Physical Properties | Metric | English | Comments |
---|---|---|---|
Linear Mold Shrinkage, Flow | 0.0013 cm/cm | 0.0013 in/in | ISO 294-4, 2577 |
Lanxess Durethan® DP 1802 H3.0 000000 Nylon 6 PA 6 injection and extrusion molding grade, non-reinforced, impact-modified, UL 94V-2 off 0,75 mm, GWIT: 775°C off 0,75 mm, halogen-free |
|||
Linear Mold Shrinkage, Flow | 0.0013 cm/cm | 0.0013 in/in | ISO 294-4, 2577 |
Lanxess Durethan® DP BC 500 H2.0 901510 Nylon 6 PA 6, extrusion and blow molding grade, non-reinforced, elastomer-modified, high viscosity, good heat-ageing resistance |
|||
Linear Mold Shrinkage, Flow | 0.0013 cm/cm | 0.0013 in/in | Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4 |
Lanxess Durethan® BKV 15 DUS008 000000 Nylon 6, Glass Fiber Reinforced PA 6, 15% glass fibers, injection moldingInformation provided by LANXESS. |
|||
Linear Mold Shrinkage, Flow | 0.0013 cm/cm | 0.0013 in/in | ISO 294-4, 2577 |
Lanxess Pocan® BF 4409 000000 PBT, 7% Glass Fiber PBT, 7% glass fibers, injection molding, flame retardant |
|||
Linear Mold Shrinkage, Flow | 0.0013 cm/cm @Thickness 3.17 mm |
0.0013 in/in @Thickness 0.125 in |
ASTM D955 |
Techmer ES Elastoblend® PA6 IM 7040 MB Availability: North AmericaForms: PelletsAdditive: Heat Stabilizer, Impact Modifier, Nucleating Agent and LubricantFeatures: Heat Stabilized, Impact Modified, Nucleated and LubricatedInformation pro.. |
|||
Linear Mold Shrinkage, Flow | 0.0013 cm/cm @Thickness 3.17 mm |
0.0013 in/in @Thickness 0.125 in |
ASTM D955 |
Techmer ES Elastoblend® PA6 IM L Availability: North AmericaForms: PelletsAdditive: Impact Modifier and LubricantFeatures: Impact Modified and LubricatedInformation provided by TP Composites, Inc. |
|||
Linear Mold Shrinkage, Flow | 0.0013 cm/cm @Thickness 3.17 mm |
0.0013 in/in @Thickness 0.125 in |
ASTM D955 |
Techmer ES Elastoblend® PA6 IM L W Availability: North AmericaForms: PelletsAdditive: Impact Modifier and LubricantFeatures: Impact Modified and LubricatedProcessing Method: Injection MoldingInformation provided by TP Composites, Inc.. |
|||
Linear Mold Shrinkage, Flow | 0.0013 cm/cm @Thickness 3.17 mm |
0.0013 in/in @Thickness 0.125 in |
ASTM D955 |
Techmer ES Elastoblend® PA6 IM X Availability: North AmericaForms: PelletsAdditive: Heat Stabilizer, Impact Modifier and LubricantFeatures: Heat Stabilized, Impact Modified and LubricatedProcessing Method: Injection MoldingInformat.. |
|||
Linear Mold Shrinkage, Flow | 0.0013 cm/cm | 0.0013 in/in | ISO 294-4 |
Solvay Specialty Polymers Kalix® 2955 Polyamide, High Performance (HPPA), Glass Fiber Kalix® 2955 is a 27% bio-sourced, PA 6,10-based compound with 55% by weight glass fiber reinforcement. This material is specifically formulated for high strength and stiffness applications where .. |
|||
Linear Mold Shrinkage, Flow | 0.0013 cm/cm | 0.0013 in/in | ISO 294-4 |
Solvay Specialty Polymers Kalix® 9950 Polyamide, High Performance (HPPA), 50% Glass Fiber Kalix® 9950 is a 50% glass-fiber reinforced high-performance polyamide. It is hot-water moldable and intended for use in components requiring superior mechanical properties and excellent surface .. |
|||
Linear Mold Shrinkage, Flow | 0.0013 cm/cm @Thickness 3.17 mm |
0.0013 in/in @Thickness 0.125 in |
ASTM D955 |
Techmer ES HiFill® PA6/6 GF7 L 7% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 7% Filler by WeightAdditive: LubricantFeatures: LubricatedInformation provided by TP Composites, Inc. |
|||
Linear Mold Shrinkage, Flow | 0.0013 - 0.0025 cm/cm @Time 86400 sec |
0.0013 - 0.0025 in/in @Time 24.0 hour |
ASTM D955 |
SABIC Innovative Plastics LNP THERMOCOMP LC00APXQ PEEK LNP* THERMOCOMP* LC00APXQ is a compound based on Polyetheretherketone resin containing 50% Carbon Fiber. Added features of this material include: Exceptional Processing, Electrically Conductive. |
|||
Linear Mold Shrinkage, Flow | 0.0013 cm/cm | 0.0013 in/in | plate with film gate 150x150x3mm<sup>3</sup> |
BASF Ultradur® S 4090 G6X High Speed 30% Glass Filled PBT Description: Low-warpage, easy-flowing injection molding grade with 30 % glass fibers for technical parts, for which dimensional stability is very important, reduction of wall thickness (eg, e/e hou.. |
|||
Linear Mold Shrinkage, Flow | 0.0013 cm/cm @Thickness 2.00 mm |
0.0013 in/in @Thickness 0.0787 in |
DAM; ISO 294-4 |
DuPont Performance Polymers Zytel® 74G33W BK196 Nylon 66
(Unverified Data**) Zytel® 74G33W BK196 is a high gloss automotive weatherable black 33% glass reinforced nylon 66 and nylon 6 comelt resin.Information provided by DuPont Performance Polymers |
|||
Linear Mold Shrinkage, Flow | 0.0013 cm/cm @Time 86400 sec |
0.0013 in/in @Time 24.0 hour |
ASTM D955 |
SABIC Innovative Plastics LNP VERTON MV00ASU PP LNP VERTON* MV00ASU is a compound based on Polypropylene resin containing 50% Long Glass Fiber. Added features of this material include: Chemically Coupled, Heat Stabilized, UV Stabilized, Structur.. |