Physical Properties | Metric | English | Comments |
---|---|---|---|
Linear Mold Shrinkage | 0.015 - 0.022 cm/cm | 0.015 - 0.022 in/in | Across Flow; ISO 2577 |
Polykemi AB POLYelast TPE E606 Thermoplastic Elastomer, EPDM-based Information provided by Polykemi AB |
|||
Linear Mold Shrinkage | 0.012 - 0.022 cm/cm | 0.012 - 0.022 in/in | FRISETTA Test Method |
Nilit FRIANYL B63 S20 Nylon 6 for injection molding Nylon 6 for injection molding, impact modified.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Linear Mold Shrinkage | 0.018 - 0.022 cm/cm | 0.018 - 0.022 in/in | ASTM D955 |
Polymer Resources AC-GP2 Acetal Copolymer, Medium Flow Process: Molding or ExtrusionNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resources Corporation. |
|||
Linear Mold Shrinkage | 0.016 - 0.022 cm/cm | 0.016 - 0.022 in/in | ASTM D955 |
Polymer Resources TP-GP2 Polybutylene Terephthalate, General Purpose Polybutylene Terephthalate, General Purpose Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provid.. |
|||
Linear Mold Shrinkage | 0.018 - 0.022 cm/cm | 0.018 - 0.022 in/in | ASTM D955 |
Polymer Resources AC-GP3 Acetal Copolymer, High Flow, Thin Wall Applications Process: Molding or ExtrusionNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resources Corporation. |
|||
Linear Mold Shrinkage | 0.015 - 0.022 cm/cm | 0.015 - 0.022 in/in | FRISETTA Test Method |
Nilit FRIANYL C73 HS28 Nylon 6.6/6 for injection molding Nylon 6.6/6 for injection molding, medium viscosity, high impact modified.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Linear Mold Shrinkage | 0.018 - 0.022 cm/cm | 0.018 - 0.022 in/in | Asahi Chemical test |
Asahi Kasei Tenac® GT525 Acetal Homopolymer, 25% Glass Beads
(discontinued **) 25% glass beads-filled grade with superior isotropic dimensional stability.Applications: Speedometer frames.This product is not a part of the standard product line dated 2003. |
|||
Linear Mold Shrinkage | 0.016 - 0.022 cm/cm | 0.016 - 0.022 in/in | |
Lehmann & Voss LUVOCOM® 80/TF/18/GY Polyacetal-copolymer, with PTFE Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Emergency running property, gl.. |
|||
Linear Mold Shrinkage | 0.016 - 0.022 cm/cm | 0.016 - 0.022 in/in | |
Lehmann & Voss LUVOCOM® 80/TF/22/NT Polyacetal-copolymer, with PTFE Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Emergency running property, gl.. |
|||
Linear Mold Shrinkage | 0.020 - 0.022 cm/cm | 0.020 - 0.022 in/in | ASTM D955 |
LG Chemical LUCEL FW-7005 Friction and Wear Resistant POM, Oil filled LUCEL semi-crystalline acetal copolymer resins are produced by gas phase polymerization. LUCEL resins can be widely accepted as the replacement of thermosets, aluminum and zinc die-casts or other m.. |
|||
Linear Mold Shrinkage | 0.018 - 0.022 cm/cm | 0.018 - 0.022 in/in | ISO 2577 |
Polyram RamTal PM1429 Polyacetal, PTFE Filled Polyacetal filled with PTFE for sliding parts, low friction and improved wear resistance of molded parts.Information provided by Polyram. |
|||
Linear Mold Shrinkage | 0.018 - 0.022 cm/cm | 0.018 - 0.022 in/in | |
Polyram RamTal PM7002 Acetal, UV Stabilized UV stabilized acetal copolymer for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
Linear Mold Shrinkage | 0.018 - 0.022 cm/cm | 0.018 - 0.022 in/in | |
Polyram RamTal PM7009 Acetal, UV Stabilized UV stabilized polyacetal copolymer for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
Linear Mold Shrinkage | 0.018 - 0.022 cm/cm | 0.018 - 0.022 in/in | ISO 2577 |
