Physical Properties | Metric | English | Comments |
---|---|---|---|
Apparent Bulk Density | 0.550 - 0.700 g/cc | 0.0199 - 0.0253 lb/in³ | ISO 60 |
Raschig Group DECAL® 5431 Phenolic Organically and inorganically filled phenolic molding compound. This product meets the allowed upper limits for heavy metals and PCAs and also conforms to the requirements of the EU directives 2002/.. |
|||
Apparent Bulk Density | 0.550 - 0.750 g/cc | 0.0199 - 0.0271 lb/in³ | ISO 60 |
Raschig Group MELOPAS® 2010 MF Melamine Organically and inorganically filled Melamine molding compound. Excellent surface hardness, good mechanical strength, good electrical properties. This product meets the allowed upper limits for heav.. |
|||
Apparent Bulk Density | 0.550 - 0.750 g/cc | 0.0199 - 0.0271 lb/in³ | ISO 60 |
Raschig Group MELOPAS® 6605 MP Melamine Cellulose reinforced Melamine molding compound. Very good electrical properties, excellent surface hardness, good mechanical strength and heat resistance, good wear and UV-stability, good gliding be.. |
|||
Apparent Bulk Density | 0.550 - 0.750 g/cc | 0.0199 - 0.0271 lb/in³ | ISO 60 |
Raschig Group MELOPLAS® 152 MF Cellulose-reinforced MF molding compound in white and colored shades. Very good electrical properties, high surface hardness, good abrasion- and UV-stability, very good resistance to chemicals - al.. |
|||
Apparent Bulk Density | 0.550 - 0.750 g/cc | 0.0199 - 0.0271 lb/in³ | ISO 60 |
Raschig Group MELOPLAS® 152.7 MF Cellulose-reinforced MF molding compound in white and colored shades. High surface hardness, very good UV stability, very good resistance to chemicals also to foodstuff ingredients, physiologically.. |
|||
Apparent Bulk Density | 0.550 - 0.750 g/cc | 0.0199 - 0.0271 lb/in³ | ISO 60 |
Raschig Group MELOPLAS® 181.5 MF Cellulose-reinforced, phenol-modified MF molding compound (MPF) in white and colored shades. Very good electrical properties, high surface hardness, good mechanical strength, high UV and heat resis.. |
|||
Apparent Bulk Density | 0.550 - 0.750 g/cc | 0.0199 - 0.0271 lb/in³ | ISO 60 |
Raschig Group MELOPLAS® 182 MF Wood flour-reinforced and inorganically filled, phenol-modified MF molding compound (MPF) in dark colors. Improved dimensional stability and electrical properties as compared with MP 180, high surf.. |
|||
Apparent Bulk Density | 0.550 - 0.750 g/cc | 0.0199 - 0.0271 lb/in³ | ISO 60 |
Raschig Group MELOPLAS® 183 MF Cellulose-reinforced and inorganically filled, phenol-modified MF molding compound (MPF) in white and colored shades. Improved dimensional stability and electrical properties as compared with MP 18.. |
|||
Apparent Bulk Density | 0.550 - 0.750 g/cc | 0.0199 - 0.0271 lb/in³ | ISO 60 |
Raschig Group MELOPLAS® 2500 MF Cellulose-reinforced MF molding compound in white and colored shades. Very good electrical properties, high surface hardness, good abrasion- and UV-stability, very good resistance to chemicals - al.. |
|||
Apparent Bulk Density | 0.550 - 0.780 g/cc | 0.0199 - 0.0282 lb/in³ | Average value: 0.650 g/cc Grade Count:5 |
Overview of materials for PVC, Powder This property data is a summary of similar materials in the MatWeb database for the category "PVC, Powder". Each property range of values reported is minimum and maximum values of appropriate MatWeb.. |
|||
Apparent Bulk Density | 0.550 g/cc | 0.0199 lb/in³ | ISO 60 |
