Physical Properties | Metric | English | Comments |
---|---|---|---|
Melt Index of Compound | 4.0 g/10 min @Load 2.16 kg, Temperature 280 °C |
4.0 g/10 min @Load 4.76 lb, Temperature 536 °F |
ASTM D1238 |
Ovation Polymers Nima™ NH PA66UT Nylon 66 Polyamide 66 - Ultra Tough, Flame Retarded Non-Hal grade with excellent retention of mechanical properties. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humi.. |
|||
Melt Index of Compound | 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
4.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
Ovation Polymers Opnyl OP6MT254 Nylon 6 Nylon 6 – Mighty Tough plasticized extrusion grade for tubing/profile applications. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humidity. All samples are p.. |
|||
Melt Index of Compound | 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
4.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
Polykemi AB POLYfill PPC TS4030 H Polypropylene Copolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
Melt Index of Compound | 4.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
4.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
SABIC Innovative Plastics Lexan® 3414R PC (Europe-Africa-Middle East) LEXAN 3414R is a high viscosity, 40% glass reinforced, flame retardant grade, especially designed for applications requiring high rigidity together with high heat resistance. |
|||
Melt Index of Compound | 4.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
4.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
MVR [cm^3/10 min]; ISO 1133 |
SABIC Innovative Plastics Cycolac® EX58F ABS High impact ABS for sheet extrusion and blow molding applications. FDA food contact compliant. |
|||
Melt Index of Compound | 4.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
4.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
MVR [cm^3/10 min]; ISO 1133 |
SABIC Innovative Plastics Cycolac® EX58F ABS (Asia Pacific) High impact ABS for sheet extrusion and blow molding applications. FDA food contact compliant. |
|||
Melt Index of Compound | 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
4.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
Polykemi AB POLYfill PPH BF4075 VT1 Polypropylene Homopolymer, Reinforced, Heat Resistant Information provided by Polykemi AB |
|||
Melt Index of Compound | 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
4.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
Polykemi AB POLYfill PPH GF4030 PD2 Polypropylene Homopolymer, Glass Fibre-Reinforced, Chemically Coupled Information provided by Polykemi AB |
|||
Melt Index of Compound | 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
4.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
Polykemi AB POLYfill PPH S4030 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
Melt Index of Compound | 4.0 - 5.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
4.0 - 5.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
Petroquimica Triunfo Trithene® TS 7045 LDPE - Film - Plastification The Trithene TS 7045 resin is a low-density polyethylene (LDPE) with an excellent processability, which allows for a low energy consumption during extrusion and warrants the production of thin films.. |
|||
Melt Index of Compound | 4.0 g/10 min @Load 2.16 kg, Temperature 250 °C |
4.0 g/10 min @Load 4.76 lb, Temperature 482 °F |
DAM; cm3/10 min; ISO 1133 |
DuPont Performance Polymers Zytel® 73G30HSL NC010 Nylon 6
(Unverified Data**) Zytel® 73G30HSL NC010 is a 30% glass fiber reinforced, heat stabilized polyamide 6 resin for injection molding.Information provided by DuPont Performance Polymers |
|||
Melt Index of Compound | 4.0 g/10 min @Temperature 190 °C |
4.0 g/10 min @Temperature 374 °F |
ASTM D1238 |
Mitsui ADMER® NF548A PE Type Polyolefin ADMER® Adhesive Resin is a modified polyolefin with functional groups, designed to bond to a variety of polyolefins, ionomers, polyamides, ethylene vinyl alcohol (EVOH), polyesters (PET), polycar.. |
|||
Melt Index of Compound | 4.0 g/10 min @Load 5.00 kg, Temperature 265 °C |
4.0 g/10 min @Load 11.0 lb, Temperature 509 °F |
MVR [cm^3/10 min]; ISO 1133 |
SABIC Innovative Plastics Xenoy® X4850 PBT+PC Xenoy X4850 is a hydrostable, high modulus, high ductile PC/PBT blend. Furthermore, this resin provides high chemicalresistance, very low creep, low CTE, excellent fatique and high heat dimensional .. |
|||
Melt Index of Compound | 4.0 - 12 g/10 min @Load 2.16 kg, Temperature 230 °C |
4.0 - 12 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
A. Schulman POLYFLAM™ E-13030B Reinforced Super Coupled Polypropylene Black DescriptionPolyfort® E-13030B is a reinforced super coupled polypropylene black. Information provided by A. Schulman. |
|||
Melt Index of Compound | 4.0 g/10 min | 4.0 g/10 min | ASTM D1238 |
DuPont Surlyn® 8945 Thermoplastic Ionomer Resin Surlyn® 8945 provides high flow properties and consistent, easy processing in molded and extruded applications. It is positioned in the medium/high acid, high neutralization area of the ionomer sp.. |