Polyram RamTal PMH2003 Polyacetal Homopolymer for Injection Molding General purpose polyacetal homopolymer for injection molding applications, MFI 3.Information provided by Polyram. |
|||
Linear Mold Shrinkage | 0.018 - 0.022 cm/cm | 0.018 - 0.022 in/in | ISO 2577 |
Polyram RamTal PMH2010 Polyacetal Homopolymer for Injection Molding General purpose polyacetal homopolymer for injection molding applications, MFI 10.Information provided by Polyram. |
|||
Linear Mold Shrinkage | 0.012 - 0.022 cm/cm | 0.012 - 0.022 in/in | D955 |
Zhejiang Juner 201-G0 Flame Resistant Nonreinforced Applications: Electrons and Electricity: TV Components, Plugs of Computers, Exhaust Fans of Computers, Plugs, Sockets, Shells of Electronics, Framework of Level Output Transformers, Pipe Pedestals, .. |
|||
Linear Mold Shrinkage | 0.018 - 0.022 cm/cm | 0.018 - 0.022 in/in | ISO 2577 |
Polyram RamTal PMH2017 Polyacetal Homopolymer for Injection Molding General purpose polyacetal homopolymer for injection molding applications, MFI 1.7.Information provided by Polyram. |
|||
Linear Mold Shrinkage | 0.018 - 0.022 cm/cm | 0.018 - 0.022 in/in | ASTM D 955 |
Cossa Polimeri ESTAPROP HK 4000 CH-HT Polypropylene Copolymer Polypropylene copolymer, high fluidityInformation provided by Cossa Polimeri S.r.l. |
|||
Linear Mold Shrinkage | 0.015 - 0.022 cm/cm | 0.015 - 0.022 in/in | ASTM D955 |
Diamond Polymers NPP25-0103 CF15 Conductive Copolymer Polypropylene Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc. |
|||
Linear Mold Shrinkage | 0.012 - 0.022 cm/cm | 0.012 - 0.022 in/in | ASTM D955 |
Beijing Chemical Industry KAIFA® 101 PBT Resin Unreinforced, good toughnessInformation provided by Beijing Chemical Industry Research Institute (Group) |
|||
Linear Mold Shrinkage | 0.018 - 0.022 cm/cm | 0.018 - 0.022 in/in | |
Beijing Ranger Chem BLUESTAR® BS450 Acetal Copolymer Modified PBT Characteristics: Unreinforced grades have abundant strength and flexibility, and have strong characteristics against brittleness. UL-certified slow-burning (94HB) and self-extinguishin.. |
|||
Linear Mold Shrinkage | 0.018 - 0.022 cm/cm | 0.018 - 0.022 in/in | Asahi Kasei Method |
Asahi Kasei Tenac® 4010 Homopolymer Acetal Resin General purpose grade, high impact, high elongation, medium viscosityInformation provided by Asahi Kasei Corporation. |
|||
Linear Mold Shrinkage | 0.016 - 0.022 cm/cm | 0.016 - 0.022 in/in | ISO 294-4 |
Premix Thermoplastics PRE-ELEC® PA 1409 Conductive Thermoplastic Compound PRE-ELEC® PA 1409 is a conductive thermoplastic compound based on polyamide 6. Conductivity is achieved by using conductive carbon black. In addition to a low electrical resistivity PRE-ELEC® PA 1.. |
|||
Linear Mold Shrinkage | 0.012 - 0.022 cm/cm | 0.012 - 0.022 in/in | ISO 294-4 |
Premix Thermoplastics PRE-ELEC® PA 1411 Conductive Thermoplastic Compound PRE-ELEC® PA 1411 is a conductive thermoplastic compound based on polyamide 6. Conductivity is achieved by using conductive carbon black. PRE-ELEC® PA 1411 has a very low electrical resistivity. P.. |
|||
Linear Mold Shrinkage | 0.018 - 0.022 cm/cm | 0.018 - 0.022 in/in | Asahi Kasei Method |
Asahi Kasei Tenac® SH410 Homopolymer Acetal Resin General purpose grade, high impact, high elongation, medium viscosityInformation provided by Asahi Kasei Corporation. |
|||
Linear Mold Shrinkage | 0.016 - 0.022 cm/cm | 0.016 - 0.022 in/in | ISO 294-4 |
Premix Thermoplastics PRE-ELEC® PA 1408 Conductive Thermoplastic Compound PRE-ELEC® PA 1408 is a conductive thermoplastic compound based on polyamide 6. Conductivity is achieved by using conductive carbon black. In addition to a low electrical resistivity PRE-ELEC® PA 1.. |