Physical Properties | Metric | English | Comments |
---|---|---|---|
Melt Index of Compound | 1.3 g/10 min @Load 2.16 kg, Temperature 230 °C |
1.3 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
3M Dyneon™ PVDF 6020/1001 Polyvinylidene Fluoride
(discontinued **) Ultra-high molecular weight grade PVDFPowder gradeExcellent chemical resistance to a wide variety of aggressive fluids and solventsGood permeation resistanceExcellent strength and dimensional stabil.. |
|||
Melt Index of Compound | 1.3 g/10 min @Load 3.80 kg, Temperature 230 °C |
1.3 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D1238 |
Lendell Parapet GR-00100 PMMA, High Impact |
|||
Melt Index of Compound | 1.3 g/10 min | 1.3 g/10 min | |
Lushan PA6+30% GF Nylon Toughener/PA Impact Modifier Nylon toughener/PA impact modifier Lushan series is a maleic anhydride grafted polyolefin elastomer, with a very low residual maleic anhydride monomer, no irritating odor when using. Nylon toughener.. |
|||
Melt Index of Compound | 1.3 - 2.5 g/10 min | 1.3 - 2.5 g/10 min | |
Sibur ABS 2802 Extrusion Grade ABS Plastic With high deformation properties and impact strength for production of sheets with following pneumatic and vacuum forming of products of technical purpose. |
|||
Melt Index of Compound | 1.3 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.3 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D-1238 |
Chevron Phillips MarFlex® 2121 Polyethylene; LDPE Low density polyethylene. This LDPE is tailored for cast film applications that require: Good processabilityGood drawdownEdge tear resistanceLow neck-in Applications: Typical cast film applicatio.. |
|||
Melt Index of Compound | 1.3 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.3 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
Dow FLEXOMER™ DFDA-1095 NT Very Low Density Polyethylene (VLDPE) Resin FLEXOMER™ DFDA-1095 NT is an ethylene-butene copolymer with a unique olefinic composition for improved process-ability and material handling. This product is produced via gas phase polymerization .. |