Polymer Property : Melt Flow = 0.20 g/10 min Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Physical Properties	Metric	English	Comments
Melt Flow	0.20 g/10 min @Load 5.00 kg, Temperature 200 °C	0.20 g/10 min @Load 11.0 lb, Temperature 392 °F	ISO 1133
Premix Thermoplastics PRE-ELEC® PS 1324 PRE-ELEC PS 1324 is a conductive thermoplastic compound based on polystyrene. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PRE-ELEC ..
Melt Flow	0.20 g/10 min @Load 2.16 kg, Temperature 190 °C	0.20 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D 1238
Chevron Phillips HiD® 9300 HDPE Orange Pipe Resin (discontinued **) Resin Type: Linear Copolymer; PE2406 Pipe Resin; ASTM D 3350 Classification: 234363E; ASTM D 4976 Classification: PE 225, A 56607Characteristics: PPI Recommended Hydrostatic Design Bases (HDB): 1250..
Melt Flow	0.20 g/10 min @Load 2.16 kg, Temperature 190 °C	0.20 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D 1238
Chevron Phillips HiD® 9302 HDPE Yellow Pipe Resin (discontinued **) Resin Type: Linear Copolymer; PE2406 Pipe Resin; ASTM D 3350 Classification: 234363E; ASTM D 4976 Classification: PE 225, A 56607Applications:Natural Gas Distribution Piping and FittingsData provide..
Melt Flow	0.20 g/10 min	0.20 g/10 min	Condition E; ASTM D 1238
Chevron Phillips HiD® 9640 HDPE Blown Film Resin (discontinued **) Copolymerization Enhances Film Toughness, Unique Combination of Density and Melt Index, Excellent Strength Properties as well as Good Heat Seal, Lower Density Imparts a Softer Feel and Lesser Tenden..
Melt Flow	0.20 g/10 min	0.20 g/10 min	Condition E; ASTM D 1238
Chevron Phillips HiD® 9647T HDPE Blown Film Resin (discontinued **) Resin Type: Linear Polyethylene CopolymerCharacteristics: Copolymerization Enhances Film Toughness, Unique Combination of Density and Melt Index, Excellent Strength Properties as well as Good Heat S..
Melt Flow	0.20 g/10 min	0.20 g/10 min	Exxon Method
ExxonMobil Escorene® LD-701 High EVA Film Resin (discontinued **) Data provided by the manufacturer, Exxon Chemical.A fractional melt, 10.5% vinyl acetate copolymer specialty film resin for applications requiring outstanding heat sealability, strength and toughnes..
Melt Flow	0.20 - 0.50 g/10 min	0.20 - 0.50 g/10 min
Kazanorgsintez 102-15 Composition of Low Density Polyethylene, Crack-Proof Production Method: Composition is achieved on the basis of grades 10204-003, 15303-003, 10703-020 and formulas of additives 15, 16, 17, 18, 19, 20, 21, 22, and 23. Application: Intended for prod..
Melt Flow	0.20 - 0.50 g/10 min	0.20 - 0.50 g/10 min
Kazanorgsintez 102-16 Composition of Low Density Polyethylene, Crack-Proof Production Method: Composition is achieved on the basis of grades 10204-003, 15303-003, 10703-020 and formulas of additives 15, 16, 17, 18, 19, 20, 21, 22, and 23. Application: Intended for prod..
Melt Flow	0.20 - 0.50 g/10 min	0.20 - 0.50 g/10 min
Kazanorgsintez 102-21 Composition of Low Density Polyethylene, Crack-Proof Production Method: Composition is achieved on the basis of grades 10204-003, 15303-003, 10703-020 and formulas of additives 15, 16, 17, 18, 19, 20, 21, 22, and 23. Application: Intended for prod..