|||
Melt Index of Compound | 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
4.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
A. Schulman PP 1247-01 Polypropylene Homopolymer Polypropylene DescriptionPolypropylene PP 1247-01 is a homopolymer polypropylene designed for general-purpose injection-molding applications where parts require excellent stiffness. ApplicationPolypropylene PP 12.. |
|||
Melt Index of Compound | 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
4.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
A. Schulman PP 1247-01 Polypropylene Homopolymer Polypropylene DescriptionPolypropylene PP 1247-01 is a homopolymer polypropylene designed for general-purpose injection-molding applications where parts require excellent stiffness. ApplicationPolypropylene PP 12.. |
|||
Melt Index of Compound | 4.0 - 12 g/10 min @Load 2.16 kg, Temperature 230 °C |
4.0 - 12 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
A. Schulman POLYFLAM™ E-13030B Reinforced Super Coupled Polypropylene Black DescriptionPolyfort® E-13030B is a reinforced super coupled polypropylene black. Information provided by A. Schulman. |
|||
Melt Index of Compound | 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
4.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
A. Schulman PP 829-01 Polypropylene Homopolymer Polypropylene DescriptionPolypropylene PP 829-01 is a homopolymer polypropylene approved to Ford specification ESB-M4D63A. Primarily used for interior automotive components, this material is also well suited for.. |
|||
Melt Index of Compound | 4.0 - 8.0 g/10 min | 4.0 - 8.0 g/10 min | ASTM D1238 |
A. Schulman POLYFORT™ FPP 4020 20% Mineral-Filled Polypropylene DescriptionPolyfort® FPP 4020 is a 20% mineral-filled polypropylene designed for use when improved heat resistance and high stiffness is needed.Information provided by A. Schulman. |
|||
Melt Index of Compound | 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
4.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
A. Schulman PP 1247-01 Polypropylene Homopolymer Polypropylene DescriptionPolypropylene PP 1247-01 is a homopolymer polypropylene designed for general-purpose injection-molding applications where parts require excellent stiffness. ApplicationPolypropylene PP 12.. |
|||
Melt Index of Compound | 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
4.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
A. Schulman PP 829-01 Polypropylene Homopolymer Polypropylene DescriptionPolypropylene PP 829-01 is a homopolymer polypropylene approved to Ford specification ESB-M4D63A. Primarily used for interior automotive components, this material is also well suited for.. |
|||
Melt Index of Compound | 4.0 - 8.0 g/10 min | 4.0 - 8.0 g/10 min | ASTM D1238 |
A. Schulman POLYFORT™ FPP 4020 20% Mineral-Filled Polypropylene DescriptionPolyfort® FPP 4020 is a 20% mineral-filled polypropylene designed for use when improved heat resistance and high stiffness is needed.Information provided by A. Schulman. |
|||
Melt Index of Compound | 4.0 g/10 min | 4.0 g/10 min | ASTM D1238 |
DuPont Surlyn® 9945 Thermoplastic Ionomer Resin Surlyn® 9945 provides high flow properties and consistent, easy processing behavior in molded and extruded applications. It is positioned in the medium/high acid, high neutralization area of the i.. |
|||
Melt Index of Compound | 4.0 - 8.0 g/10 min | 4.0 - 8.0 g/10 min | ASTM D1238 |
A. Schulman POLYFORT™ FPP 4020 20% Mineral-Filled Polypropylene DescriptionPolyfort® FPP 4020 is a 20% mineral-filled polypropylene designed for use when improved heat resistance and high stiffness is needed.Information provided by A. Schulman. |
|||
Melt Index of Compound | 4.0 g/10 min @Load 21.6 kg, Temperature 150 °C |
4.0 g/10 min @Load 47.6 lb, Temperature 302 °F |
Fainplast |
Fainplast Compounds HAX HF 029/47 Halogen Free PVC General purpose |
|||
Melt Index of Compound | 4.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
4.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
Arkema Group OREVAC® 18380 Maleic Anhydride Modified Polyethylene OREVAC® 18380 is anhydride modified polyethylene. It is available in pellet form for use in conventional extrusion and coextrusion equipment designed to process polyethylene (PE) resins. OREVAC® 1.. |
|||
Melt Index of Compound | 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
4.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
Polykemi AB POLYfill PPH TS4020 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
Melt Index of Compound | 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
4.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
Polykemi AB POLYfill PPH TS4040 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
Melt Index of Compound | 4.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
4.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
MVR [cm^3/10 min]; ISO 1133 |
SABIC Innovative Plastics Cycolac® EX39 ABS Highest impact extrusion ABS for sheet and blow molding applications. |