Physical Properties | Metric | English | Comments |
---|---|---|---|
Linear Mold Shrinkage, Flow | 0.00 - 0.0010 cm/cm @Thickness 3.20 mm |
0.00 - 0.0010 in/in @Thickness 0.126 in |
SABIC Method |
SABIC Innovative Plastics Geloy EXGY30CP ASA Pearlescent GELOY ASA resin with copper-look for capstock extrusion. Outstanding weatherability.This data was supplied by SABIC-IP for the Americas region. |
|||
Linear Mold Shrinkage, Flow | 0.00 - 0.0010 cm/cm @Thickness 3.20 mm |
0.00 - 0.0010 in/in @Thickness 0.126 in |
SABIC Method |
SABIC Innovative Plastics Geloy FXTW30PE ASA Pearlescent GELOY ASA resin with copper-look for capstock extrusion. Outstanding weatherability.This data was supplied by SABIC-IP for the Americas region. |
|||
Linear Mold Shrinkage, Flow | 0.00 - 0.0010 cm/cm @Thickness 3.20 mm |
0.00 - 0.0010 in/in @Thickness 0.126 in |
SABIC Method |
SABIC Innovative Plastics Geloy FXTW30CP ASA Pearlescent GELOY ASA resin with copper-look for capstock extrusion. Outstanding weatherability.This data was supplied by SABIC-IP for the Americas region. |
|||
Linear Mold Shrinkage, Flow | 0.00030 - 0.0010 cm/cm | 0.00030 - 0.0010 in/in | Internal Method |
Solvay Specialty Polymers Ixef® 3008 Polyarylamide (PARA)
(Unverified Data**) Ixef 3008 is a 30% carbon-fiber reinforced polyarylamide compound which exhibits extremely high strength and stiffness, good surface gloss, excellent creep resistance, and lower density than glass-f.. |
|||
Linear Mold Shrinkage, Flow | 0.00020 - 0.0010 cm/cm | 0.00020 - 0.0010 in/in | ASTM D955 |
PolyOne LubriOne™ NJ-30CF/15T-2S Nylon 12
(discontinued **) LubriOne™ Lubricated and Wear-Resistant Compounds have been specifically formulated to be self-lubricating materials, offering low coefficient of friction and improved wear resistance properties. L.. |
|||
Linear Mold Shrinkage, Flow | 0.00050 - 0.0010 cm/cm @Time 86400 sec |
0.00050 - 0.0010 in/in @Time 24.0 hour |
ISO 294 |
SABIC Innovative Plastics LNP LUBRICOMP OCL36XXP PPS - Linear (Europe-Africa-Middle East) LNP* LUBRICOMP* OCL36XXP is a compound based on PPS- Linear resin containing PTFE, Carbon Fiber. Added features include : Internally Lubricated, Electrically Conductive . |
|||
Linear Mold Shrinkage, Flow | 0.00030 - 0.0010 cm/cm | 0.00030 - 0.0010 in/in | ISO 294-4 |
Solvay Specialty Polymers Ixef® 3008 Polyarylamide (PARA), 30% Carbon Fiber Ixef® 3008 is a 30% carbon-fiber reinforced polyarylamide compound which exhibits extremely high strength and stiffness, good surface gloss, excellent creep resistance, and lower density than gla.. |
|||
Linear Mold Shrinkage, Flow | 0.00080 - 0.0010 cm/cm @Time 86400 sec |
0.00080 - 0.0010 in/in @Time 24.0 hour |
ASTM D 955 |
SABIC Innovative Plastics LNP Stat-kon DEL369E PC (Asia Pacific) LNP* Stat-Kon* DEL369E is a Polycarbonate with Carbon Fiber and PTFE. Characteristics of this grade are Flame Retardant.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
Linear Mold Shrinkage, Flow | 0.00020 - 0.0010 cm/cm @Time 86400 sec |
0.00020 - 0.0010 in/in @Time 24.0 hour |
ASTM D 955 |
SABIC Innovative Plastics LNP Stat-kon EE008E PEI (Asia Pacific) LNP STAT-KON* EE008E is a compound based on Polyetherimide resin containing Carbon Fiber. Added features of this material include: Easy Molding.This data was supplied by SABIC-IP for the Asia Pacif.. |
|||
Linear Mold Shrinkage, Flow | 0.00030 - 0.0010 cm/cm @Time 86400 sec |
0.00030 - 0.0010 in/in @Time 24.0 hour |
ASTM D955 |
SABIC Innovative Plastics LNP THERMOCOMP EC006PXQ PEI LNP* THERMOCOMP* EC006PXQ is a compound based on Polyetherimide containing 30% Carbon FIber. Added features include: Electrically Conductive, Easy Molding. |
|||
Linear Mold Shrinkage, Flow | 0.00080 - 0.0010 cm/cm @Time 86400 sec |
0.00080 - 0.0010 in/in @Time 24.0 hour |
ASTM D955 |
SABIC Innovative Plastics LNP STAT-KON OE006C1 PPS - Linear LNP* STAT-KON* OE006C1 is a compound based on PPS - Linear resin containing 30% Carbon Fiber. Added features of this material include: Electrically Conductive. |
|||
Linear Mold Shrinkage, Flow | 0.00030 - 0.0010 cm/cm @Time 86400 sec |
0.00030 - 0.0010 in/in @Time 24.0 hour |
ASTM D 955 |
SABIC Innovative Plastics LNP Lubricomp DCL36 PC LNP LUBRICOMP* DCL36 is a compound based on Polycarbonate resin containing Carbon Fiber, PTFE. Added features of this material include: Electrically Conductive.This data was supplied by SABIC-IP fo.. |