Melt Flow	0.20 - 0.50 g/10 min	0.20 - 0.50 g/10 min
Kazanorgsintez 102-23 Composition of Low Density Polyethylene, Crack-Proof Production Method: Composition is achieved on the basis of grades 10204-003, 15303-003, 10703-020 and formulas of additives 15, 16, 17, 18, 19, 20, 21, 22, and 23. Application: Intended for prod..
Melt Flow	0.20 g/10 min	0.20 g/10 min	ASTM D1238
LyondellBasell PetrotheneÂ® LP5002 High Density Polyethylene (Blow Molding Grade) ApplicationsThe PETROTHENE LP series of polyethylene resins exhibits excellent environmental stress crack resistance and is especially designed for bottles containing aggressive agricultural and hou..
Melt Flow	0.20 g/10 min	0.20 g/10 min	ASTM D1238
Hyosung Topilene R200P PP R200P Extrusion Random CopolymerApplications:Underfloor heating pipeWater service pipeCharacteristics:Pressure resistanceHigh impactLong-term heat stabilityFlexibilityInformation provided by Hyosung..
Melt Flow	0.20 g/10 min	0.20 g/10 min	@ 190 C/2160g; ASTM D1238
Ineos K38-20-160 Polyethylene Copolymer K38-20-160 is a medium density polyethylene copolymer containing an organic yellow pigment system, designed specifically for the extrusion of natural gas pipe. It exhibits excellent long term stres..
Melt Flow	0.20 g/10 min @Load 2.16 kg, Temperature 190 Â°C	0.20 g/10 min @Load 4.76 lb, Temperature 374 Â°F	ASTM D1238
Ineos K38-20-188 HDPE K38-20-188 is a natural, UV stabilized, medium density polyethylene resin designed specifically for use with an approved Ineos North America yellow masterbatch to produce pipe or tubing for natural ..
Melt Flow	0.20 - 0.28 g/10 min @Load 5.00 kg, Temperature 190 Â°C	0.20 - 0.28 g/10 min @Load 11.0 lb, Temperature 374 Â°F	ASTM D1238-00
Ipiranga Petrochem GP 9452 F HDPE IPQ produces High Density Polyethylene (HDPE) for use by different segments of the plastics molding industry in several processes, including blow molding, extrusion and injection molding.To produce ..
Melt Flow	0.20 g/10 min @Load 5.00 kg, Temperature 190 °C	0.20 g/10 min @Load 11.0 lb, Temperature 374 °F	ISO 1133
Borealis Borstar® FB1460 HDPE for Film Borstar FB1460 is a high-density polyethylene film grade, which combines superior physical properties with excellent processability. Due to the high density, the material properties are best utiliz..
Melt Flow	0.20 g/10 min @Load 5.00 kg, Temperature 90.0 °C	0.20 g/10 min @Load 11.0 lb, Temperature 194 °F	ISO 1133/T
Total HDPE XLS 12 B High Density Polyethylene - Pipes and Fittings HDPE XLS 12 B is a high performance hexene-based black compound, with a MRS 10 MPa - PE100 classification, primarily intended for extrusion of large diameter and thick wall pressure pipes.Key charac..
Melt Flow	0.20 g/10 min @Load 2.16 kg, Temperature 190 °C	0.20 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238
Chevron Phillips MarFlex® HHM TR-258 Low Density Linear Polyethylene, Blown Film This LDLPE is tailored for applications that require:Good processabilityGood melt strengthGood drawdownGood strengthSatin finishGood MD & TD shrinkageGood contact clarity and lower gel contentTypica..
Melt Flow	0.20 g/10 min @Load 2.16 kg, Temperature 190 °C	0.20 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238
Chevron Phillips Marlex® HHM TR-418Q MDPE Hexene Copolymer High performance MDPE resin has been formulated for the demanding requirements of pressure pipe applications. Meets ASTM D4976 PE 225. Meets FDA Regulation 177.1520, suitable for food packaging ap..
