Physical Properties | Metric | English | Comments |
---|---|---|---|
Melt Index of Compound | 2.0 g/10 min @Load 2.16 kg, Temperature 280 °C |
2.0 g/10 min @Load 4.76 lb, Temperature 536 °F |
ASTM D1238 |
Ovation Polymers UTTAP QU BM513 GF BM Nylon, 13% Glass Reinforced Glass reinforced (13 %) High Temperature Polyamide - Blow Molding grade with excellent chemical resistance, improved flow and high HDT. *All properties are measured after 48 hours of conditioning at.. |
|||
Melt Index of Compound | 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
2.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
Polykemi AB POLYfill PPC GF2007 PD1 Polypropylene Copolymer, Glass Fiber Reinforced, Chemically Coupled Information provided by Polykemi AB |
|||
Melt Index of Compound | 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
2.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
Polykemi AB POLYfill PPH GF2020 PD2 Polypropylene Homopolymer, Glass Fibre-Reinforced, Chemically Coupled Information provided by Polykemi AB |
|||
Melt Index of Compound | 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
2.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
Polykemi AB POLYfill PPH T2020 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
Melt Index of Compound | 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
2.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
Polykemi AB POLYfill PPH TS2020 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
Melt Index of Compound | 2.0 g/10 min @Load 5.00 kg, Temperature 230 °C |
2.0 g/10 min @Load 11.0 lb, Temperature 446 °F |
ISO 1133 |
Polykemi AB POLYplex PMMA 500 Acrylic Glass Information provided by Polykemi AB |
|||
Melt Index of Compound | 2.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
2.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
SABIC Innovative Plastics Lexan® SLX2571T PC Copolymer Transparent weatherable PC copolymer for blowmolding/extrusion. |
|||
Melt Index of Compound | 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
2.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
Polykemi AB POLYfill PP TOUCH 25325 Polypropylene, Glass Fiber Reinforced Information provided by Polykemi AB |
|||
Melt Index of Compound | 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
2.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
Polykemi AB POLYfill PP TOUCH 25325 R3 Polypropylene, Glass Fiber Reinforced, Scratch Resistant Information provided by Polykemi AB |
|||
Melt Index of Compound | 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
2.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
Polykemi AB POLYfill PPH GF2030 PD2 Polypropylene Homopolymer, Glass Fibre-Reinforced, Chemically Coupled Information provided by Polykemi AB |
|||
Melt Index of Compound | 2.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
2.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
SABIC Innovative Plastics Lexan® HPH4704 PPC (Europe-Africa-Middle East) High heat specialty polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO, steam, gamma and e-beam steril.. |
|||
Melt Index of Compound | 2.0 g/10 min @Load 5.00 kg, Temperature 372 °C |
2.0 g/10 min @Load 11.0 lb, Temperature 702 °F |
ASTM D1238 |
3M Dyneon™ PFA 6502N Perfluoroalkoxy Fluorothermoplastic
(discontinued **) The excellent chemical temperature resistance of Dyneon™ 6500N PFA is available across a range of melt flow indices, for optimal processability. Dyneon™ PFA 6502N, the highest molecular weight gra.. |
|||
Melt Index of Compound | 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
ICO Polymers ICORENEâ„¢ 150-1334 LMDPE Rotational Molding Resin Description: ICORENE 150-1334 is a linear medium density polyethylene developed for use in rotational molding. It has very high stiffness, toughness, and scratch resistance combined with good proce.. |
|||
Melt Index of Compound | 2.0 g/10 min @Load 3.80 kg, Temperature 230 °C |
2.0 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D1238 |
LG Chemical IH830C PMMA, General Purpose Grade for Injection Molding Highest of all grades in heat resistanceMechanical strength and surface hardnessParticularly recommended for tail lamp, reflectors, and general lighting fixturesFeatures: Excellent transparency and .. |
|||
Melt Index of Compound | 2.0 - 9.0 g/10 min @Temperature 190 °C |
2.0 - 9.0 g/10 min @Temperature 374 °F |
P=49, 1 H |
Sibur DST-45 RM Styrene-Butadiene-Styrene Block Copolymer (SBS-TPE) Kraton D 4271. For production of footwear compositions. |
|||
Melt Index of Compound | 2.0 - 7.0 g/10 min | 2.0 - 7.0 g/10 min | |
Sibur L-85M Polyvinyl Chloride (PVC) For use in the footwear industry for production of shoe soles. |
|||
Melt Index of Compound | 2.0 g/10 min @Load 5.00 kg, Temperature 280 °C |
2.0 g/10 min @Load 11.0 lb, Temperature 536 °F |
MVR [cm^3/10 min]; ISO 1133 |
