/10 min | 0.45 g/10 min | ASTM D1238 |
LyondellBasell Alathon® L5845 High Density Polyethylene ApplicationsALATHON L 5845 is a medium molecular weight high density homopolymer for use in blown film applications. Typical applications include paper replacement, coextrusions and laminations.Reg.. |
|||
Melt Flow | 0.45 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.45 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
Solvay Specialty Polymers Polidiemme® G/220 Thermoset Elastomer (TSE) Polidiemme® XLPO -Cross-linkable Polyolefin. Elastomer based compound crosslinkable by ambient moisture, consisting of a silane pregrafted base compound to be used with a catalyst masterbatch (S.. |
|||
Melt Flow | 0.45 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.45 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
SCG Chemicals EL-Leneâ„¢ H6240B High Density Polyethylene Blow Molding Key Characteristics:Good stiffnessGood environmental stress cracking resistance (ESCR)High compressive and impact strengthGood appearanceOdorlessSafe for food contactGood printabilityRecommended App.. |
|||
Melt Flow | 0.45 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.45 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
Total 9458 HDPE Film Grade Medium molecular weight grade. Excellent bubble stability, good compatibility with LDPE and LLDPE, good heat resistance, high stiffness and tensile strength.Applications: Release liners, Stand-up ba.. |
|||
Melt Flow | 0.45 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.45 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
Total HDPE B5845 High Density Polyethylene - Blow Molding Resin Bimodal HDPE Blow Molding ResinCharacteristics:Excellent stress cracking resistanceExcellent stiffnessApplications:Household chemicalsIndustrial chemicalsIndustrial partsFood packagingPersonal care .. |
|||
Melt Flow | 0.45 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.45 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
ExxonMobil HD 7845.30 MMW Blown Film Resin Product Description: HD 7845.30 can be processed on high stalk, pocket extrusion or cast lines. Films made from HD 7845.30 exhibit an excellent stiffness balance. High thermal stability provides exc.. |
|||
Melt Flow | 0.45 g/10 min @Load 2.16 kg, Temperature 230 °C |
0.45 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
Dow INSPIRE™ D500.00 Developmental Performance Polymer D 500.00 Developmental Performance Polymer is a performance plastic designed for cut sheet thermoforming. The propylene-based polymer offers improved formability in large part thermoforming applicat.. |
|||
Melt Flow | 0.45 g/10 min @Load 5.00 kg, Temperature 190 °C |
0.45 g/10 min @Load 11.0 lb, Temperature 374 °F |
ASTM-D1238 |
Braskem GM5010T2 HDPE High Density Extrusion Polyethylene GM5010T2 is a high-density polyethylene compound specially developed for the manufacturing of extruded pipes. It is produced with bimodal technology and has high molar mass. It shows high mechanical.. |
|||
Melt Flow | 0.45 g/10 min @Load 5.00 kg, Temperature 190 °C |
0.45 g/10 min @Load 11.0 lb, Temperature 374 °F |
ASTM-D1238 |
Braskem GM5010T2B HDPE High Density Extrusion Polyethylene GM5010T2B is a high-density polyethylene compound specially developed for the manufacturing of extruded pipes for water distribution. It is produced with bimodal technology and has high molar mass. .. |
|||
Melt Flow | 0.45 g/10 min @Load 5.00 kg, Temperature 190 °C |
0.45 g/10 min @Load 11.0 lb, Temperature 374 °F |
ASTM-D1238 |
Braskem GM7040G HDPE High Density Extrusion Polyethylene GM7040G is a high-density polyethylene compound specially developed for the manufacturing of extruded pipes for a gas pressurized line. It is produced with bimodal technology and has high molar mass.. |
|||
Melt Flow | 0.45 g/10 min @Load 5.00 kg, Temperature 190 °C |
0.45 g/10 min @Load 11.0 lb, Temperature 374 °F |
ASTM D1238 |
Braskem HF 0150 HDPE Blown Film Extrusion Polyethylene 38µm film gauge, obtained in 75mm extruder, die gap 1.0mm, output 1.75 kg/h-cm with 2:1 BUR. Applications: Grocery and T-shirt bags; merchandise bags; frozen-food bags. Information provided by Bras.. |
|||
Melt Flow | 0.45 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.45 g/10 min @Load 4.76 lb, Temperature 374 °F |
|
Arkema Group Evatane® 1003 VL 4C Ethylene Vinyl Acetate EVA copolymer made by high pressure tubular process. Anti-UV stabilized grade. Applications Thermal and colorless agricultural film to 180 at 200 µ for greenhouse coverage.ISO data provided by the .. |
|||
Melt Flow | 0.45 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.45 g/10 min @Load 4.76 lb, Temperature 374 °F |
|
Arkema Group Evatane® 1003 VL 4S Ethylene Vinyl Acetate EVA copolymer made by high pressure tubular process. Anti-UV stabilized grade. Applications Grade for transparent and thermal agricultural film to 180 at 200 µ for greenhouse coverage.ISO data prov.. |
|||
Melt Flow | 0.45 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.45 g/10 min @Load 4.76 lb, Temperature 374 °F |
|
Arkema Group Evatane® 1003 VN 4 Ethylene Vinyl Acetate EVA copolymer made by high pressure tubular process. Applications Grade for transparent and thermal agricultural film for greenhouse coverage.ISO data provided by the manufacturer, Arkema. |
|||
Melt Flow | 0.45 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.45 g/10 min @Load 4.76 lb, Temperature 374 °F |
|
Arkema Group Evatane® 1004 VL 4E Ethylene Vinyl Acetate EVA copolymer made by high pressure tubular process. Anti-UV stabilized grade. Applications Thermal and colorless agricultural film to 180 at 200 µ for greenhouse coverage.ISO data provided by the .. |
|||
Melt Flow | 0.45 g/10 min @Load 5.00 kg, Temperature 190 °C |
0.45 g/10 min @Load 11.0 lb, Temperature 374 °F |
ISO 1133 |
SCG Chemicals EL-Lene™ H5211PYL High Density Polyethylene Pipe Resin Key Characteristics: Good processing, high thermal stability, good resistance to weatheringRecommended Applications: Stripe lines for PE80 pipe, non pressure pipesCertification: Certified by LNEI.. |
|||
Melt Flow | 0.45 g/10 min | 0.45 g/10 min | Exxon Method (I2). HLMI (I21) is 30 g/10 min. |
ExxonMobil Escorene® HDZ-128 MMW-HDPE Blown Film Resin
(discontinued **) Data provided by the manufacturer, Exxon Chemical.Can be processed on high stalk, pocket extrusion or cast lines. Films made from HDZ-128 exhibit an excellent stiffness balance. High thermal stabi.. |