Physical Properties | Metric | English | Comments |
---|---|---|---|
Apparent Bulk Density | 0.450 - 0.800 g/cc | 0.0163 - 0.0289 lb/in³ | Average value: 0.584 g/cc Grade Count:16 |
Overview of materials for Polyvinyl Chloride - Polyvinyl Acetate Copolymer This property data is a summary of similar materials in the MatWeb database for the category "Polyvinyl Chloride - Polyvinyl Acetate Copolymer". Each property range of values reported is minimum and.. |
|||
Apparent Bulk Density | 0.450 g/cc | 0.0163 lb/in³ | ASTM D4894 |
Solvay Specialty Polymers Algoflon® 20FLCA PTFE; Calcium Fluoride Filled
(discontinued **) Data provided by the manufacturer.20 wt.% Calcium Fluoride. Suspension polymer powder grade recommended for compression molding. Pure PTFE possesses high inertness, excellent dielectric properties, .. |
|||
Apparent Bulk Density | 0.450 - 0.510 g/cc | 0.0163 - 0.0184 lb/in³ | Average value: 0.493 g/cc Grade Count:6 |
Overview of materials for Polytetrafluoroethylene (PTFE), Extruded This property data is a summary of similar materials in the MatWeb database for the category "Polytetrafluoroethylene (PTFE), Extruded". Each property range of values reported is minimum and maximum.. |
|||
Apparent Bulk Density | 0.450 g/cc | 0.0163 lb/in³ | DIN 53466 |
3M Dyneon™ TFM™ 2001 Modified PTFE Paste Extrusion Powder
(discontinued **) Type I, gr. 2 PTFE. Free flowing powder. Minimum reduction ratio is 20; Max is 1000. Average particle size 500µm.Modified PTFE fine powder product for paste extrusion applications. The modified .. |
|||
Apparent Bulk Density | 0.450 - 0.570 g/cc | 0.0163 - 0.0206 lb/in³ | Average value: 0.504 g/cc Grade Count:17 |
Overview of materials for Phenolic, Novolac, Impact Grade, Filled This property data is a summary of similar materials in the MatWeb database for the category "Phenolic, Novolac, Impact Grade, Filled". Each property range of values reported is minimum and maximum .. |
|||
Apparent Bulk Density | 0.450 g/cc | 0.0163 lb/in³ | ASTM D1895 |
Plenco 5314 Black (COM) Impact Grade Phenolic Molding Compound
(discontinued **) Plaslok 5314 is the replacement material for the former Union Carbide BMMA-5314. It is a two-stage, impact grade phenolic molding compound suitable for compression, transfer or injection molding of.. |
|||
Apparent Bulk Density | 0.450 g/cc | 0.0163 lb/in³ | ASTM D1895 |
Plenco 5314 Black (INJ) Impact Grade Phenolic Molding Compound
(discontinued **) Plaslok 5314 is the replacement material for the former Union Carbide BMMA-5314. It is a two-stage, impact grade phenolic molding compound suitable for compression, transfer or injection molding of.. |
|||
Apparent Bulk Density | 0.450 g/cc | 0.0163 lb/in³ | |
Lucobit Lucocell® FG3000 Cellulose Asphalt Additive Lucocell® FG3000 micro grains – cellulose additives for SMA –Stone Mastic Asphalt or Split Mastic Asphalt, which is used as finish for all road types. Due to their 3D structure, cellulo.. |
|||
Apparent Bulk Density | 0.450 g/cc | 0.0163 lb/in³ | TRM-37 |
Tipco Tipcolite® TEL 211 Phenolic Compound, Glass & Nylon Fibers, Soft Flow & Low Shrinkage Soft Flow Phenolic Compound, Reinforced with Glass & Nylon FibresApplications: Automotives & ElectricalProcessing: Compression & TransferInformation provided by the Manufacturer, Tipco Industries L.. |
|||
Apparent Bulk Density | 0.450 g/cc | 0.0163 lb/in³ | MSZ ISO 60 |
BorsodChem ONGRO CPE 4002 N Chlorinated Polyethylene IMPACT MODIFIER FOR PVChigh impact resistancegood processabilityexcellent weather resistanceELASTOMERSvariety of cross-linking technologiesexcellent ozone- and weather resistanceexcellent chemical r.. |
|||
Apparent Bulk Density | 0.450 g/cc | 0.0163 lb/in³ | ISO 1068 |
Arkema Group ORGASOL® 3202 D Nat 1 Copolyamide 6/12 Information provided by Arkema Group |
|||
Apparent Bulk Density | 0.450 g/cc | 0.0163 lb/in³ | ASTM D4894 |
Solvay Specialty Polymers Algoflon® 25CAR B PTFE; Carbon Filled
(discontinued **) Data provided by the manufacturer.25 wt.% Electrog. Carbon. Suspension polymer powder grade recommended for compression molding. Pure PTFE possesses high inertness, excellent dielectric properties, .. |
|||
Apparent Bulk Density | 0.450 g/cc | 0.0163 lb/in³ | ASTM D4894 |
Solvay Specialty Polymers Algoflon® 0.1 Mos PTFE; Molybdenum Disulfide Filled
(discontinued **) Data provided by the manufacturer.0.1 wt.% Molybdenum Disulfide. Suspension polymer powder grade recommended for compression molding. Pure PTFE possesses high inertness, excellent dielectric propert.. |
|||
Apparent Bulk Density | 0.450 g/cc | 0.0163 lb/in³ | ASTM-D1895 |
Braskem Idealis 500 Compression Molding High Molecular Weight Polyethylene Braskem Idealis 500 is the only high molecular weight polyethylene resin in powder form specially designed for the compression molding process. Its applications range from food handling, cutting boa.. |
|||
Apparent Bulk Density | 0.450 g/cc | 0.0163 lb/in³ | ASTM D1895 |
Plaslok 5314 Black (COM) Impact Grade Phenolic Molding Compound
(discontinued **) Plaslok Corporation was purchased by Plastics Engineering Company (maker of Plenco brand materials) in March 2000. The Plaslok name is no longer in use.Plaslok 5314 is the replacement material for .. |
|||
Apparent Bulk Density | 0.450 g/cc | 0.0163 lb/in³ | ASTM D1895 |
Plaslok 5314 Black (INJ) Impact Grade Phenolic Molding Compound
(discontinued **) Plaslok Corporation was purchased by Plastics Engineering Company (maker of Plenco brand materials) in March 2000. The Plaslok name is no longer in use.Plaslok 5314 is the replacement material for .. |