SABIC Innovative Plastics NORYL PX138H PPE+HIPS (Asia Pacific) Modified PPO Resin with 20% Glass Fibre Reinforced |
|||
Melt Index of Compound | 2.0 g/10 min | 2.0 g/10 min | Condition E; ASTM D1238 |
A. Schulman CP763-01 Extruded, Blow Molding and Injection Molding Grade Polyethylene DescriptionCP 763-01 is an extruded, blow molding, and injection molding grade of low density polyethylene having good processability and heat sealability. ApplicationCP 763-01 meets the specificat.. |
|||
Melt Index of Compound | 2.0 g/10 min | 2.0 g/10 min | Condition E; ASTM D1238 |
A. Schulman CP763-01 Extruded, Blow Molding and Injection Molding Grade Polyethylene DescriptionCP 763-01 is an extruded, blow molding, and injection molding grade of low density polyethylene having good processability and heat sealability. ApplicationCP 763-01 meets the specificat.. |
|||
Melt Index of Compound | 2.0 g/10 min | 2.0 g/10 min | Condition E; ASTM D1238 |
A. Schulman CP763-01 Extruded, Blow Molding and Injection Molding Grade Polyethylene DescriptionCP 763-01 is an extruded, blow molding, and injection molding grade of low density polyethylene having good processability and heat sealability. ApplicationCP 763-01 meets the specificat.. |
|||
Melt Index of Compound | 2.0 g/10 min | 2.0 g/10 min | Condition E; ASTM D1238 |
A. Schulman CP763-01 Extruded, Blow Molding and Injection Molding Grade Polyethylene DescriptionCP 763-01 is an extruded, blow molding, and injection molding grade of low density polyethylene having good processability and heat sealability. ApplicationCP 763-01 meets the specificat.. |
|||
Melt Index of Compound | 2.0 g/10 min | 2.0 g/10 min | ASTM D1238 |
A. Schulman LP552-01 Injection Molding, Extrusion Grade Compound DescriptionLP 522-01 is an injection molding and/or extrusion grade compoundApplicationLP 552-01 meets FDA Regulation CFT 177.1520(c)3.1.Information provided by A. Schulman. |
|||
Melt Index of Compound | 2.0 g/10 min | 2.0 g/10 min | ASTM D1238 |
A. Schulman LP552-01 Injection Molding, Extrusion Grade Compound DescriptionLP 522-01 is an injection molding and/or extrusion grade compoundApplicationLP 552-01 meets FDA Regulation CFT 177.1520(c)3.1.Information provided by A. Schulman. |
|||
Melt Index of Compound | 2.0 g/10 min | 2.0 g/10 min | Condition E; ASTM D1238 |
A. Schulman CP763-01 Extruded, Blow Molding and Injection Molding Grade Polyethylene DescriptionCP 763-01 is an extruded, blow molding, and injection molding grade of low density polyethylene having good processability and heat sealability. ApplicationCP 763-01 meets the specificat.. |
|||
Melt Index of Compound | 2.0 g/10 min | 2.0 g/10 min | ASTM D1238 |
A. Schulman LP552-01 Injection Molding, Extrusion Grade Compound DescriptionLP 522-01 is an injection molding and/or extrusion grade compoundApplicationLP 552-01 meets FDA Regulation CFT 177.1520(c)3.1.Information provided by A. Schulman. |
|||
Melt Index of Compound | 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D-1238 |
Chevron Phillips Marlex® HMN TR-942/942G Polyethylene; HDPE High density polyethylene. These hexene copolymers are tailored for rotational molding applications that require: Wide process windows and fair flowLong-term UV stabilizationExcellent impact stren.. |
|||
Melt Index of Compound | 2.0 g/10 min @Load 5.00 kg, Temperature 372 °C |
2.0 g/10 min @Load 11.0 lb, Temperature 702 °F |
ASTM D1238 |
3M Dyneon™ PFA FLEX 8502 UHPZ Perfluoroalkoxy Fluorothermoplastic Granules Dyneon™ PFA-FLEX UHP family exhibits improved environmental stress crack resistance to stress cracking agents such as fluorsurfactants and fluorosurfactant-containing chemicals. In addition, this f.. |
|||
Melt Index of Compound | 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
2.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
Arkema Group OREVAC® PPC Grafted Maleic Anhydride Polypropylene OREVAC PPC is a grafted maleic anhydride polypropylene used in the manufacturing of multilayer oxygen barrier tube. OREVAC PPC is mainly used in multi-layer tube to have good adhesion between PP, PA.. |
|||
Melt Index of Compound | 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
2.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
Dow H110-02NZ Polypropylene Homopolymer Resin OverviewContains a nucleating agentGood melt strengthComplies with U.S. FDA 21 CFR 177.1520 (c)3.2aDOW H110-02NZ Polypropylene Resin is intended for use in extrusion and thermoforming processes in o.. |
|||
Melt Index of Compound | 2.0 g/10 min @Temperature 190 °C |
2.0 g/10 min @Temperature 374 °F |
ASTM D1238 |
Mitsui ADMER® NF518A PE Type Polyolefin ADMER® Adhesive Resin is a modified polyolefin with functional groups, designed to bond to a variety of polyolefins, ionomers, polyamides, ethylene vinyl alcohol (EVOH), polyesters (PET), polycarbo.. |