Hexion Bakelite™ PF 84 Phenolic Formaldehyde Resin, Special Preparation Cylindrical Pellets, High Mechanical Strength
& Phenolic molding compound, organically filled, reinforced with cotton fibers, increased notched impact strength, standardized molding compound.Application areas: Contact support power switch, moldin.. |
|||
Apparent Bulk Density | 0.550 g/cc | 0.0199 lb/in³ | ISO 60 |
Hexion Bakelite™ PF 14600 Phenolic Formaldehyde Resin, High Surface Quality
(discontinued **) Phenolic molding compound, mainly organically filled, low specific gravity.Application areas: Cookware fittings, electric devices.Information provided by Bak AGBak AG became a part of Hexion in 2005.. |
|||
Apparent Bulk Density | 0.550 g/cc | 0.0199 lb/in³ | ASTM D1895 |
Plenco 306 Black General Purpose Mineral/Flock Filled Phenolic Molding Compound
(discontinued **) Plaslok 306 is a two-stage, mineral and flock-filled phenolic molding compound designed to have the heat resistant characteristics of Plaslok 504, while at the same time, improved impact strength.Da.. |
|||
Apparent Bulk Density | 0.550 g/cc | 0.0199 lb/in³ | ASTM D1895 |
Plenco 307 Black Impact Grade Mineral/Flock Filled Phenolic Molding Compound
(discontinued **) Plaslok 307 is a two-stage, mineral and flock-filled phenolic molding compound designed for the automotive industry for use in brake system components. It is characterized by good molding latitude .. |
|||
Apparent Bulk Density | 0.550 g/cc | 0.0199 lb/in³ | ASTM D1895 |
Plaslok 307 Black Impact Grade Mineral/Flock Filled Phenolic Molding Compound
(discontinued **) Plaslok Corporation was purchased by Plastics Engineering Company (maker of Plenco brand materials) in March 2000. The Plaslok name is no longer in use.Plaslok 307 is a two-stage, mineral and flock.. |
|||
Apparent Bulk Density | 0.550 g/cc | 0.0199 lb/in³ | Tap density |
Momentive Performance Materials AC-6004 Boron Nitride (BN) Powder Grade AC-6004 is a high purity, fine (99%,-325 mesh) Boron Nitride (BN) powder with a hexagonal crystal structure and large graphite-like platelets. It exhibits the unique properties of boron nitri.. |
|||
Apparent Bulk Density | 0.550 g/cc | 0.0199 lb/in³ | ASTM D1895 |
Solvay Specialty Polymers Catalyst CAT 10 Polyolefin Catalyst CAT 10 is a high density based catalyst masterbatch, which accelerates the crosslinking reaction of the pipe product during its curing process that can take place by exposure of the pipe to.. |
|||
Apparent Bulk Density | 0.550 g/cc | 0.0199 lb/in³ | ASTM D1895 |
Solvay Specialty Polymers Catalyst CT 0552/09 Polyolefin Catalyst CT 0552/09 is a PE based catalyst masterbatch, which accelerates the crosslinking reaction of the pipe product during its curing process that can take place by exposure of the pipe to water.. |
|||
Apparent Bulk Density | 0.550 g/cc | 0.0199 lb/in³ | ASTM D1895 |
Solvay Specialty Polymers Catalyst LV/1 Polyolefin Catalyst LV/1 is a PE based catalyst masterbatch, which accelerates the crosslinking reaction of the pipe product during its curing process that can take place by exposure of the pipe to water or st.. |
|||
Apparent Bulk Density | 0.550 g/cc | 0.0199 lb/in³ | ASTM D1895 |
Solvay Specialty Polymers Catalyst LV/1LR Polyolefin Catalyst LV/1LR is a PE based catalyst masterbatch, which accelerates the crosslinking reaction of the pipe product during its curing process that can take place by exposure of the pipe to water or .. |
