Physical Properties | Metric | English | Comments |
---|---|---|---|
Linear Mold Shrinkage, Transverse | 0.0015 - 0.0035 cm/cm @Thickness 3.20 mm |
0.0015 - 0.0035 in/in @Thickness 0.126 in |
SABIC Method |
SABIC Innovative Plastics Lexan® JK2000 PC+ABS (Asia Pacific) Lexan* JK2000 compound is a glass reinforced, non-Br and non-Cl FR polycarbonate blends designed for thinwall molding applications. |
|||
Linear Mold Shrinkage, Transverse | 0.0015 - 0.0035 cm/cm @Thickness 3.20 mm |
0.0015 - 0.0035 in/in @Thickness 0.126 in |
SABIC Method |
SABIC Innovative Plastics Lexan® LGK3020 PC (Asia Pacific) Glass reinforced. Flame retardant. |
|||
Linear Mold Shrinkage, Transverse | 0.0025 - 0.0035 cm/cm | 0.0025 - 0.0035 in/in | Test Condition: 150x105x3; acc. ISO 2577 |
Ineos ABS Lustran® SAN GF20 Glass Fiber Reinforced |
|||
Linear Mold Shrinkage, Transverse | 0.0020 - 0.0035 cm/cm | 0.0020 - 0.0035 in/in | |
LATI Lastil G/25-V0 SAN, 25% Glass Fiber Reinforced, Flame Retardant Styrene-Acrylonitrile copolymer (SAN) based compound. Glass fibers. UL94 V-0 classified, with brominated flame retardants. Very high dimensional stability.Availability: Africa & Middle East; Asia Pa.. |
|||
Linear Mold Shrinkage, Transverse | 0.0020 - 0.0035 cm/cm | 0.0020 - 0.0035 in/in | Test Condition: 150x105x3; acc. ISO 2577 |
Ineos ABS Lustran® SAN GF30 Glass Fiber Reinforced |
|||
Linear Mold Shrinkage, Transverse | 0.0020 - 0.0035 cm/cm | 0.0020 - 0.0035 in/in | |
LATI Latilon 28D K/20 PC, 20% Carbon Fiber Reinforced Polycarbonate (PC) based compound. Carbon fiber. Low smoke density and low toxicity index.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided b.. |
|||
Linear Mold Shrinkage, Transverse | 0.0015 - 0.0035 cm/cm @Thickness 3.20 mm |
0.0015 - 0.0035 in/in @Thickness 0.126 in |
SABIC Method |
SABIC Innovative Plastics LNP LUBRICOMP Lexan_LF1530A PC LNP* Lubricomp* Lexan_LF1530A compound is a 30% glass reinforced, 15% PTFE filled PC. Flame retardant and wear resistant. Tight tolerances. |
|||
Linear Mold Shrinkage, Transverse | 0.0015 - 0.0035 cm/cm @Thickness 3.20 mm |
0.0015 - 0.0035 in/in @Thickness 0.126 in |
SABIC Method |
SABIC Innovative Plastics LNP LUBRICOMP Lexan_LF1530A PC (Europe-Africa-Middle East) LNP* Lubricomp* Lexan_FL1530 compound is a 30% glass reinforced, 15% PTFE filled PC. Flame retardant and wear resistant. Tight tolerances. |
|||
Linear Mold Shrinkage, Transverse | 0.0015 - 0.0035 cm/cm @Thickness 3.20 mm |
0.0015 - 0.0035 in/in @Thickness 0.126 in |
SABIC Method |
SABIC Innovative Plastics LNP STAT-KON Noryl_FMC3008A PPE+HIPS (Europe-Africa-Middle East) LNP* Stat-kon* Noryl_FMC3008A compound is a 30% carbon fiber/glass/mineral filled, static dissipative, foamable resin. UL94 V1 rated. Property values at 20% weight reduction, 0.250"" wall. |
|||
Linear Mold Shrinkage, Transverse | 0.0015 - 0.0035 cm/cm @Thickness 3.20 mm |
0.0015 - 0.0035 in/in @Thickness 0.126 in |
SABIC Method |
SABIC Innovative Plastics LNP STAT-KON Noryl_FMC3008A PPE+PS LNP* Stat-kon* Noryl_FMC3008A compound is a 30% carbon fiber/glass/mineral filled, static dissipative, foamable resin. UL94 V1 rated. Property values at 20% weight reduction, 0.250"" wall. |
|||
Linear Mold Shrinkage, Transverse | 0.0015 - 0.0035 cm/cm @Thickness 3.20 mm |
0.0015 - 0.0035 in/in @Thickness 0.126 in |
SABIC Method |
SABIC Innovative Plastics LNP THERMOCOMP Lexan_JK2000 PC+ABS LNP* Thermocomp* Lexan_JK2000 compound is a 22% GR, ECO-compliant FR, PC+ABS for thinwall molding applications. |
|||
Linear Mold Shrinkage, Transverse | 0.0015 - 0.0035 cm/cm @Thickness 3.20 mm |
0.0015 - 0.0035 in/in @Thickness 0.126 in |
SABIC Method |
SABIC Innovative Plastics LNP THERMOCOMP Lexan_LGK3020 PC LNP* Thermocomp* Lexan_LGK3020 compound is a glass reinforced. Flame retardant. |
|||
Linear Mold Shrinkage, Transverse | 0.0015 - 0.0035 cm/cm @Thickness 3.20 mm |
0.0015 - 0.0035 in/in @Thickness 0.126 in |
SABIC Method |
SABIC Innovative Plastics LNP THERMOCOMP Lexan_LGK3020 PC (Europe-Africa-Middle East) LNP* Thermocomp* Lexan_LGK3020 compound is a glass reinforced, flame retardant material. |
|||
Linear Mold Shrinkage, Transverse | 0.0015 - 0.0035 cm/cm @Thickness 3.20 mm |
0.0015 - 0.0035 in/in @Thickness 0.126 in |
SABIC Method |
SABIC Innovative Plastics LNP THERMOCOMP Lexan_LGK3020 PC (Asia Pacific) Glass reinforced. Flame retardant. |