Physical Properties | Metric | English | Comments |
---|---|---|---|
Linear Mold Shrinkage | 0.000200 - 0.00900 cm/cm | 0.000200 - 0.00900 in/in | Average value: 0.00341 cm/cm Grade Count:110 |
Overview of materials for Polycarbonate, Glass Fiber Filled, Flame Retardant This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, Glass Fiber Filled, Flame Retardant". Each property range of values reported is minimum a.. |
|||
Linear Mold Shrinkage | 0.000200 - 0.0100 cm/cm | 0.000200 - 0.0100 in/in | Average value: 0.00308 cm/cm Grade Count:21 |
Overview of materials for Polyphenylene Sulfide (PPS) with 30% Glass Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS) with 30% Glass Fiber Filler". Specific grades with glass content between 25%.. |
|||
Linear Mold Shrinkage | 0.000200 - 0.00200 cm/cm | 0.000200 - 0.00200 in/in | Average value: 0.00110 cm/cm Grade Count:17 |
Overview of materials for Polyphenylene Sulfide (PPS) with 20% Carbon Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS) with 20% Carbon Fiber Filler". Specific grades with carbon fiber content bet.. |
|||
Linear Mold Shrinkage | 0.000200 - 0.00400 cm/cm | 0.000200 - 0.00400 in/in | Average value: 0.000985 cm/cm Grade Count:19 |
Overview of materials for Polyphenylene Sulfide (PPS) with 30% Carbon Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS) with 30% Carbon Fiber Filler". Specific grades with carbon fiber content bet.. |
|||
Linear Mold Shrinkage | 0.000200 - 0.0350 cm/cm | 0.000200 - 0.0350 in/in | Average value: 0.00317 cm/cm Grade Count:150 |
Overview of materials for Nylon 6, 50% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 50% Glass Fiber Filled". Specific grades with glass content between 45% and 54% are included. E.. |
|||
Linear Mold Shrinkage | 0.000200 - 0.0350 cm/cm | 0.000200 - 0.0350 in/in | Average value: 0.00376 cm/cm Grade Count:47 |
Overview of materials for Nylon 6, Carbon Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Carbon Fiber Filled". Each property range of values reported is minimum and maximum values of a.. |
|||
Linear Mold Shrinkage | 0.000200 - 0.0150 cm/cm | 0.000200 - 0.0150 in/in | Average value: 0.00252 cm/cm Grade Count:28 |
Overview of materials for Nylon 66, 30% Carbon Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 30% Carbon Fiber Filled". Specific grades with carbon fiber content between 25% and 34% are in.. |
|||
Linear Mold Shrinkage | 0.000200 - 0.0160 cm/cm | 0.000200 - 0.0160 in/in | Average value: 0.00278 cm/cm Grade Count:82 |
Overview of materials for Nylon 66, Carbon Fiber/PTFE Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Carbon Fiber/PTFE Filled". Each property range of values reported is minimum and maximum value.. |
|||
Linear Mold Shrinkage | 0.000200 - 0.0200 cm/cm | 0.000200 - 0.0200 in/in | Average value: 0.00679 cm/cm Grade Count:284 |
Overview of materials for Nylon 12 This property data is a summary of similar materials in the MatWeb database for the category "Nylon 12". Each property range of values reported is minimum and maximum values of appropriate MatWeb en.. |
|||
Linear Mold Shrinkage | 0.000200 - 0.00800 cm/cm | 0.000200 - 0.00800 in/in | Average value: 0.00255 cm/cm Grade Count:21 |
Overview of materials for Nylon 12, Carbon Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 12, Carbon Fiber Filled". Each property range of values reported is minimum and maximum values of .. |
|||
Linear Mold Shrinkage | 0.000200 - 0.00700 cm/cm | 0.000200 - 0.00700 in/in | Average value: 0.00211 cm/cm Grade Count:34 |
Overview of materials for Epoxy Molding Compound This property data is a summary of similar materials in the MatWeb database for the category "Epoxy Molding Compound". Each property range of values reported is minimum and maximum values of appropr.. |