Physical Properties | Metric | English | Comments |
---|---|---|---|
Melt Index of Compound | 3.5 - 8.5 g/10 min @Load 5.00 kg, Temperature 265 °C |
3.5 - 8.5 g/10 min @Load 11.0 lb, Temperature 509 °F |
ASTM D1238 |
3M Dyneon™ THV 510ESD Fluorothermoplastic
(discontinued **) THV 510ESD is a flexible, fluoroplastic compound composed of tetrafluoroethylene, hexafluoropropylene, and vinylidene fluoride in the form of pellets. It provides a balance of low temperature proces.. |
|||
Melt Index of Compound | 3.5 g/10 min @Load 2.16 kg, Temperature 190 °C |
3.5 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
ICO Polymers ICORENEâ„¢ 155-1326 LMDPE Rotational Molding Resin Description: ICORENE 155-1326 is a linear medium density polyethylene developed for use in rotational molding. It has a great combination of stiffness and toughness in a resin that is easy processi.. |
|||
Melt Index of Compound | 3.5 g/10 min @Load 2.16 kg, Temperature 190 °C |
3.5 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
ICO Polymers ICORENEâ„¢ 155-1330 LMDPE Rotational Molding Resin Description: ICORENE 155-1330 is a linear medium density polyethylene developed for use in rotational molding. It has a great combination of stiffness and toughness in a resin that is easy processi.. |
|||
Melt Index of Compound | 3.5 g/10 min @Load 2.16 kg, Temperature 190 °C |
3.5 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
ICO Polymers ICORENEâ„¢ 195-1326 LMDPE Rotational Molding Resin Description: ICORENE 195-1326 is a linear medium density polyethylene copolymer developed for rotational molding. It has a good balance of properties such as toughness, easy flow and stiffness. Ke.. |
|||
Melt Index of Compound | 3.5 g/10 min @Load 2.16 kg, Temperature 190 °C |
3.5 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
ICO Polymers ICORENEâ„¢ 195-1330 LMDPE Rotational Molding Resin Description: ICORENE 195-1330 is a compounded linear medium density polyethylene copolymer developed for rotational molding. It has a good balance of properties such as toughness, easy flow and sti.. |
|||
Melt Index of Compound | 3.5 g/10 min @Load 3.80 kg, Temperature 230 °C |
3.5 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D1238 |
LG Chemical HI855H PMMA, Impact Resistant Grade Molding granule designed for greater impact strength combined with the outstanding properties of conventional acrylic materialsFeatures: Excellent transparency and eleganceWeather resistance and che.. |
|||
Melt Index of Compound | 3.5 g/10 min @Load 2.16 kg, Temperature 190 °C |
3.5 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
Lushan EP252 Adhesive Resin for Sewerage and Drainage Pipe Adhesive resin Lushan EP252 is maleic grafted polyethylene. It’s mainly used for reinforced PE spiral corrugated steel pipes and steel wire with larger caliber. Adhesive resin Lushan EP252 solv.. |
|||
Melt Index of Compound | 3.5 g/10 min | 3.5 g/10 min | ASTM D1238 |
Lushan VB517 Adhesive Resin for Aluminum-Plastic Composite Panel (ACP), High Temperature Adhesive resin Lushan series for Aluminum-plastic Composite Panel (ACP) proved required bonding strength between aluminum and the filled polyethylene core. The sandwich structure of Aluminum-plastic.. |
|||
Melt Index of Compound | 3.5 - 6.2 g/10 min | 3.5 - 6.2 g/10 min | II Preparation |
Sibur ABS 1106M Extrusion Grade ABS Plastic With high thermal and light resistance for production of sheets with following pneumatic and vacuum formation of internal parts for refrigerators and other articles of technical purpose. |
|||
Melt Index of Compound | 3.5 g/10 min | 3.5 g/10 min | ASTM D1238E |
Chevron Phillips MarFlex® 7235 LLDPE Cast Film Resin Resin Type: Hexene CopolymerCharacteristics: Good OpticsGood drawdownExcellent processabilityCan use straight or in blends with LDPE or HDPEApplications: Bakery filmsOverwrapCoextrusionsInformation .. |
|||
Melt Index of Compound | 3.5 g/10 min @Load 2.16 kg, Temperature 190 °C |
3.5 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
Dow Engage® 8445 Polyolefin Elastomer Description: Engage® 8445 polyolefin elastomer is an ethyleneoctene copolymer that performs well in a wide range of thermoplastic elastomer applications. It has excellent compatibility with other p.. |
|||
Melt Index of Compound | 3.5 g/10 min @Load 21.6 kg, Temperature 150 °C |
3.5 g/10 min @Load 47.6 lb, Temperature 302 °F |
Fainplast |
Fainplast Compounds HAX HF 018/15 Halogen Free PVC General purpose |
|||
Melt Index of Compound | 3.5 g/10 min @Load 21.6 kg, Temperature 150 °C |
3.5 g/10 min @Load 47.6 lb, Temperature 302 °F |
Fainplast |
Fainplast Compounds HAX HF 018/9 Halogen Free PVC General purpose |
|||
Melt Index of Compound | 3.5 g/10 min @Load 2.16 kg, Temperature 230 °C |
3.5 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
Arkema Group OREVAC® 18211 Maleic Anhydride Grafted EVA Copolymer OREVAC® 18211 is maleic anhydride grafted EVA copolymer. It is available in pellet form for use in conventional extrusion and coextrusion equipment designed to process polyethylene (PE) resins. ORE.. |
|||
Melt Index of Compound | 3.5 - 4.5 g/10 min @Load 2.16 kg, Temperature 190 °C |
3.5 - 4.5 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
Arkema Group LOTRYL® 17 BA 04 Copolymer Ethylene - Butyl Acrylate LOTRYL® 17 BA 04 is a random copolymer of ethylene and butyl acrylate, prepared by the high pressure polymerization process. LOTRYL® 17 BA 04 is used as tie layer in coextrusion PP/PE, for extrusi.. |