|||
Apparent Bulk Density | 0.550 g/cc | 0.0199 lb/in³ | ASTM D1895 |
Solvay Specialty Polymers Catalyst PS/2 UV Polyolefin Catalyst PS/2 UV is a PE based catalyst masterbatch, which accelerates the crosslinking reaction of the pipe product during its curing process that can take place by exposure of the pipe to water or.. |
|||
Apparent Bulk Density | 0.550 g/cc | 0.0199 lb/in³ | ASTM D1895 |
Solvay Specialty Polymers Catalyst PS/2LR Polyolefin Catalyst PS/2LR is a PE based catalyst masterbatch, which accelerates the crosslinking reaction of the pipe product during its curing process that can take place by exposure of the pipe to water or .. |
|||
Apparent Bulk Density | 0.550 g/cc | 0.0199 lb/in³ | ASTM D1895 |
Solvay Specialty Polymers Catalyst PS/2LRO Polyolefin Catalyst PS/2LR0 is a PE based catalyst masterbatch, which accelerates the crosslinking reaction of the pipe product during its curing process that can take place by exposure of the pipe to water or.. |
|||
Apparent Bulk Density | 0.550 g/cc | 0.0199 lb/in³ | ASTM D1895 |
Solvay Specialty Polymers Catalyst PS/4 Polyolefin Catalyst PS/4 is a PE based catalyst masterbatch, which accelerates the crosslinking reaction of the pipe product during its curing process that can take place by exposure of the pipe to water or st.. |
|||
Apparent Bulk Density | 0.550 g/cc | 0.0199 lb/in³ | ASTM D1895 |
Solvay Specialty Polymers Catalyst CT/2-OR UV Polyolefin Catalyst CT/2-OR UV is a polyolefin based masterbatch to be used with Cogegum® GFR/380, and confers improved UV/VIS and aging resistance. It contains also a metal deactivator that allows its use .. |
|||
Apparent Bulk Density | 0.550 - 0.650 g/cc | 0.0199 - 0.0235 lb/in³ | MSZ ISO 60:1994 |
BorsodChem ONGROSTYR F-I Expandable Polystyrene (EPS) ONGROSTYR F-I is an expandable, flame-retardant styrene homopolymer, produced by suspension polymerization. The product meets the requirements of DIN 4102 and of B1 class of building materials, i.e... |
|||
Apparent Bulk Density | 0.550 - 0.650 g/cc | 0.0199 - 0.0235 lb/in³ | MSZ ISO 60:1994 |
BorsodChem ONGROSTYR F-III Expandable Polystyrene (EPS) ONGROSTYR F-III is an expandable, flame-retardant styrene homopolymer, produced by suspension polymerization. The product meets the requirements of DIN 4102 and of B1 class of building materials, i... |
|||
Apparent Bulk Density | 0.550 - 0.750 g/cc | 0.0199 - 0.0271 lb/in³ | ISO 60 |
Raschig Group MELOPLAS® 180 MF Wood flour-reinforced, phenol-modified MF molding compound (MPF) in dark colors. High surface hardness, good mechanical strength and electrical properties, good heat resistance. Self-extinguishing .. |
|||
Apparent Bulk Density | 0.550 - 0.610 g/cc | 0.0199 - 0.0220 lb/in³ | ISO 60:1977 |
BorsodChem ONGROVIL S-5258 Suspension PVC-Resin S-5258 is a suspension type PVC homopolymer of medium molecular mass. It is characterized by a porous particle structure, a narrow range of particle size and a relatively high apparent density. It r.. |
|||
Apparent Bulk Density | 0.550 g/cc | 0.0199 lb/in³ | Apparent density per ASTM D1895 |
Plenco 7467 Phenolic, Nodular, Transfer Molded
(discontinued **) Two-Stage Phenolic. PLENCO 07467 is an organic phenolic molding compound offering excellent dimensional stability under conditions of total water immersion. 07467 is formulated to provide improved .. |