Physical Properties | Metric | English | Comments |
---|---|---|---|
Linear Mold Shrinkage, Flow | 0.0025 cm/cm | 0.0025 in/in | ISO 294-4 |
Radici Raditer® B RVA 300 Polybutylene Terephthalate with 30% Glass fiber Raditer® B RVA is a range of glass fiber reinforced Polybutylene terephthalate blends for injection molding, with excellent dimensional stability, low warpage and good surface aspect.Information pr.. |
|||
Linear Mold Shrinkage, Flow | 0.0025 - 0.0035 cm/cm @Thickness 3.20 mm |
0.0025 - 0.0035 in/in @Thickness 0.126 in |
SABIC Method |
SABIC Innovative Plastics Cycoloy® C7230P PC+ABS (Asia Pacific) Cycoloy* C7230P resin is a mineral filled, flame retardant PC/ABS. Good stiffness combined with balanced flow and impact performance, makes it a good candidate for various applications. |
|||
Linear Mold Shrinkage, Flow | 0.0025 cm/cm | 0.0025 in/in | ASTM D955 |
Solvay Specialty Polymers Mindel® B-430 Polysulfone, Modified (PSU, Modified)
(discontinued **) Mindel B-430 is a 30% glass reinforced thermoplastic with excellent dimensional stability, exceptional resistance to warp, good chemical resistance, and high stiffness. It was developed specifically.. |
|||
Linear Mold Shrinkage, Flow | 0.0025 - 0.0040 cm/cm | 0.0025 - 0.0040 in/in | |
LATI Kelon® B FR H2 CEG/500-V0CT3 PA 6, Glass/Mineral Reinforced, Flame Retardant, Heat Stabilized Polyamide 6 (PA6) based compound. Heat stabilized. Glass fibers / Mineral filler. UL94 V-0 classified, with brominated flame retardants, PBB/PBDE and antimony trioxide free. Low thermal expansion co.. |
|||
Linear Mold Shrinkage, Flow | 0.0025 - 0.0040 cm/cm | 0.0025 - 0.0040 in/in | |
LATI Larton L G/40 L-PPS, 40% Glass Fiber Reinforced Linear Polyphenylene Sulfide (L-PPS) based compound. Glass fibers. Very good chemical resistance. Very good thermal properties. Low smoke density and low toxicity index.Availability: Africa & Middle.. |
|||
Linear Mold Shrinkage, Flow | 0.0025 - 0.0045 cm/cm | 0.0025 - 0.0045 in/in | |
LATI Latamid 66 E21 K/30 PA 66, 30% Carbon Fiber Reinforced Polyamide 66 (PA66) based compound. Toughened. Carbon fibers.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastic.. |
|||
Linear Mold Shrinkage, Flow | 0.0025 - 0.0045 cm/cm | 0.0025 - 0.0045 in/in | |
LATI Latamid 66 B G/20-V PA 66, 20% Glass Fiber Reinforced, Heat Stabilized, Flame Retardant Polyamide 66 (PA66) based compound. High fluidity. Glass fibers. Flame retardant, non classifiable, with brominated flame retardants, PBB/PBDE free. Availability: Africa & Middle East; Asia Pacific;.. |
|||
Linear Mold Shrinkage, Flow | 0.0025 - 0.0040 cm/cm | 0.0025 - 0.0040 in/in | |
LATI Laticonther 62 GR/70 PA 6, 70% Graphite Reinforced High thermal conductivity product based on Polyamide 6 (PA6). Graphite.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Te.. |
|||
Linear Mold Shrinkage, Flow | 0.0025 cm/cm | 0.0025 in/in | on Tensile Bar; SABIC Method |
SABIC Innovative Plastics ULTEM 3452 PEI (Europe-Africa-Middle East) 45% Glass fiber and mineral filled, enhanced flow Polyetherimide (Tg 217C) with enhanced dimensional stability. Resin is RoHS compliant. UL94 V0 and 5VA listing in recognized colors. |
|||
Linear Mold Shrinkage, Flow | 0.0025 cm/cm @Thickness 3.17 mm |
0.0025 in/in @Thickness 0.125 in |
ASTM D955 |
Techmer ES HiFill® PA6 GF50 HS UV BK 50% Glass Filled (Conditioned) Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 50% Filler by WeightAdditive: Lubricant, UV Stabilizer and Heat StabilizerFeatures: Lubricated, Good UV Resi.. |
|||
Linear Mold Shrinkage, Flow | 0.0025 cm/cm @Thickness 3.17 mm |
0.0025 in/in @Thickness 0.125 in |
ASTM D955 |
Techmer ES HiFill® PA6 GF50 L LE 50% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 50% Filler by WeightAdditive: LubricantFeatures: Low Extractables and LubricatedAppearance: Natural ColorInf.. |
|||
Linear Mold Shrinkage, Flow | 0.0025 cm/cm @Thickness 3.17 mm |
0.0025 in/in @Thickness 0.125 in |
ASTM D955 |
Techmer ES HiFill® PA6/6 GF33 SF L 33% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 33% Filler by WeightAdditive: Lubricant and Strontium FerriteFeatures: LubricatedInformation provided by TP .. |
|||
Linear Mold Shrinkage, Flow | 0.0025 - 0.0045 cm/cm | 0.0025 - 0.0045 in/in | on Tensile Bar; SABIC Method |
