Physical Properties | Metric | English | Comments |
---|---|---|---|
Linear Mold Shrinkage, Transverse | 0.0065 cm/cm | 0.0065 in/in | |
Plastcom SLOVALEN PH 92 T 40 PP, 40% mineral filling FeaturesModified homopolymer PP for injection moulding with the content of 40% microground, floated, chemically modified talc. Stable towards oxidants. General application in all industry branches -.. |
|||
Linear Mold Shrinkage, Transverse | 0.0065 cm/cm | 0.0065 in/in | |
Plastcom SLOVASTER® C FRU 2 PBT, flame retarder FeaturesPC with the flame retardant on the basis of bromine hydrocarbons. Anisotropy of shrinkage enables the injection moulding of round, cylindrical or other hole products. Application in engineer.. |
|||
Linear Mold Shrinkage, Transverse | 0.0065 - 0.0085 cm/cm | 0.0065 - 0.0085 in/in | |
LATI Kelon® B FR H2 CE/25-V2HF PA 6, Mineral Reinforced, Flame Retardant, Heat Stabilized Polyamide 6 (PA6) based compound. Heat stabilized. Mineral filler. UL94 V-2 classified, halogens-based flame retardants and red phosphorous free.Availability: Africa & Middle East; Asia Pacific; Eur.. |
|||
Linear Mold Shrinkage, Transverse | 0.0065 - 0.0085 cm/cm | 0.0065 - 0.0085 in/in | |
LATI Latamid 12 CP/85 PA 12 Polyamide 12 (PA12) based compound. Special filler.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A. |
|||
Linear Mold Shrinkage, Transverse | 0.0065 - 0.0090 cm/cm | 0.0065 - 0.0090 in/in | |
LATI Latamid 6 H2 G/30-V0HF1 PA 6, 30% Glass Fiber Reinforced, Heat Stabilized, Flame Retardant Polyamide 6 (PA6) based compound. Heat stabilized. Glass fibers. UL94 V-0 classified, halogens-based flame retardants and red phosphorous free. Very good electrical properties.Availability: Africa &.. |
|||
Linear Mold Shrinkage, Transverse | 0.0065 - 0.0095 cm/cm | 0.0065 - 0.0095 in/in | |
LATI Latamid 66 E21 K/30 PA 66, 30% Carbon Fiber Reinforced Polyamide 66 (PA66) based compound. Toughened. Carbon fibers.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastic.. |
|||
Linear Mold Shrinkage, Transverse | 0.0065 - 0.0095 cm/cm | 0.0065 - 0.0095 in/in | |
LATI Latamid 66 H2 G/50 PA 66, 50% Glass Fiber Reinforced, Heat Stabilized Polyamide 66 (PA66) based compound. Heat stabilized. Glass fibers.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termopl.. |
|||
Linear Mold Shrinkage, Transverse | 0.0065 - 0.0095 cm/cm | 0.0065 - 0.0095 in/in | |
LATI Latamid 66 H2 G/50-V0KB1 PA 66, 50% Glass Fiber Reinforced, Heat Stabilized, Flame Retardant Polyamide 66 (PA66) based compound. Heat stabilized. Glass fibers. UL94 V-0 classified, with red phosphorous.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInf.. |
|||
Linear Mold Shrinkage, Transverse | 0.0065 - 0.0095 cm/cm | 0.0065 - 0.0095 in/in | |
LATI Latilub 66-01M G/50 PA66, 50% Glass Fiber Reinforced, Molybdenum disulphide Filled Self-lubricating product based on Polyamide 66 (PA66). Molybdenum disulphide. Glass fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided.. |
|||
Linear Mold Shrinkage, Transverse | 0.0065 - 0.0080 cm/cm | 0.0065 - 0.0080 in/in | |
LATI Latilub 85-10T G/30 PES, 30% Glass Fiber Reinforced, PTFE Filled Self-lubricating product based on Polyether Sulfone (PES). PTFE. Glass fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Indu.. |
|||
Linear Mold Shrinkage, Transverse | 0.0065 - 0.0095 cm/cm | 0.0065 - 0.0095 in/in | |
LATI Latiohm 62-03 PD01 G/20 PPA, 20% Glass Fiber Reinforced Semiconductive/dissipative product based on Polyamide 6 (PA6). Glass fibers.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Indust.. |
|||
Linear Mold Shrinkage, Transverse | 0.0065 - 0.0090 cm/cm | 0.0065 - 0.0090 in/in | |
LATI Latiohm 63-08 PD02 G/25 PA6, 25% Glass Fiber Reinforced Dissipative product based on Polyamide 6 (PA6), impact modified. Glass fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Ind.. |
|||
Linear Mold Shrinkage, Transverse | 0.0065 - 0.0090 cm/cm | 0.0065 - 0.0090 in/in | |
LATI Latiohm 80-04 PD01 G/30 PPS, 30% Glass Fiber Reinforced Semiconductive/dissipative product based on Polyphenylene Sulfide (PPS). Glass fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by.. |
|||
Linear Mold Shrinkage, Transverse | 0.0065 cm/cm @Time 86400 sec |
0.0065 in/in @Time 24.0 hour |
ASTM D955 |
SABIC Innovative Plastics NORYL WCP921 PPE-TPE Flexible Noryl* injection molding grade. Low specific gravity with good non-halogenated flame retardant performance. Developed for evaluation in overmolding applications such as plugs, strain relief.. |
|||