Melt Flow	0.20 - 0.50 g/10 min @Load 2.16 kg, Temperature 190 °C	0.20 - 0.50 g/10 min @Load 4.76 lb, Temperature 374 °F
Breplast Bretene HD Bottles Flakes High Density Polyethylene Recovered polyethylene compositeInformation provided by Breplast S.p.A.
Melt Flow	0.20 - 5.0 g/10 min	0.20 - 5.0 g/10 min	ASTM D1238
Buckeye Polymers BP FLEX 8000 VPL BLK Thermoplastic Elastomer TPV Product Information: BP Flex TPV's are partially vulcanized thermoplastic elastomers designed to meet higher end applications that require the following performance criteria.Product Features:Higher ..
Melt Flow	0.20 g/10 min @Load 2.16 kg, Temperature 190 °C	0.20 g/10 min @Load 4.76 lb, Temperature 374 °F	ISO 1133
Carmel Olefins IPETHENE® 4203 Low Density Polyethylene IPETHENE® 4203 is a low density polyethylene extrusion grade. It exhibits good impact and puncture resistance, very good bubble stability in thick-gauge blown film processing, and excellent ESCR. ..
Melt Flow	0.20 g/10 min	0.20 g/10 min	ASTM D1238
Aclo Accutech ABS ABS834G40L Glass Reinforced
Melt Flow	<= 0.20 g/10 min @Load 21.6 kg, Temperature 230 °C	<= 0.20 g/10 min @Load 47.6 lb, Temperature 446 °F	ASTM D1238
Solvay Specialty Polymers Solef® 6020 Polyvinylidene Fluoride (PVDF) (Unverified Data**) Solef® 6020 PVDF homopolymer has very high viscosity for membranes and lithium batteries. It is available exclusively as powder.Information provided by Solvay Specialty Polymers.
Melt Flow	0.20 g/10 min	0.20 g/10 min	I<sub>2</sub>; ASTM D1238
Petromont 7001 Medium Density Polyethylene Resin Petromont HDPE 7001 is a medium-density polyethylene hexene modified resin with an excellent balance of chemical resistance and durability. It is designed to be readily processed by flat die extrusi..
Melt Flow	0.20 - 0.60 g/10 min @Load 2.16 kg, Temperature 190 °C	0.20 - 0.60 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238
Ravago Manufacturing Americas Echo® RPEHD BK HDPE Available in North AmericaDescription: Fractional Melt Recycled Content: Yes Color: Black Form: Pellets Information provided by Entec
Melt Flow	0.20 - 0.50 g/10 min	0.20 - 0.50 g/10 min
Kazanorgsintez 153-16 Composition of Low Density Polyethylene, Crack-Proof Production Method: Composition is achieved on the basis of grades 10204-003, 15303-003, 10703-020 and formulas of additives 15, 16, 17, 18, 19, 20, 21, 22, and 23. Application: Intended for prod..
Melt Flow	0.20 g/10 min @Load 2.16 kg, Temperature 190 °C	0.20 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238
ExxonMobil Paxon™ AA50-002 Blow Molding Resin (discontinued **) AA50-002 is a blow molding grade high density polyethylene. This resin has excellent stress crack resistance combined with high impact strength, rigidity, and melt strength.Information provided by ..
Melt Flow	0.20 g/10 min	0.20 g/10 min	I<sub>2</sub>; ASTM D1238/E
Petromont 7002 Medium Density Polyethylene Resin Petromont HDPE 7002 is a medium-density polyethylene hexene modified resin with an excellent balance of chemical resistance and durability. It is designed to be readily processed by flat die extrusi..
Melt Flow	0.20 g/10 min @Load 2.16 kg, Temperature 190 °C	0.20 g/10 min @Load 4.76 lb, Temperature 374 °F	Condition E; ASTM D1238
Formosa Plastics Formolene® HP3902 Pipe HDPE Natural Medium Density Hexene CopolymerApplications: Pipe for gas distribution, oilfield and other industrial pipe, telecommunications conduit.Formolene HP3902 is a high performance copolymer that i..