SABIC Innovative Plastics LNP THERMOCOMP DF004ER PC (Europe-Africa-Middle East) LNP* Thermocomp* DF004ER is a compound based on Polycarbonate resin containing Glass Fiber. Added features of this material include: Easy Molding, Mold Release. |
|||
Linear Mold Shrinkage, Flow | 0.0025 cm/cm | 0.0025 in/in | GB/T 15585-1995 |
Sichuan Deyang Haton® hGR40DL Polyphenylene Sulfide, Glass Fiber Reinforced Injection molding, low chlorineInformation provided by Sichuan Deyang Chemical Co., LTD |
|||
Linear Mold Shrinkage, Flow | 0.0025 cm/cm | 0.0025 in/in | SABIC Method |
SABIC Innovative Plastics LNP THERMOCOMP PX94085 PA 6 (Europe-Africa-Middle East) LNP* THERMOCOMP* PX94085 is a compound based on PA6 resin, containing Glass Fiber. |
|||
Linear Mold Shrinkage, Flow | 0.0025 - 0.0030 cm/cm @Thickness 3.20 mm |
0.0025 - 0.0030 in/in @Thickness 0.126 in |
SABIC Method |
SABIC Innovative Plastics NORYL HFM3015P PPE+PS (Asia Pacific) 30% GF/MF filled FR PPE/PS blend |
|||
Linear Mold Shrinkage, Flow | 0.0025 cm/cm @Thickness 3.17 mm |
0.0025 in/in @Thickness 0.125 in |
ASTM D955 |
Techmer ES HiFill® PPS F GF/M55 BK 55% Glass/Mineral Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass/Mineral, 55% Filler by WeightAppearance: BlackInformation provided by TP Composites, Inc. |
|||
Linear Mold Shrinkage, Flow | 0.0025 cm/cm @Time 86400 sec |
0.0025 in/in @Time 24.0 hour |
ISO 294 |
SABIC Innovative Plastics LNP THERMOCOMP UFW49S PPA (Asia Pacific) LNP* Thermocomp* UFW49S is a compound based on Polyphthalamide resin containing Glass Fiber, Mineral. Added features of this material include: Heat Stabilized, Low Warpage. |
|||
Linear Mold Shrinkage, Flow | 0.0025 - 0.0035 cm/cm @Thickness 3.20 mm |
0.0025 - 0.0035 in/in @Thickness 0.126 in |
SABIC Method |
SABIC Innovative Plastics NORYL CN1134 PPE+PS (Asia Pacific) 20% filled FR high modulus PPE/PS blend |
|||
Linear Mold Shrinkage, Flow | 0.0025 cm/cm | 0.0025 in/in | |
Solvay TECHNYL® 2912GMH7-P PA66, 63% glass fiber, DRY Description: Polyamide 66, reinforced with 63% of glass fiber for injection molding.Available in: Asia PacificProduct Applications: TECHNYL® 2912GMH7-P is used in all sectors of industry, offerin.. |
|||
Linear Mold Shrinkage, Flow | 0.0025 - 0.0055 cm/cm | 0.0025 - 0.0055 in/in | ISO DIS 294-4 |
Wellman Wellamid® GF1758-BK2 33% Glass Fiber Reinforced Nylon 66 Description: Glass Fiber Reinforced Nylon 66Information provided by Wellman. |
|||
Linear Mold Shrinkage, Flow | 0.0025 cm/cm | 0.0025 in/in | Annealed; ISO 294-4 |
DuPont Performance Polymers Rynite® FR543 NC010 PET Rynite® FR543 NC010 is a flame retardant, 43% glass reinforced polyethylene terephthalate. Has a 155C temperature index that is equivalent to many thermosets. Recognized by UL as UL94V-0 at 0.8mm.. |
|||
Linear Mold Shrinkage, Flow | 0.0025 - 0.0035 cm/cm | 0.0025 - 0.0035 in/in | on Tensile Bar; ISO 294 |
Eurostar Staramide AG5K PA66, 25% Glass Filled, Injection Molded AG5 is a Heat and Hydrolytically Stabilized, 25% Glass Fiber Reinforced Polyamide 66 Injection Molding ResinInformation provided by Polymer Technology & Services, the North American exclusive suppli.. |
|||
Linear Mold Shrinkage, Flow | 0.0025 - 0.0035 cm/cm | 0.0025 - 0.0035 in/in | on Tensile Bar; E2P method |
Eurostar Starflam AFR560B1 PA66, Mineral/Glass Fiber Reinforced, Flame Retardant, Injection Molding Starflam AFR560B1 is a Flame Retardant, Mineral Filled and Glass Fiber Reinforced Polyamide 66, Injection Molding ResinInformation provided by Eurostar. |
|||
Linear Mold Shrinkage, Flow | 0.0025 cm/cm | 0.0025 in/in | ISO 2577 |
BASF Ultramid® B3WG6 HP BK 23210 30% Glass Filled PA6 (Dry) Description: 30% Glass fiber reinforced and heat aging resistant injection molding grade with enhances flowability used e.g. for automobile manifold.Information provided by BASF |
|||
Linear Mold Shrinkage, Flow | 0.0025 cm/cm @Diameter 2.00 mm |
0.0025 in/in @Diameter 0.0787 in |
ISO 294-4 |
Ascend Performance Materials Vydyne® R860 BK02 Nylon 66, Glass/Mineral Reinforced, Conditioned Vydyne® R860 BK02 is general-purpose, glass-fiber and mineral-reinforced PA66 resin. Available in black, this product is also lubricated for improved flow and offers superior surface appearance. Gl.. |