Linear Mold Shrinkage, Transverse | 0.0065 cm/cm @Thickness 3.20 mm |
0.0065 in/in @Thickness 0.126 in |
ASTM D955 |
Samsung Cheil Industries Starex® LX-0989EXS ABS, Unreinforced Metallic-Look Luminous Grade - gives aesthetics of a painted surface without painting. Reduces time, cost, and environmental hazards (such as soilvents).Information provided by Samsung Cheil Industries. |
|||
Linear Mold Shrinkage, Transverse | 0.0065 - 0.0085 cm/cm @Thickness 3.20 mm |
0.0065 - 0.0085 in/in @Thickness 0.126 in |
SABIC Method |
SABIC Innovative Plastics NORYL GTX GTX820 PPE+PS+PA (Asia Pacific) GR 20%. Higher stiffness of 800000 psi (4000 MPa) flexural modulus. Excellent chemical and high heat resistance. Application: valves. |
|||
Linear Mold Shrinkage, Transverse | 0.0065 - 0.0085 cm/cm @Thickness 3.20 mm |
0.0065 - 0.0085 in/in @Thickness 0.126 in |
SABIC Method |
SABIC Innovative Plastics NORYL GTX GTX830 PPE+PS+PA 30% Glass Reinforced PPE+PA Alloy. |
|||
Linear Mold Shrinkage, Transverse | 0.0065 - 0.0085 cm/cm @Thickness 3.20 mm |
0.0065 - 0.0085 in/in @Thickness 0.126 in |
SABIC Method |
SABIC Innovative Plastics NORYL GTX GTX830 PPE+PS+PA (Asia Pacific) GR 30%. Highest stiffness of 1200000 psi (8200 MPa) flexural modulus. Excellent chemical and high heat resistance. Application: under the bonnet. |
|||
Linear Mold Shrinkage, Transverse | 0.0065 - 0.0080 cm/cm @Thickness 3.20 mm |
0.0065 - 0.0080 in/in @Thickness 0.126 in |
SABIC Method |
SABIC Innovative Plastics NORYL GTX GTX8730 PPE+PA (Asia Pacific) Noryl GTX* GTX8730 resin is a glass filled, high performance blend of PPE/PA that exhibits an excellent balance of high-heat resistance, strength, flow, and conductivity. This grade can be electro-s.. |
|||
Linear Mold Shrinkage, Transverse | 0.0065 - 0.0085 cm/cm @Thickness 3.20 mm |
0.0065 - 0.0085 in/in @Thickness 0.126 in |
SABIC Method |
SABIC Innovative Plastics NORYL GTX GTX810 PPE+PS+PA (Asia Pacific) GR 10%. Increased stiffness of 200000 psi (3000 MPa) flexural modulus. Excellent chemical and high heat resistance. Application: lighting. |
|||
Linear Mold Shrinkage, Transverse | 0.0065 cm/cm @Thickness 2.00 mm |
0.0065 in/in @Thickness 0.0787 in |
60x60x2 mm; 500 bar; ISO 294-4 |
Covestro Makrolon® 2258 Polycarbonate Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• Medical devices - bioc.. |
|||
Linear Mold Shrinkage, Transverse | 0.0065 cm/cm @Thickness 2.00 mm |
0.0065 in/in @Thickness 0.0787 in |
60x60x2 mm; 500 bar; ISO 294-4 |
Covestro Makrolon® 2405 MAS048 Polycarbonate Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• General purpose• Low.. |
|||
Linear Mold Shrinkage, Transverse | 0.0065 cm/cm @Thickness 2.00 mm |
0.0065 in/in @Thickness 0.0787 in |
60x60x2 mm; 500 bar; ISO 294-4 |
Covestro Makrolon® Rx2435 Polycarbonate Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• Medical devices• Low.. |
|||
Linear Mold Shrinkage, Transverse | 0.0065 cm/cm | 0.0065 in/in | ISO 2577 |
BASF Ultramid® B3WG6 HP BK 23210 30% Glass Filled PA6 (Dry) Description: 30% Glass fiber reinforced and heat aging resistant injection molding grade with enhances flowability used e.g. for automobile manifold.Information provided by BASF |
|||
Linear Mold Shrinkage, Transverse | 0.0065 cm/cm | 0.0065 in/in | LATI |
LATI LARTON G/30 30% Glass Fiber Filled Polyphenylene sulfide (PPS)
(discontinued **) Description: Larton thermoplastics are polyphenylene sulfide (PPS) products. They are distinguished by a group of very interesting properties combined with easy moldability. Larton parts feature: ex.. |
|||
Linear Mold Shrinkage, Transverse | 0.0065 - 0.0095 cm/cm | 0.0065 - 0.0095 in/in | |
LATI Latiohm 66-04 PD01 G/25-V0CT1 PA66, 25% Glass Fiber Reinforced, Flame Retardant Semiconductive/dissipative product based on Polyamide 66 (PA66). Glass fibers. UL94 V-0 classified, with brominated flame retardants, PBB/PBDE free. Availability: Africa & Middle East; Asia Pacific;.. |
|||
Linear Mold Shrinkage, Transverse | 0.0065 cm/cm | 0.0065 in/in | |
Solvay TECHNYL® 1021GF6 PA6, 30% glass fiber, DRY Description: Polyamide 6, 30% glass fiber reinforced, for injection molding.Available in: Asia Pacific Product Applications: TECHNYL® 1021GF6 is used in all sectors of industry, offering an excelle.. |
|||
Linear Mold Shrinkage, Transverse | 0.0065 cm/cm | 0.0065 in/in | |
Kuraray Genestar™ GR2300 Nylon, 30% Glass Filled Standard V-0 Grade. Delivers increased fluidity and weld strength. Well suited for a wide range of electrical and electronic components. |